东莞市铭汇塑胶有限公司
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.493 g/cc | 0.05394 lb/in3 | ISO 1183 |
| 线性成型收缩率,Flow | 0.0030 - 0.0050 cm/cm
@Thickness 2.00 mm
|
0.0030 - 0.0050 in/in
@Thickness 0.0787 in
|
ISO 294-4 |
| 线性成型收缩率，横向 | 0.0050 - 0.0090 cm/cm
@Thickness 2.00 mm
|
0.0050 - 0.0090 in/in
@Thickness 0.0787 in
|
ISO 294-4 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | 91.0 MPa
@Temperature 23.0 °C
|
13200 psi
@Temperature 73.4 °F
|
ISO 527 |
| 伸长率 (断裂) | 2.8 %
@Temperature 23.0 °C
|
2.8 %
@Temperature 73.4 °F
|
ISO 527 |
| 拉伸模量 | 5.70 GPa
@Temperature 23.0 °C
|
827 ksi
@Temperature 73.4 °F
|
ISO 527 |
| 简支梁无缺口冲击强度 | 2.15 J/cm2
@Temperature -30.0 °C
|
10.2 ft-lb/in2
@Temperature -22.0 °F
|
ISO 179/1eU |
| 2.31 J/cm2
@Temperature 23.0 °C
|
11.0 ft-lb/in2
@Temperature 73.4 °F
|
ISO 179/1eU | |
| 简支梁缺口冲击强度 | 0.500 J/cm2
@Temperature -30.0 °C
|
2.38 ft-lb/in2
@Temperature -22.0 °F
|
ISO 179/1eA |
| 0.510 J/cm2
@Temperature 23.0 °C
|
2.43 ft-lb/in2
@Temperature 73.4 °F
|
ISO 179/1eA |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 熔融温度 | 223 °C | 433 °F | 10°C/min; ISO 11357-1/-3 |
| 载荷下热变形温度(1.8 MPa) | 195 °C | 383 °F | ISO 75-1/-2 |
| UL RTI | 130 °C
@Thickness 0.710 mm
|
266 °F
@Thickness 0.0280 in
|
UL 746B |
| 130 °C
@Thickness 1.50 mm
|
266 °F
@Thickness 0.0591 in
|
UL 746B | |
| 130 °C
@Thickness 3.00 mm
|
266 °F
@Thickness 0.118 in
|
UL 746B | |
| UL RTI，机械冲击 | 110 °C
@Thickness 0.710 mm
|
230 °F
@Thickness 0.0280 in
|
UL 746B |
| 110 °C
@Thickness 1.50 mm
|
230 °F
@Thickness 0.0591 in
|
UL 746B | |
| 120 °C
@Thickness 3.00 mm
|
248 °F
@Thickness 0.118 in
|
UL 746B | |
| UL RTI，机械无冲击 | 130 °C
@Thickness 0.710 mm
|
266 °F
@Thickness 0.0280 in
|
UL 746B |
| 130 °C
@Thickness 1.50 mm
|
266 °F
@Thickness 0.0591 in
|
UL 746B | |
| 130 °C
@Thickness 3.00 mm
|
266 °F
@Thickness 0.118 in
|
UL 746B | |
| 可燃性(UL94) | V-0
@Thickness 0.710 mm
|
V-0
@Thickness 0.0280 in
|
UL94 |
| V-0
@Thickness 1.50 mm
|
V-0
@Thickness 0.0591 in
|
UL94 | |
| V-0
@Thickness 3.00 mm
|
V-0
@Thickness 0.118 in
|
UL94 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 250 °C | 482 °F | Optimum; Injection Molding |
| 240 - 260 °C | 464 - 500 °F | Injection Molding | |
| 模具温度 | 60.0 °C | 140 °F | optimum; Injection Molding |
| 10.0 - 110 °C | 50.0 - 230 °F | Injection Molding | |
| 干燥温度 | 100 - 140 °C | 212 - 284 °F | Injection Molding |
| 干燥时间 | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Injection Molding |
| 水分含量 | = 0.040 % | = 0.040 % | Injection Molding |
| 材料描述 | 测试方法 | |
|---|---|---|
| 形式 | Pellets | |
| Generic | PBT | |
| Material Status | Current | |
| 部件标识代码 | PBT-GF15FR(17) | ISO 11469 |
| 加工方法 | Injection Molding | |
| 产品分类 | Extrusion Resins | |
| Glass Reinforced Resins | ||
| 树脂识别 | PBT-GF15FR(17) | ISO 1043 |
| 符合RoHS指令 | Contact Manufacturer |