BASF PA66 Ultramid A3EG6物性参数物性表
|
BASF Ultramid? A3EG6 PA66(尼龙66-聚酰胺)
The property table is provided bywww.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Density密度
|
1.36g/cc
|
0.0491lb/in3
|
ISO 1183
|
|
Water Absorption吸水率
|
5.2 - 5.8 %
|
5.2 - 5.8 %
|
ISO 62
|
|
Moisture Absorption at Equilibrium吸湿平衡
|
1.5 - 1.9 %
|
1.5 - 1.9 %
|
23°C/50% R.H.; ISO 62
|
|
Viscosity Test粘度
|
145cm3/g
|
145cm3/g
|
Viscosity number
|
|
Linear Mold Shrinkage线性收缩率
|
0.0055cm/cm
|
0.0055in/in
|
|
|
Melt Flow熔体流动速率
|
54.4g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133
|
|
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Tensile Strength, Yield屈服拉伸强度
|
190MPa
|
27600psi
|
ISO 527
|
|
Elongation at Yield屈服伸长率
|
3.0 %
|
3.0 %
|
ISO 527
|
|
Modulus of Elasticity弹性模量
|
10.0GPa
|
1450ksi
|
|
|
Flexural Strength弯曲强度
|
280MPa
|
40600psi
|
iso 178
|
|
Flexural Modulus弯曲弹性模量
|
8.60GPa
|
1250ksi
|
ISO 178
|
|
Izod Impact, Notched悬臂梁缺口冲击强度(ISO)
|
11.5kJ/m2
|
5.47ft-lb/in2
|
ISO 180/A
|
|
Charpy Impact Unnotched夏比缺口试样冲击
|
8.50J/cm2
|
40.5ft-lb/in2
|
ISO 179/1eU
|
|
7.00J/cm2 @Temperature -30.0 °C |
33.3ft-lb/in2 @Temperature -22.0 °F |
ISO 179/1eU
|
|
|
Charpy ImPAct, Notched夏比缺口冲击
|
1.30J/cm2
|
6.19ft-lb/in2
|
ISO 179/1eA
|
|
1.00J/cm2 @Temperature -30.0 °C |
4.76ft-lb/in2 @Temperature -22.0 °F |
ISO 179/1eA
|
|
|
Electrical Properties电性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Volume ResiSTivity体积电阻率
|
1.00e 13ohm-cm
|
1.00e 13ohm-cm
|
IEC 60093
|
|
Dielectric Constant介电常数
|
3.5 @Frequency 1.00e 6 Hz |
3.5 @Frequency 1.00e 6 Hz |
IEC 60250
|
|
Dissipation Factor耗散因数
|
0.014 @Frequency 1.00e 6 Hz |
0.014 @Frequency 1.00e 6 Hz |
IEC 60250
|
|
Comparative Tracking Index跟踪指数
|
550V
|
550V
|
IEC 60112
|
|
Thermal Properties热性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
CTE, linear, Parallel to Flow线性热膨胀系数
|
0.200-0.300μm/m-°C @Temperature 23.0 - 80.0 °C |
0.111-0.167μin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359
|
|
CTE, linear, Transverse to Flow线性热膨胀系数/横向
|
0.600-0.700μm/m-°C @Temperature 23.0 - 80.0 °C |
0.333-0.389μin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359
|
|
Specific Heat Capacity比热容
|
1.50J/g-°C
|
0.359BTU/lb-°F
|
|
|
Thermal Conductivity导热系数
|
0.350W/m-K
|
2.43BTU-in/hr-ft2-°F
|
DIN 52612
|
|
Melting Point熔点
|
260°C
|
500°F
|
DIN 53765
|
|
Maximum Service Temperature, Air最高使用温度
|
240°C
|
464°F
|
ISO 527
|
|
Deflection Temperature at热变形温度0.46 MPa (66 psi)
|
250°C
|
482°F
|
ISO 75
|
|
Deflection Temperature at热变形温度1.8 MPa (264 psi)
|
250°C
|
482°F
|
ISO 75
|
|
Flammability, UL94阻燃等级
|
HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
|
Processing Properties加工性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Melt Temperature熔体温度
|
280-300°C
|
536-572°F
|
|
|
Mold Temperature模具温度
|
80.0-90.0°C
|
176-194°F
|
|
用途：电子电器：连PA66中文名称聚酰胺，俗称尼龙双6，系结晶性热塑性工程塑料。
优点：1、具高抗张强度；2、耐韧、耐冲击性特优；3、自润性、耐药品性优；4、低温特性佳；5、具自熄性。
用途：
1、电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座、插座、接头、垫圈等；
2、汽车：散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座、滤油器、变速杆等；
3、工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑轮、电动工具等；
4、其他：电动工具、护罩、风叶、齿轮、机床附件、运动器材、玩具制品、扎带等。
分类：导电PA、加纤防火PA、防火PA、抗紫外线耐候PA、高温挤出级PA。