东莞市天之鸿塑化有限公司
PC/PBT/美国基础创新/5720-1001产品说明：
未填充的 PBT+PC 合金。出色的低温冲击/耐化学性。XENOY 的紫外线稳定版
|
用途
|
|
|||
|
Also Available In
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度 / 比重
|
|||
|
--
|
|
g/cm3
|
ASTM D792 |
|
--
|
1.17
|
g/cm3
|
ISO 1183 |
|
特定体积
|
0.850
|
cm3/g
|
ASTM D792 |
|
熔流率（熔体流动速率）
|
|||
|
250°C/2.16 kg
|
3.8
|
g/10 min
|
ASTM D1238 |
|
250°C/5.0 kg
|
11
|
g/10 min
|
ASTM D1238,ISO 1133 |
|
265°C/2.16 kg
|
6.0
|
g/10 min
|
ASTM D1238 |
|
266°C/5.0 kg
|
20
|
g/10 min
|
ASTM D1238 |
|
250°C/2.16 kg
|
3.0
|
g/10 min
|
ISO 1133 |
|
熔融体积流量（MVR）
|
ISO 1133 | ||
|
250°C/2.16 kg
|
3.0
|
cm3/10min
|
|
|
250°C/5.0 kg
|
10
|
cm3/10min
|
|
|
265°C/2.16 kg
|
6.0
|
cm3/10min
|
|
|
265°C/5.0 kg
|
18
|
cm3/10min
|
|
|
收缩率 - 流动(3.20 mm)
|
1.0 到 1.2
|
%
|
内部方法 |
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
0.28
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.080
|
%
|
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
--2
|
1830
|
MPa
|
ASTM D638 |
|
--3
|
1830
|
MPa
|
内部方法 |
|
--4
|
1810
|
MPa
|
ASTM D638 |
|
--
|
1790
|
MPa
|
ISO 527-1/1 |
|
抗张强度
|
|||
|
屈服5
|
47.0
|
MPa
|
ASTM D638 |
|
屈服6
|
45.0
|
MPa
|
内部方法 |
|
屈服7
|
44.0
|
MPa
|
ASTM D638 |
|
屈服
|
44.0
|
MPa
|
ISO 527-2/5 |
|
屈服
|
47.0
|
MPa
|
ISO 527-2/50 |
|
断裂7
|
50.0
|
MPa
|
ASTM D638 |
|
断裂6
|
47.0
|
MPa
|
内部方法 |
|
断裂5
|
48.0
|
MPa
|
ASTM D638 |
|
断裂
|
43.0
|
MPa
|
ISO 527-2/5,ISO 527-2/50 |
|
伸长率
|
|||
|
屈服7
|
4.6
|
%
|
ASTM D638 |
|
屈服6
|
4.6
|
%
|
内部方法 |
|
屈服5
|
4.0
|
%
|
ASTM D638 |
|
屈服
|
4.1
|
%
|
ISO 527-2/5 |
|
屈服
|
4.6
|
%
|
ISO 527-2/50 |
|
断裂7
|
120
|
%
|
ASTM D638 |
|
断裂6
|
110
|
%
|
内部方法 |
|
断裂5
|
120
|
%
|
ASTM D638 |
|
断裂
|
110
|
%
|
ISO 527-2/5 |
|
断裂
|
120
|
%
|
ISO 527-2/50 |
|
弯曲模量
|
|||
|
50.0 mm 跨距8
|
1660
|
MPa
|
ASTM D790 |
|
--9
|
1860
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
--9,10
|
71.0
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距8
|
70.0
|
MPa
|
ASTM D790 |
|
断裂, 50.0 mm 跨距8
|
69.0
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度11
|
ISO 179/1eA | ||
|
-30°C
|
47
|
kJ/m2
|
|
|
23°C
|
55
|
kJ/m2
|
|
|
悬壁梁缺口冲击强度
|
|||
|
-40°C
|
600
|
J/m
|
ASTM D256 |
|
-30°C
|
650
|
J/m
|
ASTM D256 |
|
-20°C
|
700
|
J/m
|
ASTM D256 |
|
-10°C
|
660
|
J/m
|
ASTM D256 |
|
0°C
|
690
|
J/m
|
ASTM D256 |
|
23°C
|
720
|
J/m
|
ASTM D256 |
|
-40°C12
|
46
|
kJ/m2
|
ISO 180/1A |
|
-30°C12
|
48
|
kJ/m2
|
ISO 180/1A |
|
-20°C12
|
50
|
kJ/m2
|
ISO 180/1A |
|
-10°C12
|
52
|
kJ/m2
|
ISO 180/1A |
|
0°C12
|
55
|
kJ/m2
|
ISO 180/1A |
|
23°C12
|
55
|
kJ/m2
|
ISO 180/1A |
|
装有测量仪表的落镖冲击
|
ASTM D3763 | ||
|
-40°C, Energy at Peak
|
49.0
|
J
|
|
|
-40°C, Total Energy
|
59.0
|
J
|
|
|
-30°C, Energy at Peak
|
49.0
|
J
|
|
|
-30°C, Total Energy
|
61.0
|
J
|
|
|
-20°C, Energy at Peak
|
41.0
|
J
|
|
|
-20°C, Total Energy
|
53.0
|
J
|
|
|
23°C, Energy at Peak
|
44.0
|
J
|
|
|
23°C, Total Energy
|
54.0
|
J
|
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 3.20 mm
|
108
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 6.40 mm
|
117
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距12
|
109
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, 未退火, 3.20 mm
|
83.0
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 6.40 mm
|
95.0
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距12
|
87.0
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
|||
|
--
|
119
|
°C
|
ASTM D152513,ISO 306/B5013 |
|
--
|
122
|
°C
|
ISO 306/B120 |
|
线形热膨胀系数
|
|||
|
流动 : -40 到 95°C
|
9.8E-5
|
cm/cm/°C
|
ASTM E831 |
|
流动 : -30 到 80°C
|
9.8E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
垂直 : -40 到 95°C
|
1.0E-4
|
cm/cm/°C
|
ASTM E831 |
|
垂直 : -30 到 80°C
|
1.0E-4
|
cm/cm/°C
|
ISO 11359-2 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
110
|
°C
|
|
|
干燥时间
|
4.0 到 6.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
50 到 80
|
%
|
|
|
料筒后部温度
|
245 到 265
|
°C
|
|
|
料筒中部温度
|
250 到 270
|
°C
|
|
|
料筒前部温度
|
255 到 275
|
°C
|
|
|
射嘴温度
|
255 到 270
|
°C
|
|
|
加工（熔体）温度
|
260 到 275
|
°C
|
|
|
模具温度
|
65 到 90
|
°C
|
|
|
背压
|
0.300 到 0.700
|
MPa
|
|
|
螺杆转速
|
50 到 80
|
rpm
|
|
|
排气孔深度
|
0.013 到 0.020
|
mm
|
|
| 注射说明 | |||
|
|||