LNP? THERMOCOMP? DX11355 compound
聚碳酸酯
产品说明：
This is a PC based compound with good plating, surface, mechanical performance and flame retardant (Halogen free), a good candidate for Laser Direct Structuring applications.
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 密度 |
1.27 |
g/cm3 |
ASTM D792 |
| 熔流率（熔体流动速率）(300°C/1.2 kg) |
12 |
g/10 min |
ASTM D1238 |
| 收缩率 |
|
|
ASTM D955 |
| 流动 : 24小时 |
0.50 |
% |
ASTM D955 |
| 横向流动 : 24小时 |
0.50 |
% |
ASTM D955 |
| 吸水率(24 hr, 50% RH) |
0.010 |
% |
ASTM D570 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量1 |
2600 |
MPa |
ASTM D638 |
| 抗张强度2 |
|
|
ASTM D638 |
| 屈服 |
58.0 |
MPa |
ASTM D638 |
| 断裂 |
52.0 |
MPa |
ASTM D638 |
| 伸长率3 |
|
|
ASTM D638 |
| 屈服 |
5.4 |
% |
ASTM D638 |
| 断裂 |
70 |
% |
ASTM D638 |
| 弯曲模量4(50.0 mm 跨距) |
2400 |
MPa |
ASTM D790 |
| 弯曲强度5 |
|
|
ASTM D790 |
| 屈服, 50.0 mm 跨距 |
90.0 |
MPa |
ASTM D790 |
| 断裂, 50.0 mm 跨距 |
89.0 |
MPa |
ASTM D790 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 悬壁梁缺口冲击强度(23°C) |
800 |
J/m |
ASTM D256 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度(1.8 MPa, 未退火, 3.20 mm) |
114 |
°C |
ASTM D648 |
| 线形热膨胀系数 |
|
|
ASTM E831 |
| 流动 : -40 到 40°C |
6.2E-5 |
cm/cm/°C |
ASTM E831 |
| 横向 : -40 到 40°C |
6.7E-5 |
cm/cm/°C |
ASTM E831 |
| 电气性能 |
额定值 |
|
测试方法 |
| 相对电容率(1.00 GHz) |
2.92 |
|
IEC 60250 |
| 耗散因数(1.00 GHz) |
7.0E-3 |
|
IEC 60250 |
| 可燃性 |
额定值 |
|
测试方法 |
| UL 阻燃等级(0.600 mm) |
V-0 |
|
UL 94 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
100 到 110 |
°C |
|
| 干燥时间 |
3.0 到 4.0 |
hr |
|
| 干燥时间，最大 |
8.0 |
hr |
|
| 建议的最大水分含量 |
0.020 |
% |
|
| 建议注射量 |
30 到 80 |
% |
|
| 料斗温度 |
60.0 到 80.0 |
°C |
|
| 料筒后部温度 |
250 到 290 |
°C |
|
| 料筒中部温度 |
255 到 295 |
°C |
|
| 料筒前部温度 |
260 到 300 |
°C |
|
| 射嘴温度 |
275 到 300 |
°C |
|
| 加工（熔体）温度 |
275 到 300 |
°C |
|
| 模具温度 |
60.0 到 90.0 |
°C |
|
| 背压 |
0.300 到 0.700 |
MPa |
|
| 螺杆转速 |
40 到 70 |
rpm |
|
| 排气孔深度 |
0.038 到 0.076 |
mm |
|
| 备注 |
| 1 . |
50 mm/min |
| 2 . |
类型 1, 50 mm/min |
| 3 . |
类型 1, 50 mm/min |
| 4 . |
1.3 mm/min |
| 5 . |
1.3 mm/min |