LEXAN? EXL1414T resin
聚碳酸酯
产品说明：
LEXAN EXL1414T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers extreme low temperature (-40 °C) ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1414T resin is a general purpose product available in transparent and opaque colors and is an excellent candidate for a broad range of applications.
| 特性 |
- 共聚物
- 可加工性，良好
- 快的成型周期
- 流动性中等
- 通用
- 延展性
|
| 用途 |
|
| 外观 |
|
| 加工方法 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.19 |
g/cm3 |
ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率）(300°C/1.2 kg) |
10 |
g/10 min |
ASTM D1238 |
| 溶化体积流率（MVR）(300°C/1.2 kg) |
9.50 |
cm3/10min |
ISO 1133 |
| 收缩率 |
|
|
内部方法 |
| 流动 : 3.20 mm |
0.40 到 0.80 |
% |
内部方法 |
| 横向流动 : 3.20 mm |
0.40 到 0.80 |
% |
内部方法 |
| 吸水率 |
|
|
ISO 62 |
| 饱和, 23°C |
0.12 |
% |
ISO 62 |
| 平衡, 23°C, 50% RH |
0.093 |
% |
ISO 62 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 洛氏硬度(L 计秤) |
87 |
|
ISO 2039-2 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 |
|
|
|
| --1 |
2190 |
MPa |
ASTM D638 |
| -- |
2310 |
MPa |
ISO 527-2/1 |
| 抗张强度 |
|
|
|
| 屈服2 |
57.6 |
MPa |
ASTM D638 |
| 屈服 |
56.8 |
MPa |
ISO 527-2/50 |
| 断裂3 |
59.1 |
MPa |
ASTM D638 |
| 断裂 |
55.3 |
MPa |
ISO 527-2/50 |
| 伸长率 |
|
|
|
| 屈服4 |
5.6 |
% |
ASTM D638 |
| 屈服 |
5.4 |
% |
ISO 527-2/50 |
| 断裂5 |
120 |
% |
ASTM D638 |
| 断裂 |
110 |
% |
ISO 527-2/50 |
| 弯曲模量 |
|
|
|
| 50.0 mm 跨距6 |
2180 |
MPa |
ASTM D790 |
| --7 |
2120 |
MPa |
ISO 178 |
| 弯曲应力 |
|
|
|
| -- |
88.6 |
MPa |
ISO 178 |
| 屈服, 50.0 mm 跨距8 |
92.0 |
MPa |
ASTM D790 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度9 |
|
|
ISO 179/1eA |
| -30°C |
60 |
kJ/m2 |
ISO 179/1eA |
| 23°C |
70 |
kJ/m2 |
ISO 179/1eA |
| 简支梁无缺口冲击强度10 |
|
|
ISO 179/1eU |
| -30°C |
无断裂 |
|
ISO 179/1eU |
| 23°C |
无断裂 |
|
ISO 179/1eU |
| 悬壁梁缺口冲击强度 |
|
|
|
| -30°C |
710 |
J/m |
ASTM D256 |
| 23°C |
820 |
J/m |
ASTM D256 |
| -30°C11 |
55 |
kJ/m2 |
ISO 180/1A |
| 23°C12 |
65 |
kJ/m2 |
ISO 180/1A |
| 无缺口伊佐德冲击强度13 |
|
|
ISO 180/1U |
| -30°C |
无断裂 |
|
ISO 180/1U |
| 23°C |
无断裂 |
|
ISO 180/1U |
| 装有测量仪表的落镖冲击 |
|
|
ASTM D3763 |
| -30°C, Total Energy |
77.4 |
J |
ASTM D3763 |
| 23°C, Total Energy |
75.5 |
J |
ASTM D3763 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
|
| 1.8 MPa, 未退火, 3.20 mm |
121 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距14 |
116 |
°C |
ISO 75-2/Af |
| 维卡软化温度 |
|
|
|
| -- |
139 |
°C |
ASTM D1525, ISO 306/B1201115 |
| -- |
138 |
°C |
ISO 306/B50 |
| Ball Pressure Test(125°C) |
Pass |
|
IEC 60695-10-2 |
| 线形热膨胀系数 |
|
|
|
| 流动 : -40 到 95°C |
6.7E-5 |
cm/cm/°C |
ASTM E831 |
| 流动 : 23 到 80°C |
6.7E-5 |
cm/cm/°C |
ISO 11359-2 |
| 横向 : -40 到 95°C |
8.0E-5 |
cm/cm/°C |
ASTM E831 |
| 横向 : 23 到 80°C |
8.0E-5 |
cm/cm/°C |
ISO 11359-2 |
| RTI Elec |
130 |
°C |
UL 746 |
| RTI |
130 |
°C |
UL 746 |
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 表面电阻率 |
1.0E+15 |
ohms |
ASTM D257 |
| 体积电阻率 |
1.0E+15 |
ohms·cm |
ASTM D257 |
| 可燃性 |
额定值 |
单位制 |
测试方法 |
| UL 阻燃等级 |
|
|
UL 94 |
| 0.800 mm |
HB |
|
UL 94 |
| 3.00 mm |
V-2 |
|
UL 94 |
| 灼热丝易燃指数(3.00 mm) |
960 |
°C |
IEC 60695-2-12 |
| 热灯丝点火温度 |
|
|
IEC 60695-2-13 |
| 0.800 mm |
850 |
°C |
IEC 60695-2-13 |
| 3.00 mm |
850 |
°C |
IEC 60695-2-13 |
| 光学性能 |
额定值 |
单位制 |
测试方法 |
| 透射率(2540 μm) |
82.0 |
% |
ASTM D1003 |
| 雾度(2540 μm) |
3.0 |
% |
ASTM D1003 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
121 |
°C |
|
| 干燥时间 |
3.0 到 4.0 |
hr |
|
| 干燥时间，最大 |
48 |
hr |
|
| 建议的最大水分含量 |
0.020 |
% |
|
| 建议注射量 |
40 到 60 |
% |
|
| 料筒后部温度 |
271 到 293 |
°C |
|
| 料筒中部温度 |
282 到 304 |
°C |
|
| 料筒前部温度 |
293 到 316 |
°C |
|
| 射嘴温度 |
288 到 310 |
°C |
|
| 加工（熔体）温度 |
293 到 316 |
°C |
|
| 模具温度 |
71.1 到 93.3 |
°C |
|
| 背压 |
0.345 到 0.689 |
MPa |
|
| 螺杆转速 |
40 到 70 |
rpm |
|
| 排气孔深度 |
0.025 到 0.076 |
mm |
|
| 备注 |
| 1 . |
50 mm/min |
| 2 . |
类型 1, 50 mm/min |
| 3 . |
类型 1, 50 mm/min |
| 4 . |
类型 1, 50 mm/min |
| 5 . |
类型 1, 50 mm/min |
| 6 . |
1.3 mm/min |
| 7 . |
2.0 mm/min |
| 8 . |
1.3 mm/min |
| 9 . |
80*10*3 sp=62mm |
| 10 . |
80*10*3 sp=62mm |
| 11 . |
80*10*3 |
| 12 . |
80*10*3 |
| 13 . |
80*10*3 |
| 14 . |
80*10*4 mm |
| 15 . |
速率 A (50°C/h), 载荷2 (50N) |