东莞市高创塑胶原料有限公司
TPEE(热塑性聚酯弹性体)/美国杜邦 4057/陶氏杜邦
用途：电子电器,电线电缆,汽车部件,运动器材
重要参数：熔体流动速率:10 g/10min拉伸强度:10.3 MPa断裂伸长率:200 %
生产厂商：陶氏杜邦公司
物理性能额定值 (公制)额定值 (英制)测试方法
| 比重 | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| 密度 | 1.15 g/cc | 0.0415 lb/in3 | ISO 1183 |
| Water Absorption | 5.0 % @Temperature 23.0 °C |
5.0 % @Temperature 73.4 °F |
Immersion 24h; ASTM D570 |
| 5.0 % @Temperature 23.0 °C |
5.0 % @Temperature 73.4 °F |
Immersion 24h; ISO 62 | |
| 线性成型收缩率 | 0.0050 cm/cm | 0.0050 in/in | Flow; ASTM D955 |
| 线性成型收缩率,Flow | 0.010 cm/cm @Thickness 2.00 mm |
0.010 in/in @Thickness 0.0787 in |
ISO 294-4 |
| 线性成型收缩率，横向 | 0.010 cm/cm @Thickness 2.00 mm |
0.010 in/in @Thickness 0.0787 in |
ISO 294-4 |
| 熔体流动速率 | 10 g/10 min @Load 2.16 kg, Temperature 190 °C |
10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| 10 g/10 min @Load 2.16 kg, Temperature 190 °C |
10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
机械性能额定值 (公制)额定值 (英制)测试方法
| 肖氏硬度 (邵氏 D) | ASTM D2240 | ||
| ISO 868 | |||
| 26 @Time 15.0 sec |
26 @Time 0.00417 hour |
ISO 868 | |
| 抗张强度(断裂) | 9.70 MPa @Temperature 23.0 °C |
1410 psi @Temperature 73.4 °F |
ISO 527 (1BA bar) |
| 10.3 MPa @Temperature 23.0 °C |
1490 psi @Temperature 73.4 °F |
ASTM D638 | |
| 抗张强度 | 1.70 MPa @Strain 5.00 %, Temperature 23.0 °C |
247 psi @Strain 5.00 %, Temperature 73.4 °F |
ASTM D638 |
| 2.50 MPa @Strain 10.0 %, Temperature 23.0 °C |
363 psi @Strain 10.0 %, Temperature 73.4 °F |
ISO 527 (1BA bar) | |
| 2.60 MPa @Strain 10.0 %, Temperature 23.0 °C |
377 psi @Strain 10.0 %, Temperature 73.4 °F |
ASTM D638 | |
| 伸长率 (断裂) | 200 % @Temperature 23.0 °C |
200 % @Temperature 73.4 °F |
ASTM D638 |
| 240 % @Temperature 23.0 °C |
240 % @Temperature 73.4 °F |
ISO 527 (1BA bar) | |
| 拉伸模量 | 0.0230 GPa @Temperature 23.0 °C |
3.34 ksi @Temperature 73.4 °F |
ISO 527 |
| 弯曲模量 | 0.00700 GPa @Temperature 100 °C |
1.02 ksi @Temperature 212 °F |
ASTM D790 |
| 0.00700 GPa @Temperature 100 °C |
1.02 ksi @Temperature 212 °F |
ISO 178 | |
| 0.0320 GPa @Temperature 23.0 °C |
4.64 ksi @Temperature 73.4 °F |
ISO 178 | |
| 0.0324 GPa @Temperature 23.0 °C |
4.70 ksi @Temperature 73.4 °F |
ASTM D790 | |
| 0.0500 GPa @Temperature -40.0 °C |
7.25 ksi @Temperature -40.0 °F |
ISO 178 | |
| 0.0620 GPa @Temperature -40.0 °C |
8.99 ksi @Temperature -40.0 °F |
ASTM D790 | |
| 悬壁梁缺口冲击强度 | NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
ASTM D256 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D256 | |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
ISO 180/1A | |
| 简支梁缺口冲击强度 | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eA |
电气性能额定值 (公制)额定值 (英制)测试方法
| 相比耐漏电起痕指数(CTI) | = 600 V @Thickness 3.00 mm, Temperature 23.0 °C |
= 600 V @Thickness 0.118 in, Temperature 73.4 °F |
UL 746A |