物性表
物性纠错
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
|---|---|---|---|---|
| 密度 / 比重 | ASTM D-792 | DAM｜1.14 | ||
| ASTM D-792 | 50%RH｜- | |||
| 模具收缩率 | DAM｜1.5 | % | ||
| 50%RH｜- | % | |||
| 阻燃性 | UL 94 | DAM｜0.71 | mm | |
| UL 94 | 50%RH｜- | mm | ||
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| IZOD缺口冲击强度 | ASTM D-256 | DAM｜53 | J/m | |
| ASTM D-256 | 50%RH｜105 | J/m | ||
| 断裂拉伸强度 | ASTN D-638 | DAM｜83 | Mpa | |
| ASTN D-638 | 50%RH｜- | Mpa | ||
| 断裂伸长率 | ASTM D638/ISO 527 | 50 | % | |
| 拉伸强度 | ASTM D638/ISO 527 | 83 | kg/cm2(MPa)[Lb/in2] | |
| ASTN D-638 | DAM｜83 | Mpa | ||
| ASTN D-638 | 50%RH｜64 | Mpa | ||
| 屈服伸长率 | ASTN D-638 | DAM｜4 | % | |
| ASTN D-638 | 50%RH｜- | % | ||
| 伸长率 | 断裂 | ASTM D-638 | DAM｜50 | % |
| 断裂 | ASTM D-638 | 50%RH｜＞300 | % | |
| ASTM D638/ISO 527 | 4 | % | ||
| 弯曲模量 | ASTM D790/ISO 178 | 2800 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D-790 | DAM｜2800 | Mpa | ||
| ASTM D-790 | 50%RH｜1210 | Mpa | ||
| Charpy冲击强度 | ASTM D256/ISO 179 | 53 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 105 | kg·cm/cm(J/M)ft·lb/in | ||
| 拉伸断裂伸长率(延伸率) | ASTM D638/ISO 527 | 83 | % | |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 燃烧性（率） | UL94 | 0.71 | ||
| 热变形温度 | ASTM D648/ISO 75 | 210 | ℃（℉） | |
| ASTM D648/ISO 75 | 65 | ℃（℉） | ||
| 0.45MPa | ASTM D-648 | DAM｜210 | ℃ | |
| 0.45MPa | ASTM D-648 | 50%RH｜- | ℃ | |
| 1.80MPa | ASTM D-648 | DAM｜65 | ℃ | |
| 1.80MPa | ASTM D-648 | 50%RH｜- | ℃ | |
| 熔点 | ASTM D-3418 | DAM｜262 | ℃ | |
| ASTM D-3418 | 50%RH｜- | ℃ | ||
| 262 | ℃（℉） | |||
| 线性膨胀系数 | ASTM D696/ISO 11359 | 16.5 | mm/mm.℃ | |
| 电气性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 表面电阻率 | ASTM D257/IEC 60093 | 1014 | Ω | |
| ASTM D-257 | DAM｜1014 | |||
| ASTM D-257 | 50%RH｜- | |||
| 介电常数 | 106Hz | ASTM D-150 | DAM｜3.7 | |
| 106Hz | ASTM D-150 | 50%RH｜- | ||
| ASTM D150/IEC 60250 | 23.2 | |||
| ASTM D150/IEC 60250 | 4.0 | |||
| 103Hz | ASTM D-150 | DAM｜4.0 | ||
| 103Hz | ASTM D-150 | 50%RH｜- | ||
| 介电强度 | 3.2mm | ASTM D-149 | DAM｜16.5 | KV/mm |
| 3.2mm | ASTM D-149 | 50%RH｜- | KV/mm | |
| 1.6mm | ASTM D-150 | DAM｜23.2 | KV/mm | |
| 1.6mm | ASTM D-150 | 50%RH｜- | KV/mm | |
| 损耗因数 | 106Hz | ASTM D-150 | DAM｜0.02 | |
| 106Hz | ASTM D-150 | 50%RH｜- | ||
| 102Hz | ASTM D-150 | DAM｜0.01 | ||
| 102Hz | ASTM D-150 | 50%RH｜- | ||
| 103Hz | ASTM D-150 | DAM｜0.02 | ||
| 103Hz | ASTM D-150 | 50%RH｜- | ||
| 体积电阻率 | ASTM D-257 | DAM｜1015 | Ω.m | |
| ASTM D-257 | 50%RH｜- | Ω.m | ||
| ASTM D257/IEC 60093 | 1015 | Ω.cm | ||
| 物性性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 比重（密度） | ASTM D792/ISO 1183 | 1.14 | ||
| 吸水率 23℃/24H | ASTM D570/ISO 62 | 1.2 | % | |
| 基本性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 密度 / 比重 | ASTM D-792 | DAM｜1.14 | g/cm3 | |
| ASTM D-792 | 50%RH｜- | g/cm3 | ||
| 吸水率 | 24hr | ASTM D-570 | DAM｜1.2 | % |
| 24hr | ASTM D-570 | 50%RH｜- | % |