PA6 Zytel 73G15L NC010物性参数物性表
|
DuPont Zytel? 73G15L NC010 Nylon 6（PA6-聚酰胺-尼龙6）
The property table is provided bywww.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Density密度
|
1.23g/cc
|
0.0444lb/in3
|
DAM; ISO 1183
|
|
Filler Content填充的内容
|
15 %
|
15 %
|
DAM
|
|
Water Absorption吸水率
|
2.5 % @Temperature 23.0 °C |
2.5 % @Temperature 73.4 °F |
Equilibrium 50%RH; DAM; ISO 62, Similar to
|
|
7.6 % @Temperature 23.0 °C |
7.6 % @Temperature 73.4 °F |
Saturation, immersed; DAM; ISO 62, Similar to
|
|
|
Linear Mold Shrinkage线性收缩率
|
0.0030cm/cm @Thickness 3.20 mm |
0.0030in/in @Thickness 0.126 in |
Flow; DAM
|
|
0.0090cm/cm @Thickness 1.60 mm |
0.0090in/in @Thickness 0.0630 in |
Transverse; DAM
|
|
|
0.013cm/cm @Thickness 6.40 mm |
0.013in/in @Thickness 0.252 in |
Transverse; DAM
|
|
|
Linear Mold Shrinkage, Flow线性收缩率/流动
|
0.0030cm/cm @Thickness 2.00 mm |
0.0030in/in @Thickness 0.0787 in |
Parallel; DAM; ISO 294-4
|
|
Linear Mold Shrinkage, Transverse线性收缩率/横向
|
0.0080cm/cm @Thickness 2.00 mm |
0.0080in/in @Thickness 0.0787 in |
Normal; DAM; ISO 294-4
|
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Tensile Strength at Break断裂拉伸强度
|
72.0MPa @Temperature 23.0 °C |
10400psi @Temperature 73.4 °F |
50%RH; ISO 527
|
|
135MPa @Temperature 23.0 °C |
19600psi @Temperature 73.4 °F |
DAM; ISO 527
|
|
|
Tensile Strength拉伸强度
|
75.0MPa @Temperature 23.0 °C |
10900psi @Temperature 73.4 °F |
50%RH; ASTM D638
|
|
18600psi @Temperature 73.4 °F |
DAM; ASTM D638
|
||
|
Tensile Stress拉伸应力
|
0.000MPa @Strain 0.000 %, Temperature -40.0 °C |
0.000psi @Strain 0.000 %, Temperature -40.0 °F |
DAM; ISO 11403-1/-2
|
|
19.54MPa @Strain 0.650 %, Temperature -20.0 °C |
2834psi @Strain 0.650 %, Temperature -4.00 °F |
50%RH; ISO 11403-1/-2
|
|
|
39.48MPa @Strain 4.23 %, Temperature 120 °C |
5726psi @Strain 4.23 %, Temperature 248 °F |
50%RH; ISO 11403-1/-2
|
|
|
59.7MPa @Strain 3.93 %, Temperature 40.0 °C |
8660psi @Strain 3.93 %, Temperature 104 °F |
50%RH; ISO 11403-1/-2
|
|
|
79.3MPa @Strain 1.41 %, Temperature 23.0 °C |
11500psi @Strain 1.41 %, Temperature 73.4 °F |
DAM; ISO 11403-1/-2
|
|
|
98.54MPa @Strain 1.69 %, Temperature -20.0 °C |
14290psi @Strain 1.69 %, Temperature -4.00 °F |
DAM; ISO 11403-1/-2
|
|
|
119.64MPa @Strain 2.24 %, Temperature 0.000 °C |
17352psi @Strain 2.24 %, Temperature 32.0 °F |
DAM; ISO 11403-1/-2
|
|
|
139.16MPa @Strain 3.81 %, Temperature 23.0 °C |
20183psi @Strain 3.81 %, Temperature 73.4 °F |
DAM; ISO 11403-1/-2
|
|
|
156.08MPa @Strain 3.17 %, Temperature -20.0 °C |
22638psi @Strain 3.17 %, Temperature -4.00 °F |
DAM; ISO 11403-1/-2
|
|
|
175MPa @Strain 3.20 %, Temperature -40.0 °C |
25400psi @Strain 3.20 %, Temperature -40.0 °F |
DAM; ISO 11403-1/-2
|
|
|
Elongation at Break断裂伸长率
|
3.5 % @Temperature 23.0 °C |
3.5 % @Temperature 73.4 °F |
DAM; ASTM D638
|
|
10 % @Temperature 23.0 °C |
10 % @Temperature 73.4 °F |
50%RH; ISO 527
|
|
|
Tensile Modulus拉伸模量
|
3.50GPa @Temperature 23.0 °C |
508ksi @Temperature 73.4 °F |
50%RH; ISO 527
|
|
6.00GPa @Temperature 23.0 °C |
870ksi @Temperature 73.4 °F |
DAM; ISO 527
|
|
|
Flexural Modulus弯曲弹性模量
|
2.41GPa @Temperature 23.0 °C |
350ksi @Temperature 73.4 °F |
50%RH; ASTM D790
|
|
5.38GPa @Temperature 23.0 °C |
780ksi @Temperature 73.4 °F |
DAM; ASTM D790
|
|
|
Shear Modulus剪切模量
|
0.0170GPa @Temperature 226 °C |
2.47ksi @Temperature 439 °F |
DAM; ISO 6721
|
|
0.396GPa @Temperature 170 °C |
57.4ksi @Temperature 338 °F |
DAM; ISO 6721
|
|
|
0.481GPa @Temperature 80.0 °C |
69.8ksi @Temperature 176 °F |
DAM; ISO 6721
|
|
|
0.663GPa @Temperature 60.0 °C |
96.2ksi @Temperature 140 °F |
DAM; ISO 6721
|
|
PA6美国杜邦73G15L 高强度：GF15%
PA6简介：
结构式：[NH(CH2)m NHCO(CH2)n-2CO]
PA6性质：结晶性热可塑性塑料，有明显熔点，Nylon6 Tm为220~230℃，Nylon66则为260~270℃，Nylon本身 具吸水基故有吸水性，成形前须干燥，温度过高干燥则尼龙粒变色
PA6优点：1、具高抗张强度、2、耐韧、耐冲击性特优、3、自润性、耐磨性佳、耐药品性优、4、低温特性佳、5、具自熄性
缺点：尼龙吸湿性高、长期尺寸精密度及物性受影响。
PA6用途：
电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座
汽 车：散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座
工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输