PA66 Zytel 103FHS NC010中英文物性参数物性表
DuPont Zytel? 103FHS NC010 Nylon 66
The property table is provided bywww.plas-cn.com, welcome to download, reprint please indicate the source!
Physical Properties物理性质
Metric公制数据
English英制数据
Comments测试方法
Specific Gravity比重
1.14g/cc
1.14g/cc
DAM; ASTM D792
Density密度
1.14g/cc
0.0412lb/in3
DAM; ISO 1183
Water Absorption吸水率
1.2 %
@Temperature 23.0 °C
1.2 %
@Temperature 73.4 °F
Immersion 24h; DAM; ASTM D570
8.5 %
@Temperature 23.0 °C
8.5 %
@Temperature 73.4 °F
Saturation, immersed; DAM; ISO 62, Similar to
8.6 %
@Temperature 23.0 °C
8.6 %
@Temperature 73.4 °F
Saturation; DAM; ASTM D570
Linear Mold Shrinkage线性收缩率
0.014cm/cm
@Thickness 1.60 mm
0.014in/in
@Thickness 0.0630 in
Flow; DAM
0.018cm/cm
@Thickness 3.20 mm
0.018in/in
@Thickness 0.126 in
Flow; DAM
Linear Mold Shrinkage, Flow线性收缩率/流动
0.014cm/cm
@Thickness 2.00 mm
0.014in/in
@Thickness 0.0787 in
Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse线性收缩率/横向
0.013cm/cm
@Thickness 2.00 mm
0.013in/in
@Thickness 0.0787 in
Normal; DAM; ISO 294-4
Mechanical Properties力学性能
Metric公制数据
English英制数据
Comments测试方法
Hardness, Rockwell R罗氏硬度R
121
121
DAM; ASTM D785
Tensile Strength拉伸强度
41.0MPa
@Temperature 121 °C
5950psi
@Temperature 250 °F
DAM; ASTM D638
83.0MPa
@Temperature 23.0 °C
12000psi
@Temperature 73.4 °F
DAM; ASTM D638
Tensile Stress拉伸应力
0.000MPa
@Strain 0.000 %,
Temperature -40.0 °C
0.000psi
@Strain 0.000 %,
Temperature -40.0 °F
DAM; ISO 11403-1/-2
7.03MPa
@Strain 1.10 %,
Temperature 60.0 °C
1020psi
@Strain 1.10 %,
Temperature 140 °F
50%RH; ISO 11403-1/-2
25.58MPa
@Strain 14.0 %,
Temperature 120 °C
3710psi
@Strain 14.0 %,
Temperature 248 °F
DAM; ISO 11403-1/-2
29.95MPa
@Strain 21.0 %,
Temperature 100 °C
4344psi
@Strain 21.0 %,
Temperature 212 °F
50%RH; ISO 11403-1/-2
PA66103FHS美国杜邦 热稳定级 经润滑 耐磨损
通途:电气/电子应用领域.连接器.紧固件.汽车领域的应用
PA66 Zytel 103FHS NC010中英文物性参数物性表
DuPont Zytel? 103FHS NC010 Nylon 66
The property table is provided bywww.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
Specific Gravity比重
|
1.14g/cc
|
1.14g/cc
|
DAM; ASTM D792
|
Density密度
|
1.14g/cc
|
0.0412lb/in3
|
DAM; ISO 1183
|
Water Absorption吸水率
|
1.2 % @Temperature 23.0 °C |
1.2 % @Temperature 73.4 °F |
Immersion 24h; DAM; ASTM D570
|
8.5 % @Temperature 23.0 °C |
8.5 % @Temperature 73.4 °F |
Saturation, immersed; DAM; ISO 62, Similar to
|
|
8.6 % @Temperature 23.0 °C |
8.6 % @Temperature 73.4 °F |
Saturation; DAM; ASTM D570
|
|
Linear Mold Shrinkage线性收缩率
|
0.014cm/cm @Thickness 1.60 mm |
0.014in/in @Thickness 0.0630 in |
Flow; DAM
|
0.018cm/cm @Thickness 3.20 mm |
0.018in/in @Thickness 0.126 in |
Flow; DAM
|
|
Linear Mold Shrinkage, Flow线性收缩率/流动
|
0.014cm/cm @Thickness 2.00 mm |
0.014in/in @Thickness 0.0787 in |
Parallel; DAM; ISO 294-4
|
Linear Mold Shrinkage, Transverse线性收缩率/横向
|
0.013cm/cm @Thickness 2.00 mm |
0.013in/in @Thickness 0.0787 in |
Normal; DAM; ISO 294-4
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
Hardness, Rockwell R罗氏硬度R
|
121
|
121
|
DAM; ASTM D785
|
Tensile Strength拉伸强度
|
41.0MPa @Temperature 121 °C |
5950psi @Temperature 250 °F |
DAM; ASTM D638
|
83.0MPa @Temperature 23.0 °C |
12000psi @Temperature 73.4 °F |
DAM; ASTM D638
|
|
Tensile Stress拉伸应力
|
0.000MPa @Strain 0.000 %, Temperature -40.0 °C |
0.000psi @Strain 0.000 %, Temperature -40.0 °F |
DAM; ISO 11403-1/-2
|
7.03MPa @Strain 1.10 %, Temperature 60.0 °C |
1020psi @Strain 1.10 %, Temperature 140 °F |
50%RH; ISO 11403-1/-2
|
|
25.58MPa @Strain 14.0 %, Temperature 120 °C |
3710psi @Strain 14.0 %, Temperature 248 °F |
DAM; ISO 11403-1/-2
|
|
29.95MPa @Strain 21.0 %, Temperature 100 °C |
4344psi @Strain 21.0 %, Temperature 212 °F |
50%RH; ISO 11403-1/-2
|
PA66103FHS美国杜邦 热稳定级 经润滑 耐磨损
通途:电气/电子应用领域.连接器.紧固件.汽车领域的应用
PA66性质:结晶性热可塑性塑料,有明显熔点,Nylon6Tm为220-230℃,Nylon66则为260-270℃,
Nylon本身具吸水基故有吸水性,成形前须干燥,温度过高干燥则尼龙粒变色。
优点:1、具高抗张强度;2、耐韧、耐冲击性特优;3、自润性、**性佳、耐 性优;4、低温特性佳;5、具自熄性;
用途:广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。
电子电器:连接器、卷线轴、计时器、护盖断路器、开关壳座
汽车:散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座
工业零件:椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输
分类:防静电PA,导电PA,加纤防火PA,防火PA,抗紫外线耐候PA,高温挤出级PA。
导电尼龙66:具有良好的**性、耐热性、耐油性及耐化学 性,还大大降低了原材料的吸水率和收缩率,
具有优良的尺寸稳定性及优异的机械强度。能满足静电消散和静电放电(ESD)防护的要求。这些特殊改性材料经特殊配制,
适用于从100到1012欧姆/平方(ohms/sq)的表面电阻范围,可用于注塑及挤出等成型。
有很多*金属和涂装的优点:零件重量较轻,较易处理,运输成本较低。它们的装配简便,制造成本较低,并且较不会受到撞凹,割损和刮伤。
为了标识或美观目的,一些材料可被预先染色,避**时且昂贵的两次着色加工