| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
|---|---|---|---|---|
| 密度 / 比重 | ASTM D-792 | 无水｜1.25 | ||
| ASTM D-792 | 3%水｜- | |||
| 23°C | g/cm3 | 1.25 | -- | |
| ASTM D-792 | 无水｜1.5 | |||
| ASTM D-792 | 1.9%水｜- | |||
| 收缩率 | TD:3.00mm2 | % | 0.70到1.1 | -- |
| MD:3.00mm3 | % | 0.50到0.70 | -- | |
| 泰伯磨耗量 | 1000g,CS-17 | ASTM D-1044 | 无水｜30 | mg/1000次 |
| 1000g,CS-17 | ASTM D-1044 | 1.9%水｜- | mg/1000次 | |
| 1000g,CS-17 | ASTM D-1044 | 无水｜10 | mg/1000次 | |
| 1000g,CS-17 | ASTM D-1044 | 3%水｜- | mg/1000次 | |
| 吸水率 | 23°C,24hr | % | 1.3 | -- |
| 饱和,23°C | % | 8.3 | -- | |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 断裂伸长率 | 23℃ | ASTM D-638 | 无水｜5 | % |
| 23℃ | ASTM D-638 | 1.9%水｜5 | % | |
| 23℃ | ASTM D-638 | 无水｜4 | % | |
| 23℃ | ASTM D-638 | 3%水｜200 | % | |
| 80℃ | ASTM D-638 | 无水｜10 | % | |
| 80℃ | ASTM D-638 | 3%水｜200 | % | |
| -40℃ | ASTM D-638 | 无水｜3.5 | % | |
| -40℃ | ASTM D-638 | 3%水｜200 | % | |
| 剪切强度 | 23°C | MPa | 105 | -- |
| 抗剪强度 | 23℃ | ASTM D-732 | 无水｜940 | kg/cm2 |
| 23℃ | ASTM D-732 | 1.9%水｜750 | kg/cm2 | |
| 80℃ | ASTM D-792 | 无水｜- | kg/cm2 | |
| 80℃ | ASTM D-792 | 3%水｜770 | kg/cm2 | |
| 23℃ | ASTM D-732 | 无水｜- | kg/cm2 | |
| 23℃ | ASTM D-732 | 3%水｜770 | kg/cm2 | |
| 抗拉屈服强度 | -40 | ASTM D-638 | 无水｜1550 | kg/cm2 |
| -40 | ASTM D-638 | 3%水｜1100 | kg/cm2 | |
| 23℃ | ASTM D-638 | 无水｜1200 | kg/cm2 | |
| 23℃ | ASTM D-638 | 3%水｜5300 | kg/cm2 | |
| 80℃ | ASTM D-638 | 无水｜550 | kg/cm2 | |
| 80℃ | ASTM D-638 | 3%水｜400 | kg/cm2 | |
| 23℃ | ASTM D-638 | 无水｜2000 | kg/cm2 | |
| 23℃ | ASTM D-638 | 1.9%水｜1300 | kg/cm2 | |
| 80℃ | ASTM D-638 | 无水｜1200 | kg/cm2 | |
| 80℃ | ASTM D-638 | 1.9%水｜- | kg/cm2 | |
| -40℃ | ASTM D-638 | 无水｜2900 | kg/cm2 | |
| -40℃ | ASTM D-638 | 1.9%水｜- | kg/cm2 | |
| 拉伸应变 | 断裂,-40°C | % | 2.0 | 5.0 |
| 断裂,23°C | % | 2.5 | 6.0 | |
| 断裂,80°C | % | 6.0 | 7.5 | |
| 拉伸应力 | -40°C | MPa | 150 | |
| 23°C | MPa | 130 | 65.0 | |
| 80°C | MPa | 55.0 | 30.0 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜95 | M-标度 |
| 23℃ | ASTM D-785 | 1.9%水｜- | M-标度 | |
| 23℃ | ASTM D-785 | 无水｜121 | R-标度 | |
| 23℃ | ASTM D-785 | 1.9%水｜- | R-标度 | |
| 23℃ | ASTM D-785 | 无水｜119 | R-标度 | |
| 23℃ | ASTM D-785 | 3%水｜100 | R-标度 | |
| 23℃ | ASTM D-785 | 无水｜90 | M-标度 | |
| 23℃ | ASTM D-785 | 3%水｜100 | M-标度 | |
| ASTM D785 | R119,M90 | |||
| 摩擦系数-vs.Metal4 | 0.15 | -- | ||
| 挠曲模量 | 23℃ | ASTM D-790 | 无水｜122000 | kg/cm2 |
| 23℃ | ASTM D-790 | 1.9%水｜72000 | kg/cm2 | |
| 80℃ | ASTM D-790 | 无水｜63000 | kg/cm2 | |
| 80℃ | ASTM D-790 | 1.9%水｜45000 | kg/cm2 | |
