LDPE SABIC PCG09
| General | |
|
Material Status
|
|
|
Availability
|
Africa Middle EastAsia PacificEuropeLatin AmericaNorth America |
|
Uses
|
Industrial ApplicationsMedical/Healthcare Applications |
|
Agency Ratings
|
|
|
Processing Method
|
Cast FilmInjection Molding |
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
|
g/cm3
|
ASTM D1505 |
|
Melt Mass-Flow Rate (MFR)
|
ISO 1133 | ||
|
190°C/2.16 kg
|
|
g/10 min
|
|
|
190°C/5.0 kg
|
|
g/10 min
|
|
|
Melt Volume-Flow Rate (MVR)
|
ISO 1133 | ||
|
190°C/2.16 kg
|
|
cm3/10min
|
|
|
190°C/5.0 kg
|
|
cm3/10min
|
|
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|
psi
|
ISO 527-2/1A/50 |
|
Tensile Stress
|
ISO 527-2/1A/50 | ||
|
Yield
|
|
psi
|
|
|
Break
|
|
psi
|
|
|
Tensile Strain(Break)
|
|
%
|
ISO 527-2/1A/50 |
LDPE SABIC PCG09
(1)乙烯聚合反应过程是一个强烈的放热过程。乙烯的聚合热约为93.5kJ/mol(或3.3kJ/g)，在235MPa、150~300℃下乙烯的比热容为2.51~2.85J/(g·℃)，反应热如果不能及时移去，每1%乙烯发生聚合将使温度升高12~13℃。如果温度过高，还会导致乙烯分解。
(2)在高压下，乙烯已被压缩到密度为0.5g/mL的气密相状态，近似于不能再压缩的液体，此时乙烯分子间的距离显著缩短，从而增加了游离基与乙烯分子的碰撞概率，所以容易发生聚合反应。
(3)高温下增长链的自由基活性大，容易发生链转移反应，所得到的聚合物为带有较多支链的线型结构。通常每1000个碳链原子中含有20~30个支链，结晶度为45%~65%，密度在0.910~0.925g/mL，质轻、具柔性，耐低温性、耐冲击性较好。
LDPE产品性能
低密度聚乙烯其特征主要有以下几点：
(1)薄膜呈微乳白透明色，柔软。强度比高密度聚乙烯小，抗冲击强度则比高密度聚乙烯大。
(2)耐寒、耐低温及耐较高温度。较厚的薄膜能承受90℃热水浸泡的杀菌过程。
(3)防潮性能比较好，化学性能稳定，不溶于一般溶剂。
(4)有较大的透气性，故用作易氧化的食品包装时，其内容物的贮存期不宜过长。
(5)耐油脂性较差，制品能被缓慢溶涨。包装含油脂食品时，久贮后会使食品出现哈喇味。
(6)长时期受紫外线及热作用会老化，影响其物理性能和介电性能。
(7)熔点为110~115℃，加工温度为150~210℃，若在惰性气体中，温度可达300℃仍稳定。但熔体和氧接触易发生降解作用。
LDPE应用领域
低密度聚乙烯的应用范围:适用于调味料、糕点、糖、蜜饯、饼干、奶粉、茶叶、鱼肉松等食品包装。片剂、粉剂等药品包装,衬衫、服装、针织棉制品及化纤制品等纤维制品包装。洗衣粉、洗涤剂、化妆品等日化用品包装。由于单层PE薄膜的机械性能较差,所以通常用作复合包装袋的内层,即多层复合薄膜热封性基材。
LDPE SABIC PCG09 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）