东莞市聚隆塑胶原料有限公司
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度 / 比重
|
|||
|
--
|
|
g/cm3
|
ASTM D792 |
|
--
|
1.17
|
g/cm3
|
ISO 1183 |
|
特定体积
|
0.850
|
cm3/g
|
ASTM D792 |
|
熔流率（熔体流动速率）
|
|||
|
250°C/2.16 kg
|
3.8
|
g/10 min
|
ASTM D1238 |
|
250°C/5.0 kg
|
11
|
g/10 min
|
ASTM D1238,ISO 1133 |
|
265°C/2.16 kg
|
6.0
|
g/10 min
|
ASTM D1238 |
|
266°C/5.0 kg
|
20
|
g/10 min
|
ASTM D1238 |
|
250°C/2.16 kg
|
3.0
|
g/10 min
|
ISO 1133 |
|
熔融体积流量（MVR）
|
ISO 1133 | ||
|
250°C/2.16 kg
|
3.0
|
cm3/10min
|
|
|
250°C/5.0 kg
|
10
|
cm3/10min
|
|
|
265°C/2.16 kg
|
6.0
|
cm3/10min
|
|
|
265°C/5.0 kg
|
18
|
cm3/10min
|
|
|
收缩率 - 流动(3.20 mm)
|
1.0 到 1.2
|
%
|
内部方法 |
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
0.28
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.080
|
%
|
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
--2
|
1830
|
MPa
|
ASTM D638 |
|
--3
|
1830
|
MPa
|
内部方法 |
|
--4
|
1810
|
MPa
|
ASTM D638 |
|
--
|
1790
|
MPa
|
ISO 527-1/1 |
|
抗张强度
|
|||
|
屈服5
|
47.0
|
MPa
|
ASTM D638 |
|
屈服6
|
45.0
|
MPa
|
内部方法 |
|
屈服7
|
44.0
|
MPa
|
ASTM D638 |
|
屈服
|
44.0
|
MPa
|
ISO 527-2/5 |
|
屈服
|
47.0
|
MPa
|
ISO 527-2/50 |
|
断裂7
|
50.0
|
MPa
|
ASTM D638 |
|
断裂6
|
47.0
|
MPa
|
内部方法 |
|
断裂5
|
48.0
|
MPa
|
ASTM D638 |
|
断裂
|
43.0
|
MPa
|
ISO 527-2/5,ISO 527-2/50 |
|
伸长率
|
|||
|
屈服7
|
4.6
|
%
|
ASTM D638 |
|
屈服6
|
4.6
|
%
|
内部方法 |
|
屈服5
|
4.0
|
%
|
ASTM D638 |
|
屈服
|
4.1
|
%
|
ISO 527-2/5 |
|
屈服
|
4.6
|
%
|
ISO 527-2/50 |
|
断裂7
|
120
|
%
|
ASTM D638 |
|
断裂6
|
110
|
%
|
内部方法 |
|
断裂5
|
120
|
%
|
ASTM D638 |
|
断裂
|
110
|
%
|
ISO 527-2/5 |
|
断裂
|
120
|
%
|
ISO 527-2/50 |
|
弯曲模量
|
|||
|
50.0 mm 跨距8
|
1660
|
MPa
|
ASTM D790 |
|
--9
|
1860
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
--9,10
|
71.0
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距8
|
70.0
|
MPa
|
ASTM D790 |
|
断裂, 50.0 mm 跨距8
|
69.0
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度11
|
ISO 179/1eA | ||
|
-30°C
|
47
|
kJ/m2
|
|
|
23°C
|
55
|
kJ/m2
|
|
|
悬壁梁缺口冲击强度
|
|||
|
-40°C
|
600
|
J/m
|
ASTM D256 |
|
-30°C
|
650
|
J/m
|
ASTM D256 |
|
-20°C
|
700
|
J/m
|
ASTM D256 |
|
-10°C
|
660
|
J/m
|
ASTM D256 |
|
0°C
|
690
|
J/m
|
ASTM D256 |
|
23°C
|
720
|
J/m
|
ASTM D256 |
|
-40°C12
|
46
|
kJ/m2
|
ISO 180/1A |
|
-30°C12
|
48
|
kJ/m2
|
ISO 180/1A |
|
-20°C12
|
50
|
kJ/m2
|
ISO 180/1A |
|
-10°C12
|
52
|
kJ/m2
|
ISO 180/1A |
|
0°C12
|
55
|
kJ/m2
|
ISO 180/1A |
|
23°C12
|
55
|
kJ/m2
|
ISO 180/1A |
|
装有测量仪表的落镖冲击
|
ASTM D3763 | ||
|
-40°C, Energy at Peak
|
49.0
|
J
|
|
|
-40°C, Total Energy
|
59.0
|
J
|
|
|
-30°C, Energy at Peak
|
49.0
|
J
|
|
|
-30°C, Total Energy
|
61.0
|
J
|
|
|
-20°C, Energy at Peak
|
41.0
|
J
|
|
|
-20°C, Total Energy
|
53.0
|
J
|
|
|
23°C, Energy at Peak
|
44.0
|
J
|
|
|
23°C, Total Energy
|
54.0
|
J
|
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 3.20 mm
|
108
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 6.40 mm
|
117
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距12
|
109
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, 未退火, 3.20 mm
|
83.0
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 6.40 mm
|
95.0
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距12
|
87.0
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
|||
|
--
|
119
|
°C
|
ASTM D152513,ISO 306/B5013 |
|
--
|
122
|
°C
|
ISO 306/B120 |
|
线形热膨胀系数
|
|||
|
流动 : -40 到 95°C
|
9.8E-5
|
cm/cm/°C
|
ASTM E831 |
|
流动 : -30 到 80°C
|
9.8E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
垂直 : -40 到 95°C
|
1.0E-4
|
cm/cm/°C
|
ASTM E831 |
|
垂直 : -30 到 80°C
|
1.0E-4
|
cm/cm/°C
|
ISO 11359-2 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
110
|
°C
|
|
|
干燥时间
|
4.0 到 6.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
50 到 80
|
%
|
|
|
料筒后部温度
|
245 到 265
|
°C
|
|
|
料筒中部温度
|
250 到 270
|
°C
|
|
|
料筒前部温度
|
255 到 275
|
°C
|
|
|
射嘴温度
|
255 到 270
|
°C
|
|
|
加工（熔体）温度
|
260 到 275
|
°C
|
|
|
模具温度
|
65 到 90
|
°C
|
|
|
背压
|
0.300 到 0.700
|
MPa
|
|
|
螺杆转速
|
50 到 80
|
rpm
|
|
|
排气孔深度
|
0.013 到 0.020
|
mm
|
1、本司原料订货500KG以上珠三角地区可送货上门; 省外客户物流，快递或货运; 不便之处敬请谅解!
2、选用物流或者快递的买家，请先确认当地是否有该物流或快递的营业网点。
3、原料到厂后，请不要拆外包装，应先仔细检查原料的外包装是否完好及原料型号是否与您所订购原料型号相匹配。
4、货物送达后，请当面检查，若物流过程中出现大量包装损坏及原料外漏的,请让物流人员出具证明并保存，并立即与我们联系。
5、我们承诺期限内发货，但对承运人效率无法作出保证，如果物流快递超出3天，货运超出5天，请联络我们协助查询。
6、买家也可以根据交易状态中填写的单号信息，自行联系承运方，以便第一时间获知详细信息。