| -40℃ | ASTM D-790 | 无水｜140000 | kg/cm2 | |
| -40℃ | ASTM D-790 | 1.9%水｜120000 | kg/cm2 | |
| 23℃ | ASTM D-790 | 无水｜51000 | kg/cm2 | |
| 23℃ | ASTM D-790 | 3%水｜14000 | kg/cm2 | |
| 80℃ | ASTM D-790 | 无水｜21000 | kg/cm2 | |
| 80℃ | ASTM D-790 | 3%水｜5000 | kg/cm2 | |
| -40℃ | ASTM D-790 | 无水｜68000 | kg/cm2 | |
| -40℃ | ASTM D-790 | 3%水｜42000 | kg/cm2 | |
| 挠曲强度 | 23℃ | ASTM D-790 | 无水｜1700 | kg/cm2 |
| 23℃ | ASTM D-790 | 3%水｜650 | kg/cm2 | |
| 80℃ | ASTM D-790 | 无水｜850 | kg/cm2 | |
| 80℃ | ASTM D-790 | 3%水｜400 | kg/cm2 | |
| -40℃ | ASTM D-790 | 无水｜2100 | kg/cm2 | |
| -40℃ | ASTM D-790 | 3%水｜1300 | kg/cm2 | |
| 23℃ | ASTM D-790 | 无水｜2900 | kg/cm2 | |
| 23℃ | ASTM D-790 | 1.9%水｜1850 | kg/cm2 | |
| 80℃ | ASTM D-790 | 无水｜16000 | kg/cm2 | |
| 80℃ | ASTM D-790 | 1.9%水｜- | kg/cm2 | |
| -40℃ | ASTM D-790 | 无水｜3300 | kg/cm2 | |
| -40℃ | ASTM D-790 | 1.9%水｜- | kg/cm2 | |
| 泰伯耐磨性 | 1000Cycles | mg | 0.300 | -- |
| 弯曲模量 | -40°C | MPa | 7300 | |
| 23°C | MPa | 5800 | 2700 | |
| 80°C | MPa | 2300 | 1700 | |
| 弯曲应力 | -40°C | MPa | 245 | -- |
| 23°C | MPa | 200 | ||
| 80°C | MPa | 100 | 50.0 | |
| 压缩强度 | 23℃ | ASTM D-695 | 无水｜1900 | kg/cm2 |
| 23℃ | ASTM D-695 | 1.9%水｜- | kg/cm2 | |
| 80℃ | ASTM D-695 | 无水｜1000 | kg/cm2 | |
| 80℃ | ASTM D-695 | 1.9%水｜- | kg/cm2 | |
| -40℃ | ASTM D-695 | 无水｜2600 | kg/cm2 | |
| -40℃ | ASTM D-695 | 1.9%水｜- | kg/cm2 | |
| 压缩应力 | -40°C | MPa | 220 | 140 |
| 23°C | MPa | 150 | 75.0 | |
| 80°C | MPa | 85.0 | 45.0 | |
| IZOD冲击强度 | 23℃，V-缺口1/2 | ASTM D-256 | 无水｜6 | kg.cm/cm |
| 23℃，V-缺口1/2 | ASTM D-256 | 3%水｜28 | kg.cm/cm | |
| 23℃，无缺口1/8 | ASTM D-256 | 1.9%水｜120 | kg·cm/cm | |
| -40℃，无缺口1/8 | ASTM D-256 | 无水｜12.5 | kg·cm/cm | |
| -40℃，无缺口1/8 | ASTM D-256 | 1.9%水｜15 | kg·cm/cm | |
| -40℃，无缺口1/8 | ASTM D-256 | 无水｜12.5 | kg·cm/cm2 | |
| -40℃，无缺口1/8 | ASTM D-256 | 1.9%水｜15 | kg·cm/cm2 | |
| 23℃，V缺口1/2 | ASTM D-256 | 无水｜15 | kg·cm/cm | |
| 23℃，V缺口1/2 | ASTM D-256 | 1.9%水｜20 | kg·cm/cm | |
| 23℃，无缺口1/8 | ASTM D-256 | 无水｜98 | kg·cm/cm | |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| UL-94抗燃级 | 1/32" | UL 94 | 无水｜HB | |
| 1/32" | UL 94 | 1.9%水｜- | ||
| 比热 | 无水｜0.31 | Cal/g·℃ | ||
| 1.9%水｜- | Cal/g·℃ | |||
| J/kg/°C | 1700 | -- | ||
| 无水｜0.37 | Cal/g.°C | |||
| 3%水｜- | Cal/g.°C | |||
| 导热系数 | W/m/K | 0.31 | -- | |
| 热变形温度 | 0.45MPa,未退火 | °C | 210 | -- |
| 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 | 无水｜225 | ℃ |
| 4.6kg/cm2 | ASTM D-648 | 1.9%水｜- | ℃ | |
| 18.6kg/cm2 | ASTM D-648 | 无水｜175 | ℃ | |
| 18.6kg/cm2 | ASTM D-648 | 3%水｜- | ℃ | |
