BASF PA6 Capron B3EG6物性参数物性表
|
BASF Ultramid? B3EG6 PA6 GF30(尼龙6-聚酰胺)
The property table is provided bywww.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Density密度
|
1.36g/cc
|
0.0491lb/in3
|
ISO 1183
|
|
Water Absorption吸水率
|
6.3 - 6.9 %
|
6.3 - 6.9 %
|
ISO 62
|
|
Moisture Absorption at Equilibrium吸湿平衡
|
1.9 - 2.3 %
|
1.9 - 2.3 %
|
23°C/50% R.H.; ISO 62
|
|
Viscosity Test
|
140cm3/g
|
140cm3/g
|
Viscosity number; ISO 307
|
|
Linear Mold Shrinkage线性收缩率
|
0.0035cm/cm
|
0.0035in/in
|
|
|
Melt Flow熔体流动速率
|
68g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133
|
|
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Tensile Strength, Yield屈服拉伸强度
|
185MPa
|
26800psi
|
50mm/min; ISO 527
|
|
Elongation at Yield屈服伸长率
|
3.5 %
|
3.5 %
|
50mm/min; ISO 527
|
|
Modulus of Elasticity弹性模量
|
9.50GPa
|
1380ksi
|
ISO 527
|
|
Flexural Strength弯曲强度
|
270MPa
|
39200psi
|
ISO 178
|
|
Flexural Modulus弯曲弹性模量
|
8.60GPa
|
1250ksi
|
ISO 178
|
|
Izod Impact, Notched悬臂梁缺口冲击强度(ISO)
|
15.0kJ/m2
|
7.14ft-lb/in2
|
ISO 180/A
|
|
Charpy Impact Unnotched夏比缺口试样冲击
|
9.50J/cm2
|
45.2ft-lb/in2
|
ISO 179/1eU
|
|
8.00J/cm2 @Temperature -30.0 °C |
38.1ft-lb/in2 @Temperature -22.0 °F |
ISO 179/1eU
|
|
|
Charpy ImPAct, Notched夏比缺口冲击
|
1.50J/cm2
|
7.14ft-lb/in2
|
ISO 179/1eA
|
|
1.10J/cm2 @Temperature -30.0 °C |
5.24ft-lb/in2 @Temperature -22.0 °F |
ISO 179/1eA
|
|
用途：电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座
汽车：散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座
工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输
分类：***PA，导电PA，加纤防火PA，防火PA，抗紫外线耐候PA，高温挤出级PA。
聚酰胺纤维俗称尼龙（Nylon），英文名称Polyamide（简称PA），是分子主链上含有重复酰胺基团—[NHCO]—的热塑性树脂总称。包括脂肪族PA，脂肪—芳香族PA和芳香族PA。其中，脂肪族PA品种多，产量大，应用***，其命名由合成单体具体的碳原子数而定。是美国***化学家卡罗瑟斯和他的科研小组发明的。尼龙[1],是聚酰胺纤维（锦纶）是一种说法.可制成长纤或短纤。