Ultradur? B 4520
聚丁烯对苯二甲酸酯
产品说明：
Ultradur B 4520 is a medium viscosity, rapidly freezing injection molding grade.
Applications
Typical applications include chassis and housings for home appliances, office and sewing machines, and coil formers.
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| RoHS 合规性 |
|
| 形式 |
|
| 加工方法 |
|
| 多点数据 |
- Isothermal Stress vs. Strain (ISO 11403-1)
- Secant Modulus vs. Strain (ISO 11403-1)
- Shear Modulus vs. Temperature (ISO 11403-1)
- Specific Volume vs Temperature (ISO 11403-2)
- Viscosity vs. Shear Rate (ISO 11403-2)
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.30 |
g/cm3 |
ASTM D792, ISO 1183 |
| 溶化体积流率（MVR）(250°C/2.16 kg) |
19.0 |
cm3/10min |
ISO 1133 |
| 收缩率 - 流动(3.18 mm) |
1.5 |
% |
|
| 吸水率 |
|
|
|
| 饱和 |
0.50 |
% |
ASTM D570 |
| 饱和, 23°C |
0.50 |
% |
ISO 62 |
| 平衡, 50% RH |
0.25 |
% |
ASTM D570 |
| 平衡, 23°C, 50% RH |
0.25 |
% |
ISO 62 |
| Viscosity Number (Reduced Viscosity) |
130.0 |
ml/g |
ISO 1628 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量(23°C) |
2500 |
MPa |
ISO 527-2 |
| 抗张强度 |
|
|
|
| 屈服, 23°C |
60.0 |
MPa |
ASTM D638, ISO 527-2 |
| 屈服, -40°C |
94.0 |
MPa |
ISO 527-2 |
| 屈服, 80°C |
22.0 |
MPa |
ISO 527-2 |
| 屈服, 121°C |
18.0 |
MPa |
ISO 527-2 |
| 伸长率(屈服, 23°C) |
3.7 |
% |
ASTM D638, ISO 527-2 |
| 标称拉伸断裂应变(23°C) |
50 |
% |
ISO 527-2 |
| 拉伸蠕变模量 |
|
|
ISO 899-1 |
| 1 hr |
1800 |
MPa |
ISO 899-1 |
| 1000 hr |
1200 |
MPa |
ISO 899-1 |
| 弯曲模量 |
|
|
|
| 23°C |
2300 |
MPa |
ASTM D790 |
| 23°C |
2400 |
MPa |
ISO 178 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度 |
|
|
ISO 179 |
| -30°C |
3.0 |
kJ/m2 |
ISO 179 |
| 23°C |
6.0 |
kJ/m2 |
ISO 179 |
| 简支梁无缺口冲击强度(23°C) |
无断裂 |
|
ISO 179 |
| 悬壁梁缺口冲击强度 |
|
|
ASTM D256 |
| -40°C |
37 |
J/m |
ASTM D256 |
| 23°C |
43 |
J/m |
ASTM D256 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
|
| 0.45 MPa, 未退火 |
163 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火 |
60.0 |
°C |
ASTM D648, ISO 75-2/A |
| 熔融峰值温度 |
223 |
°C |
ASTM D3418, ISO 3146 |
| 线形热膨胀系数 - 流动 |
1.5E-4 |
cm/cm/°C |
|
| RTI Elec |
|
|
UL 746 |
| 0.750 mm |
130 |
°C |
UL 746 |
| 1.50 mm |
130 |
°C |
UL 746 |
| 2.80 mm |
130 |
°C |
UL 746 |
| RTI Imp |
|
|
UL 746 |
| 0.750 mm |
130 |
°C |
UL 746 |
| 1.50 mm |
130 |
°C |
UL 746 |
| 2.80 mm |
130 |
°C |
UL 746 |
| RTI |
|
|
UL 746 |
| 0.750 mm |
140 |
°C |
UL 746 |
| 1.50 mm |
140 |
°C |
UL 746 |
| 2.80 mm |
140 |
°C |
UL 746 |
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 表面电阻率1 |
1.0E+13 |
ohms |
ASTM D257, IEC 60093 |
| 体积电阻率 |
|
|
|
| 1.50 mm |
1.0E+13 |
ohms·cm |
ASTM D257 |
| -- |
1.0E+13 |
ohms·cm |
IEC 60093 |
| 介电常数 |
|
|
IEC 60250 |
| 100 Hz |
3.40 |
|
IEC 60250 |
| 1 MHz |
3.30 |
|
IEC 60250 |
| 耗散因数 |
|
|
IEC 60250 |
| 100 Hz |
2.0E-3 |
|
IEC 60250 |
| 1 MHz |
0.020 |
|
IEC 60250 |
| 漏电起痕指数 |
550 |
V |
IEC 60112 |
| 可燃性 |
额定值 |
单位制 |
测试方法 |
| UL 阻燃等级 |
|
|
UL 94 |
| 0.750 mm |
HB |
|
UL 94 |
| 1.50 mm |
HB |
|
UL 94 |
| 2.80 mm |
HB |
|
UL 94 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
100 到 120 |
°C |
|
| 干燥时间 |
4.0 |
hr |
|
| 建议的最大水分含量 |
0.040 |
% |
|
| 加工（熔体）温度 |
250 到 270 |
°C |
|
| 模具温度 |
40.0 到 80.0 |
°C |
|
| 注塑压力 |
3.50 到 12.5 |
MPa |
|
| 注射速度 |
快速 |
|
|
| 背压 |
1.00 |
MPa |
|