Vydyne R533首诺PA66料/快速成型PA66
产品牌号详细信息
PA66
产品中文名称:聚酰胺66
产品英文名称:PA66
商标名及牌号:Vydyne R533
PA66物性表 Ascend美国首诺Vydyne R533物性表
|
Ascend Vydyne? R533 Nylon 66（聚氨酯-尼龙66）
本物性表由中国塑商之家www.plas-cn.com塑料网提供，转载请注明来源！
|
|||
|
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Specific Gravity比重
|
1.40g/cc
|
1.40g/cc
|
ISO 1183
|
|
Water Absorption吸水率
|
0.80 % @Time 86400 sec |
0.80 % @Time 24.0 hour |
ISO 62
|
|
Moisture Absorption at Equilibrium吸湿平衡
|
1.8 %
|
1.8 %
|
50% RH; ISO 62
|
|
Linear Mold Shrinkage线性收缩率
|
0.0040cm/cm @Thickness 2.00 mm |
0.0040in/in @Thickness 0.0787 in |
ISO 294-4
|
|
Linear Mold Shrinkage, Transverse线性收缩率/横向
|
0.0090cm/cm @Thickness 2.00 mm |
0.0090in/in @Thickness 0.0787 in |
ISO 294-4
|
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Tensile Strength at Break断裂拉伸强度
|
204MPa
|
29600psi
|
ISO 527
|
|
Elongation at Break断裂伸长率
|
3.0 %
|
3.0 %
|
ISO 527
|
|
Tensile Modulus拉伸模量
|
10.2GPa
|
1480ksi
|
ISO 527
|
|
Flexural Strength弯曲强度
|
290MPa
|
42100psi
|
ISO 178
|
|
Flexural Modulus弯曲弹性模量
|
9.70GPa
|
1410ksi
|
ISO 178
|
|
Poissons Ratio泊松比
|
0.40
|
0.40
|
ISO 527
|
|
Shear Modulus剪切模量
|
3.64GPa
|
528ksi
|
Calculated
|
|
Izod Impact, Notched悬臂梁缺口冲击强度(ISO)
|
12.0kJ/m2
|
5.71ft-lb/in2
|
ISO 180
|
|
Charpy Impact Unnotched夏比缺口试样冲击
|
5.60J/cm2 @Temperature -30.0 °C |
26.7ft-lb/in2 @Temperature -22.0 °F |
ISO 179
|
|
6.70J/cm2 @Temperature 23.0 °C |
31.9ft-lb/in2 @Temperature 73.4 °F |
ISO 179
|
|
|
Charpy ImPAct, Notched夏比缺口冲击
|
1.23J/cm2 @Temperature 23.0 °C |
5.85ft-lb/in2 @Temperature 73.4 °F |
ISO 179
|
|
1.27J/cm2 @Temperature -30.0 °C |
6.04ft-lb/in2 @Temperature -22.0 °F |
ISO 179
|
|
|
Electrical Properties电性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Volume ResiSTivity体积电阻率
|
3.00e 15ohm-cm @Thickness 3.00 mm |
3.00e 15ohm-cm @Thickness 0.118 in |
IEC 60093
|
|
Dielectric Strength介电强度
|
16.0kV/mm @Thickness 3.00 mm |
406kV/in @Thickness 0.118 in |
IEC 60243
|
|
Arc Resistance耐电弧性
|
60-120sec @Thickness 3.00 mm |
60-120sec @Thickness 0.118 in |
UL 746A
|
|
Comparative Tracking Index跟踪指数
|
400-599V @Thickness 3.00 mm |
400-599V @Thickness 0.118 in |
IEC 60112
|
|
Hot Wire Ignition, HWI热线圈点燃测试
|
7.0-15sec @Thickness 0.750 mm |
7.0-15sec @Thickness 0.0295 in |
UL 746A
|
|
7.0-15sec @Thickness 3.00 mm |
7.0-15sec @Thickness 0.118 in |
UL 746A
|
|
|
15-30sec @Thickness 1.50 mm |
15-30sec @Thickness 0.0591 in |
UL 746A
|
|
|
High Amp Arc Ignition, HAI高电流电弧点燃测试
|
=120arcs @Thickness 0.710 mm |
=120arcs @Thickness 0.0280 in |
UL 746A
|
|
=120arcs @Thickness 1.50 mm |
=120arcs @Thickness 0.0591 in |
UL 746A
|
|
|
=120arcs @Thickness 3.00 mm |
=120arcs @Thickness 0.118 in |
UL 746A
|
|
|
High Voltage Arc-Tracking Rate, HVTR高压电弧跟踪速度
|
10.0-25.4mm/min @Thickness 3.00 mm |
0.394-1.00in/min @Thickness 0.118 in |
UL 746A
|
|
Thermal Properties热性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
CTE, linear线性热膨胀系数
|
2.00μm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
1.11μin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359
|
|
CTE, linear, Transverse to Flow线性热膨胀系数/横向
|
8.20μm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
4.56μin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359
|
|
Melting Point熔点
|
260°C
|
500°F
|
ISO 3146
|
|
Deflection Temperature at热变形温度0.46 MPa (66 psi)
|
258°C
|
496°F
|
ISO 75
|
产品说明:
Vydyne? R533 是一种 聚酰胺66(尼龙66) 以 33% 玻璃纤维增强材料填充的 产品。 它 可以通过 注射成型 进行处理,且可以在 北美洲、欧洲或亚太地区中获得。 Vydyne? R533 应用包括 房屋、工程/工业配件、工具、军事应用 和 汽车行业。
特性包括:
阻燃/额定火焰
高强度
坚硬
润滑
优良的脱模剂