PC LUPOY GN1006FMR

Description: Injection Molding, PC, Halogen Free Flame Retardant, Transparency, Mold Release

Application: IT/OA, Electric Electronic Housing and Components

CAS: 103598-77-2

Information provided by LG Chemical

Physical Properties	Metric	English	Comments
Specific Gravity	1.20g/cc	1.20g/cc	ASTM D792
Maximum Moisture Content	0.020	0.020	Injection Molding
Linear Mold Shrinkage, Flow	0.0050-0.0070cm/cm @Thickness 3.20 mm	0.0050-0.0070in/in @Thickness 0.126 in	ASTM D955
Melt Flow	10g/10 min @Load 1.20 kg, Temperature 300 °C	10g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	118	118	ASTM D785
Tensile Strength, Yield	61.8MPa @Thickness 3.20 mm	8960psi @Thickness 0.126 in	50mm/min; ASTM D638
Elongation at Break	= 100 % @Thickness 3.20 mm	= 100 % @Thickness 0.126 in	50mm/min; ASTM D638
Flexural Yield Strength	91.2MPa @Thickness 3.20 mm	13200psi @Thickness 0.126 in	10mm/min; ASTM D790
Flexural Modulus	2.26GPa @Thickness 3.20 mm	327ksi @Thickness 0.126 in	10mm/min; ASTM D790

PC LUPOY GN1006FMR

塑料的处理

PC塑胶原料的吸水率较大，加工前一定要预热干燥，纯PC干燥120℃，改性PC一般用110℃温度干燥4小时以上。干燥时间不能超过10小时。一般可用对空挤出法判断干燥是否足够。再生料的使用比例可达20%。在某些情况下，可100%的使用再生料，实际份量要视制品的品质要求而定。再生料不能同时混合不同的色母粒，否则会严重损坏成品的性质。

注塑机选用

PC塑料制品由于成本及其它方面的原因，多用改性材料，特别是电工产品，还须增加防火性能，在阻燃的PC和其它塑料合金产品成型时，对注塑机塑化系统的要求是混合好、耐腐蚀，常规的塑化螺杆难以做到，在选购时，一定要预先说明。

主要优点

1．具高强度及弹性系数、高冲击强度、使用温度范围广；

2．高度透明性及自由染色性；

3．成形收缩率低、尺寸安定性良好；

4．耐疲劳性佳；

5．耐候性佳；

6．电气特性优。

性能特点:良好的流动性;脱模性能良好;

粘度，高；光学透明性好、抗冲击强度高；

并具有优异的热安稳性、耐蠕变性、抗寒性、电绝缘性和阻燃性等。

加工方法:薄膜挤出；吹塑成型；挤出成型；热成型；树脂传递成型；涂层；砑光；注射成型也是最重要的加工方法之一；

用途:在透明建筑板材、电子电器、光盘、汽车工业、机械、光学、医药等领域得到广泛运用。

PC塑料物理性能以及加工

低温-45度聚碳酸酯无色透明，耐热，抗冲击，阻燃BI级，在普通运用温度内都有出色的机械功用。