东莞市宏阔塑胶有限公司
TPC-ET物性TPE物性参数Hytrel 6356-BKB09物性表
|
本物性表由中国塑商之家www.plas-cn.com塑料网提供，转载请注明来源！
|
|||
|
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Specific Gravity比重
|
1.22g/cc
|
1.22g/cc
|
ASTM D792
|
|
Density密度
|
1.22g/cc
|
0.0441lb/in3
|
ISO 1183
|
|
Water Absorption吸水率
|
0.20 % @Temperature 23.0 °C |
0.20 % @Temperature 73.4 °F |
Equilibrium 50%RH; ISO 62
|
|
0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
Immersion 24h; ASTM D570
|
|
|
0.50 % @Temperature 23.0 °C |
0.50 % @Temperature 73.4 °F |
Immersion 24h; ISO 62
|
|
|
0.60 % @Temperature 23.0 °C |
0.60 % @Temperature 73.4 °F |
Saturation, immersed; ISO 62
|
|
|
Linear Mold Shrinkage线性收缩率
|
0.015cm/cm
|
0.015in/in
|
Flow; ASTM D955
|
|
Linear Mold Shrinkage, Flow线性收缩率/流动
|
0.015cm/cm @Thickness 2.00 mm |
0.015in/in @Thickness 0.0787 in |
Parallel; ISO 294-4
|
|
Linear Mold Shrinkage, Transverse线性收缩率/横向
|
0.015cm/cm @Thickness 2.00 mm |
0.015in/in @Thickness 0.0787 in |
Normal; ISO 294-4
|
|
Melt Flow熔体流动速率
|
8.5g/10 min @Load 2.16 kg, Temperature 230 °C |
8.5g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238
|
|
9.0g/10 min @Load 2.16 kg, Temperature 230 °C |
9.0g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133
|
|
|
Melt Index of Compound熔体流动速率
|
7.0g/10 min @Load 2.16 kg, Temperature 230 °C |
7.0g/10 min @Load 4.76 lb, Temperature 446 °F |
cm3/10 min; ISO 1133
|
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Hardness, Shore D肖氏硬度D
|
= 63
|
= 63
|
ASTM D2240
|
|
= 63
|
= 63
|
ISO 868
|
|
|
58 @Time 15.0 sec |
58 @Time 0.00417 hour |
ISO 868
|
|
|
Tensile Strength at Break断裂拉伸强度
|
41.0MPa @Temperature 23.0 °C |
5950psi @Temperature 73.4 °F |
ASTM D638
|
|
43.0MPa @Temperature 23.0 °C |
6240psi @Temperature 73.4 °F |
ISO 527 (1BA bar)
|
|
|
Tensile Stress拉伸应力
|
0.000MPa @Strain 0.000 %, Temperature -40.0 °C |
0.000psi @Strain 0.000 %, Temperature -40.0 °F |
ISO 527
|
|
9.98MPa @Strain 47.3 %, Temperature 100 °C |
1450psi @Strain 47.3 %, Temperature 212 °F |
ISO 527
|
|
|
10.97MPa @Strain 66.96 %, Temperature 90.0 °C |
1591psi @Strain 66.96 %, Temperature 194 °F |
IS
|
|