物性表
物性纠错
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
|---|---|---|---|---|
| 密度 / 比重 | ASTM D-792 | DAM｜1.14 | ||
| ASTM D-792 | 50%RH｜1.14 | |||
| 泰伯磨耗量 | cs-17 Wheel,1000g | DAM｜- | mg/1000 cycles | |
| cs-17 Wheel,1000g | 50%RH｜7 | mg/1000 cycles | ||
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 1%形变时的压应力 | ASTM D-695 | DAM｜33.8 | Mpa | |
| ASTM D-695 | 50%RH｜- | Mpa | ||
| 埃佐冲击强度 | 23℃ | ASTM D-256 | DAM｜53 | J/m |
| 23℃ | ASTM D-256 | 50%RH｜112 | J/m | |
| 断裂伸长率 | 23℃ | ASTM D-638 | DAM｜60 | % |
| 23℃ | ASTM D-638 | 50%RH｜≥300 | % | |
| ASTM D638/ISO 527 | 60 | % | ||
| 剪切强度 | 23℃ | ASTM D-732 | DAM｜66.2 | Mpa |
| 23℃ | ASTM D-732 | 50%RH｜- | Mpa | |
| 拉伸冲击强度 | 短试样23℃ | ASTM D-1822 | DAM｜157 | kJ/m2 |
| 短试样23℃ | ASTM D-1822 | 50%RH｜231 | kJ/m2 | |
| 长试样23℃ | ASTM D-1822 | DAM｜504 | kJ/m2 | |
| 长试样23℃ | ASTM D-1822 | 50%RH｜1470 | kJ/m2 | |
| 拉伸强度 | 23℃ | ASTM D-638 | DAM｜82.7 | Mpa |
| 23℃ | ASTM D-638 | 50%RH｜77.2 | Mpa | |
| ASTM D638/ISO 527 | 82.7 | kg/cm2(MPa)[Lb/in2] | ||
| 洛氏硬度M | ASTM D-785 | DAM｜M79 | ||
| ASTM D-785 | 50%RH｜M59 | |||
| 洛氏硬度R | ASTM D-785 | DAM｜R121 | ||
| ASTM D-785 | 50%RH｜R108 | |||
| 屈服强度 | 23℃ | DAM｜82.7 | Mpa | |
| 23℃ | 50%RH｜58.6 | Mpa | ||
| 屈服伸长率 | ASTM D-638 | DAM｜5 | % | |
| ASTM D-638 | 50%RH｜25 | % | ||
| 揉曲模量 | 23℃ | ASTM D-790 | DAM｜2827 | Mpa |
| 23℃ | ASTM D-790 | 50%RH｜1207 | Mpa | |
| 伸长率 | ASTM D638/ISO 527 | 82.7 | % | |
| 硬度计硬度 | ASTM D-676 | DAM｜89 | ||
| ASTM D-676 | 50%RH｜82 | |||
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| UL可燃性导级 | UL 94 | DAM｜94 | ||
| UL 94 | 50%RH｜V-2 | |||
| 脆化温度 | ASTM D-746 | DAM｜-80 | ℃ | |
| ASTM D-746 | 50%RH｜-65 | ℃ | ||
| 导热系数 | DAM｜0.25 | w/mk | ||
| 50%RH｜- | w/mk | |||
| 荷重形变 | 13.8MPa，50℃ | ASTM D-621 | DAM｜1.4 | % |
| 13.8MPa，50℃ | ASTM D-621 | 50%RH｜- | % | |
| 热畸变温度 | (0.5)×106Pa | ASTM D-648 | DAM｜235 | ℃ |
| (0.5)×106Pa | ASTM D-648 | 50%RH｜- | ℃ | |
| 18×106Pa | ASTM D-648 | DAM｜90 | ℃ | |
| 18×106Pa | ASTM D-648 | 50%RH｜- | ℃ | |
| 熔点 | Fisher Johns法 | ASTM D-789 | DAM｜255 | ℃ |
| Fisher Johns法 | ASTM D-789 | 50%RH｜255 | ℃ | |
| 255 | ℃（℉） | |||
| 熔点结晶 | ASTM D-2177 | DAM｜270 | ℃ | |
| ASTM D-2177 | 50%RH｜- | ℃ | ||
| 线性膨胀系数 | ASTM D696/ISO 11359 | 7×10-5 | mm/mm.℃ | |
