SABIC? COHERE? 8102L
聚烯烃塑料
Saudi Basic Industries Corporation (SABIC)
产品说明：
SABIC? COHERE? 8102L is a ethylene-octene copolymer produced via Nexlene? Technology. It performs well in a wide range of general purpose and high performance LLDPE blown film applications and has excellent processability.
SABIC? COHERE? 8102L does contain Slip and Antiblock.
Applications
Typical application for SABIC? COHERE? 8102L is low temperature sealing layer for high value packaging (low SIT, seal through contamination, toughness improvement).
SABIC? COHERE? 8102L 物性表
| 基本信息 |
|
| 添加剂 |
|
| 特性 |
- Excellent Processability
- 共聚物
- 光滑性
- 抗结块性
- 辛烯共聚单体
|
| 用途 |
|
| 加工方法 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 密度 |
0.902 |
g/cm3 |
ASTM D1505 |
| 熔流率（熔体流动速率）(190°C/2.16 kg) |
1.0 |
g/10 min |
ASTM D1238 |
| 薄膜 |
额定值 |
单位制 |
测试方法 |
| 薄膜厚度 - 经测试 |
50 |
μm |
|
| 割线模量 |
ASTM D882 |
|
|
| 1% 正割, MD |
68.0 |
MPa |
ASTM D882 |
| 1% 正割, TD |
76.0 |
MPa |
ASTM D882 |
| 抗张强度 |
ASTM D882 |
|
|
| MD : 断裂 |
47.0 |
MPa |
ASTM D882 |
| TD : 断裂 |
42.0 |
MPa |
ASTM D882 |
| 伸长率 |
ASTM D882 |
|
|
| MD : 断裂 |
600 |
% |
ASTM D882 |
| TD : 断裂 |
620 |
% |
ASTM D882 |
| 落锤冲击1 |
1000 |
g |
ASTM D1709 |
| 埃尔曼多夫抗撕强度 |
ASTM D1922 |
|
|
| MD |
10 |
g |
ASTM D1922 |
| TD |
17 |
g |
ASTM D1922 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 熔融温度 |
100 |
°C |
内部方法 |
| 光学性能 |
额定值 |
单位制 |
测试方法 |
| 雾度 |
4.0 |
% |
ASTM D1003 |
| 补充信息 |
额定值 |
单位制 |
| Blown Film Melt Temperature |
180 到 200 |
°C |
| Blow-up Ratio |
2.00 到 3.00 |
|
| Properties have been measured on blown film of 50 μm and BUR = 2.5 |
|
|