POM CELCON M140-L1

Celcon? M140-L1 is a general purpose acetal copolymer material with a slightly lower viscosity for improved flow in molding that has been modified to reduce or eliminate noise (squeak) when wearing against itself.

Information provided by Celanese

Physical Properties	Metric	English	Comments
Density	1.40g/cc	0.0506lb/in3	ISO 1183
Density of Compound	1.165g/cc	0.04209lb/in3
Linear Mold Shrinkage, Flow	0.019cm/cm	0.019in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.017cm/cm	0.017in/in	ISO 294-4
Melt Flow	12g/10 min @Load 2.16 kg, Temperature 190 °C	12g/10 min @Load 4.76 lb, Temperature 374 °F	[cm3/10min]; ISO 1133
Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	63.0MPa	9140psi	50mm/min; ISO 527-2/1A
Elongation at Yield	9.5 %	9.5 %	50mm/min; ISO 527-2/1A
Tensile Modulus	2.60GPa	377ksi	50mm/min; ISO 527-2/1A
Flexural Modulus	2.50GPa	363ksi	ISO 178
Izod Impact, Notched (ISO)	5.70kJ/m2	2.71ft-lb/in2	ISO 180/1A
Charpy Impact, Notched	0.600J/cm2	2.86ft-lb/in2	ISO 179/1eA
Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	110μm/m-°C	61.1μin/in-°F	ISO 11359-2
CTE, linear, Transverse to Flow	120μm/m-°C	66.7μin/in-°F	ISO 11359-2
Melting Point	166°C	331°F	10°C/min; ISO 11357-1,-2,-3

POM CELCON M140-L1

特性

POM是一种坚韧有弹性的材料，即使在低温下仍有很好的抗蠕变特性、几何稳定性和抗冲击特性。POM既有均聚物材料也有共聚物材料。均聚物材料具有很好的延展强度、抗疲劳强度，但不易于加工。共聚物材料有很好的热稳定性、化学稳定性并且易于加工。无论均聚物材料还是共聚物材料，都是结晶性材料并且不易吸收水分。POM的高结晶程度导致它有相当高的收缩率，可高达到2%~3.5%。对于各种不同的增强型材料有不同的收缩率。

用途

聚甲醛（POM）是一种性能优良的工程塑料，在国外有“夺钢”、

聚甲醛制品2

超钢”之称。POM具有类似金属的硬度、强度和钢性，在很宽的温度和湿度范围内都具有很好的自润滑性、良好的耐疲劳性，并富于弹性，此外它还有较好的耐化学品性。POM以低于其他许多工程塑料的成本，正在替代一些传统上被金属所占领的市场，如替代锌、黄铜、铝和钢制作许多部件，自问世以来，POM已经广泛应用于电子电气、机械、仪表、日用轻工、汽车、建材、农业等领域。在很多新领域的应用，如医疗技术、运动器械等方面，POM也表现出较好的增长态势。