Ultradur? B 4040 G10 BK5110
聚丁烯对苯二甲酸酯
50% 玻璃纤维增强材料
产品说明：
Ultradur B 4040 G10 BK5110 is a pigmented black, injection molding PBT with 50% glass fiber reinforced for technical parts with excellent surface finish.
Applications
Typical applications include automotive exterior, door handles, exterior mirror housings, rear screen, wiper arms.
| 基本信息 |
|
| 填料/增强材料 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.73 |
g/cm3 |
ASTM D792, ISO 1183 |
| 溶化体积流率（MVR）(275°C/2.16 kg) |
6.00 |
cm3/10min |
ISO 1133 |
| 收缩率 - 流动(3.18 mm) |
0.20 |
% |
|
| 吸水率 |
|
|
|
| 饱和 |
0.40 |
% |
ASTM D570 |
| 饱和, 23°C |
0.40 |
% |
ISO 62 |
| 平衡, 50% RH |
0.12 |
% |
ASTM D570 |
| 平衡, 23°C, 50% RH |
0.12 |
% |
ISO 62 |
| Viscosity Number (Reduced Viscosity) |
97.0 |
ml/g |
ISO 1628 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量(23°C) |
16500 |
MPa |
ISO 527-2 |
| 抗张强度 |
|
|
|
| 断裂, 23°C |
140 |
MPa |
ASTM D638 |
| 断裂, 23°C |
155 |
MPa |
ISO 527-2 |
| 伸长率(断裂, 23°C) |
1.5 |
% |
ASTM D638, ISO 527-2 |
| 弯曲模量 |
|
|
|
| 23°C |
13600 |
MPa |
ASTM D790 |
| 23°C |
15000 |
MPa |
ISO 178 |
| 弯曲应力(23°C) |
225 |
MPa |
ISO 178 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度 |
|
|
ISO 179 |
| -30°C |
8.5 |
kJ/m2 |
ISO 179 |
| 23°C |
10 |
kJ/m2 |
ISO 179 |
| 简支梁无缺口冲击强度 |
|
|
ISO 179 |
| -30°C |
69 |
kJ/m2 |
ISO 179 |
| 23°C |
52 |
kJ/m2 |
ISO 179 |
| 悬壁梁缺口冲击强度 |
|
|
|
| -40°C |
64 |
J/m |
ASTM D256 |
| 23°C |
75 |
J/m |
ASTM D256 |
| -40°C |
8.1 |
kJ/m2 |
ISO 180 |
| 23°C |
8.2 |
kJ/m2 |
ISO 180 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
|
| 0.45 MPa, 未退火 |
220 |
°C |
ASTM D648 |
| 0.45 MPa, 未退火 |
221 |
°C |
ISO 75-2/B |
| 1.8 MPa, 未退火 |
215 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火 |
205 |
°C |
ISO 75-2/A |
| 熔融峰值温度 |
223 |
°C |
ASTM D3418, ISO 3146 |
| 线形热膨胀系数 - 流动 |
2.5E-5 |
cm/cm/°C |
|
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 表面电阻率 |
|
|
|
| 1.50 mm |
1.0E+13 |
ohms |
ASTM D257 |
| -- |
1.0E+13 |
ohms |
IEC 60093 |
| 体积电阻率 |
|
|
|
| 1.50 mm |
1.0E+15 |
ohms·cm |
ASTM D257 |
| -- |
1.0E+15 |
ohms·cm |
IEC 60093 |
| 介电常数 |
|
|
IEC 60250 |
| 100 Hz |
4.00 |
|
IEC 60250 |
| 1 MHz |
4.00 |
|
IEC 60250 |
| 耗散因数 |
|
|
IEC 60250 |
| 100 Hz |
1.2E-3 |
|
IEC 60250 |
| 1 MHz |
0.015 |
|
IEC 60250 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
100 到 120 |
°C |
|
| 干燥时间 |
4.0 |
hr |
|
| 建议的最大水分含量 |
0.040 |
% |
|
| 加工（熔体）温度 |
250 到 270 |
°C |
|
| 模具温度 |
60.0 到 100 |
°C |
|
| 注塑压力 |
3.50 到 12.5 |
MPa |
|
| 注射速度 |
快速 |
|
|
| 背压 |
1.00 |
MPa |
|