| 线性热膨胀系数 | ASTM D-696 | DAM｜7×10-5 | m/m/℃ | |
| ASTM D-696 | 50%RH｜- | m/m/℃ | ||
| 电气性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 耗散因数 | 100Hz(cps) | ASTM D-150 | DAM｜0.01 | |
| 100Hz(cps) | ASTM D-150 | 50%RH｜0.2 | ||
| 106Hz(cps) | ASTM D-150 | DAM｜0.02 | ||
| 106Hz(cps) | ASTM D-150 | 50%RH｜0.1 | ||
| 103Hz(cps) | ASTM D-150 | DAM｜0.02 | ||
| 103Hz(cps) | ASTM D-150 | 50%RH｜0.2 | ||
| 介电常数 | 103Hz(cps) | ASTM D-150 | DAM｜3.9 | |
| 103Hz(cps) | ASTM D-150 | 50%RH｜7.0 | ||
| 100Hz(cps) | ASTM D-150 | DAM｜4.0 | ||
| 100Hz(cps) | ASTM D-150 | 50%RH｜8.0 | ||
| 106Hz(cps) | ASTM D-150 | DAM｜3.6 | ||
| 106Hz(cps) | ASTM D-150 | 50%RH｜4.6 | ||
| ASTM D150/IEC 60250 | 4.0 | |||
| ASTM D150/IEC 60250 | 3.6 | |||
| 体积电阻率 | ASTM D257/IEC 60093 | 1015 | Ω.cm | |
| ASTM D-257 | DAM｜1015 | Ω.cm | ||
| ASTM D-257 | 50%RH｜1013 | Ω.cm | ||
| 物性性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 比重（密度） | ASTM D792/ISO 1183 | 1.14 | ||
| 吸水率 23℃/24H | ASTM D570/ISO 62 | 1.2 | % | |
| 基本性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 吸水率 | 饱和(23℃) | 50%RH｜- | % | |
| 24小时浸渍(23℃) | ASTM D-570 | DAM｜1.2 | % | |
| 24小时浸渍(23℃) | ASTM D-570 | 50%RH｜- | % | |
| 饱和(23℃) | ASTM D-570 | DAM｜8.5 | % | |
| 其他性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 需氧指数 | ASTM D-2863 | DAM｜28 | % | |
| ASTM D-2863 | 50%RH｜31 | % |
PA66 101L（Dupont）PA66美国杜邦101L
PA66 101L（Dupont）PA66美国杜邦101L
【供应】PA66 101L美国杜邦耐磨级经润滑电气性能佳
【供应】PA66 101F美国杜邦耐磨级经润滑易脱模电气性能佳成型周期快
【供应】PA66 ST801美国杜邦超韧级耐低温注射成型
【供应】PA66 ST801A美国杜邦超韧耐寒级注射成型
【供应】PA66 ST801AHS美国杜邦热稳定超韧耐寒级注射成型
【供应】PA66 ST801AW美国杜邦抗紫外线超高韧性注射成型
【供应】PA66 FR10 FR15美国杜邦纯树脂防火阻燃V-0注塑级
【供应】PA66 FR50美国杜邦防火阻燃加25%玻纤V-0注射成型
【供应】PA66 103HSL 103FHS美国杜邦热稳定经润滑耐磨损
【供应】PA66 FR7025V0F美国杜邦热稳定经润滑无卤阻燃V-0
【供应】PA66 FR7026V0F美国杜邦热稳定无卤阻燃V-0
【供应】PA66 FR70M30V0美国杜邦矿物增强加30%矿物填料阻燃V-0
【供应】PA66 FE3071美国杜邦食品级抗冲击耐化学性
【供应】PA66 MT409AHS美国杜邦热稳定抗冲击
【供应】PA66 WRF403美国杜邦加30%玻纤热稳定
纯树脂原料PA66用处:本产物居于高强度、高耐热性、热胀系数和缩短率小，吸水性低，标准稳定性随大气湿度和温度改动而不大，它适合制造凸轮、伐座、收音机零部件、电子外表零件、汽车交通零部件等玻璃纤维增强尼龙66(PA66+GF30)资料的密度1.30-1.40g/cm^3。尼龙中的首要种类是尼龙6和尼龙66，占肯定主导地位，其次是尼龙11，尼龙12，尼龙610，尼龙612，别的还有尼龙 1010，尼龙46，尼龙7，尼龙9，尼龙13，新种类有尼龙6I，尼龙9T和一起尼龙MXD6（阻隔性树脂）等，尼龙的改性种类数量繁复，如增强尼龙，单体浇铸尼龙（MC尼龙），反响注射成型（RIM）尼龙，芳香族尼龙，通明尼龙，高抗冲（超韧）尼龙，电镀尼龙，导电尼龙，阻燃尼龙，尼龙与其他聚合物共混物和合金等，广泛用作金属。