| 4.6kg/cm2 | ASTM D-648 | 无水｜210 | ℃ | |
| 4.6kg/cm2 | ASTM D-648 | 3%水｜- | ℃ | |
| 熔点 | 差示扫描测热计DSC法 | 无水｜225 | ℃ | |
| 差示扫描测热计DSC法 | 3%水｜- | ℃ | ||
| 225 | ℃（℉） | |||
| 差示扫描测热计DSC | 无水｜225 | ℃ | ||
| 差示扫描测热计DSC | 1.9%水｜- | ℃ | ||
| 熔融温度 | °C | 225 | -- | |
| 线形热膨胀系数 | MD | cm/cm/°C | 4.5E-05 | -- |
| 线性热膨胀系数 | ASTM D-696 | 无水｜2-3 | ×10-5cm/cm/℃ | |
| ASTM D-696 | 1.9%水｜- | ×10-5cm/cm/℃ | ||
| ASTM D-696 | 无水｜4.5 | 10-5cm/cm.℃ | ||
| ASTM D-696 | 3%水｜- | |||
| 电气性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 耗散因数5 | 23°C,50Hz | 0.050 | -- | |
| 23°C,1kHz | 0.040 | -- | ||
| 23°C,1MHz | 0.030 | -- | ||
| 介电常数 | 106Hz | ASTM D-150 | 无水｜4.2 | |
| 106Hz | ASTM D-150 | 1.9%水｜4.5 | ||
| 103Hz | ASTM D-150 | 无水｜4.9 | ||
| 103Hz | ASTM D-150 | 1.9%水｜7.4 | ||
| 介电常数5 | 23°C,50Hz | 4.50 | -- | |
| 23°C,1kHz | 4.30 | -- | ||
| 23°C,1MHz | 3.70 | -- | ||
| 介电强度 | 1/8" | ASTM D-149 | 无水｜20 | KV/mm |
| 1/8" | ASTM D-149 | 3%水｜- | KV/mm | |
| 1/8" | ASTM D-149 | 无水｜19 | KV/mm | |
| 1/8" | ASTM D-149 | 1.9%水｜15 | KV/mm | |
| kV/mm | 20 | -- | ||
| 抗电弧性 | 1/8" | ASTM D-495 | 无水｜104 | S |
| 1/8" | ASTM D-495 | 1.9%水｜119 | S | |
| 耐电弧性6 | sec | 120 | -- | |
| 损耗因数 | 106Hz | ASTM D-150 | 无水｜0.02 | |
| 106Hz | ASTM D-150 | 1.9%水｜0.06 | ||
| 50Hz | ASTM D-150 | 无水｜0.03 | ||
| 50Hz | ASTM D-150 | 1.9%水｜0.16 | ||
| 体积电阻率 | ASTM D-257 | 1.9%水｜1012 | Ω.cm | |
| ohms·cm | 1E+15 | 1E+12 | ||
| ASTM D-257 | 无水｜1015 | Ω.cm | ||
| ASTM D-257 | 3%水｜1012-1013 | Ω.cm | ||
| ASTM D257/IEC 60093 | 10^13 | Ω.cm | ||
| 冲击性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 简支梁缺口冲击强度 | -40°C | kJ/m2 | 6.0 | 7.0 |
| 23°C | kJ/m2 | 9.0 | 9.5 | |
| 简支梁无缺口冲击强度 | -40°C | kJ/m2 | 20 | 25 |
| 23°C | kJ/m2 | 50 | ||
| 可燃性(Flammability) | 测试条件 | 测试方法 | 测试结果 | 单位 |
| UL阻燃等级 | HB | -- | ||
| 硬度Hardness | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 洛氏硬度 | M计秤,23°C | 90 | -- | |
| R计秤,80°C | 10 | -- | ||
| R计秤,23°C | 119 | -- | ||
| 其它性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 强化含量 | 无水｜45 | wt% | ||
| 1.9%水｜- | wt% | |||
| 物性性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 比重（密度） | ASTM D792/ISO 1183 | 1.25 | ||
| 吸水率 23℃/24H | ASTM D570/ISO 62 | 1.3 | % | |
| 基本性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 吸水率 | 23℃，24小时 | ASTM D-570 | 无水｜0.9 | % |
| 23℃，24小时 | ASTM D-570 | 1.9%水｜- | % | |
| 23℃，24小时 | ASTM D-570 | 无水｜1.3 | % | |
| 23℃，24小时 | ASTM D-570 | 3%水｜- | % | |
| 其他性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 强化含量 | 无水｜15 | wt% | ||
| 3%水｜- | wt% |