LDPE SABIC 2201H3W

Produktbeschreibung
SABIC? LDPE 2201H3W is a grade anti block and slip agent. The grade has very good draw down ability. Films based on 2201H3W combine toughness with high tear strength, good optical properties and low CoF. Application SABIC? LDPE 2201H3W is typically used for thin packaging film purposes, where good optical properties are required. SABIC? LDPE 2201H3W can typically be used for food applications due to very low migration levels. Film properties Film properties have been measured at film of 50 μm with a BUR of 3. The film has been produced on Kiefel IBC blown film line with 200 kg/h. Die size 200 mm, die gap 0.8 mm. This product is not intended for and must not be used in any pharmaceutical/medical applications.
Allgemein
Materialstatus	Kommerziell: Aktiv
Verfügbarkeit	Afrika und Mittlerer OstenAsien PazifikEuropaLateinamerikaNordamerika
Additiv	AntiblockErucamid Gleiten
Merkmale	AntiblockGeringe bis keine MigrationGie?schlickerGute Ausl?ngenGute Ausrei?widerstandGute Z?higkeitNiedrige DichteNiedrige FriktionOptisch
Anwendungen	Industrielle Anwendungen
Verarbeitungsmethoden	Blasfolie

Physikalische Eigenschaften	Nominalwert	Einheit	Prüfmethode
Dichte		g/cm3	ASTM D1505
Schmelze-Masseflie?rate (MFR)(190°C/2,16 kg)		g/10 min	ISO 1133
Mechanische Eigenschaften	Nominalwert	Einheit	Prüfmethode
Reibkoeffizient			ASTM D1894
Einreissfestigkeit			ISO 6383-2
MD		lbf/in
TD		lbf/in
Kunststofffolie	Nominalwert	Einheit	Prüfmethode
Zug-E-Modul - TD		psi	ISO 527-3
Zugfestigkeit			ISO 527-3
TD : Einsinkweg		psi
MD : Bruch		psi
TD : Bruch		psi
Streckdehnung			ISO 527-3
MD : Bruch		%
TD : Bruch		%
Schlagz?higkeit	Nominalwert	Einheit	Prüfmethode
Impact Strength			ASTM D4272
Thermische Eigenschaften	Nominalwert	Einheit	Prüfmethode
Vicat-Erweichungstemperatur		°F	ISO 306/A
Optische Eigenschaften	Nominalwert	Einheit	Prüfmethode
Gl?nzen(45°)			ASTM D2457
Trübung		%	ASTM D1003

LDPE SABIC 2201H3W

(1)乙烯聚合反应过程是一个强烈的放热过程。乙烯的聚合热约为93.5kJ/mol(或3.3kJ/g)，在235MPa、150~300℃下乙烯的比热容为2.51~2.85J/(g·℃)，反应热如果不能及时移去，每1%乙烯发生聚合将使温度升高12~13℃。如果温度过高，还会导致乙烯分解。

(2)在高压下，乙烯已被压缩到密度为0.5g/mL的气密相状态，近似于不能再压缩的液体，此时乙烯分子间的距离显著缩短，从而增加了游离基与乙烯分子的碰撞概率，所以容易发生聚合反应。

(3)高温下增长链的自由基活性大，容易发生链转移反应，所得到的聚合物为带有较多支链的线型结构。通常每1000个碳链原子中含有20~30个支链，结晶度为45%~65%，密度在0.910~0.925g/mL，质轻、具柔性，耐低温性、耐冲击性较好。

LDPE产品性能

低密度聚乙烯其特征主要有以下几点：

(1)薄膜呈微乳白透明色，柔软。强度比高密度聚乙烯小，抗冲击强度则比高密度聚乙烯大。

(2)耐寒、耐低温及耐较高温度。较厚的薄膜能承受90℃热水浸泡的杀菌过程。

(3)防潮性能比较好，化学性能稳定，不溶于一般溶剂。

(4)有较大的透气性，故用作易氧化的食品包装时，其内容物的贮存期不宜过长。

(5)耐油脂性较差，制品能被缓慢溶涨。包装含油脂食品时，久贮后会使食品出现哈喇味。

(6)长时期受紫外线及热作用会老化，影响其物理性能和介电性能。

(7)熔点为110~115℃，加工温度为150~210℃，若在惰性气体中，温度可达300℃仍稳定。但熔体和氧接触易发生降解作用。

LDPE应用领域

低密度聚乙烯的应用范围:适用于调味料、糕点、糖、蜜饯、饼干、奶粉、茶叶、鱼肉松等食品包装。片剂、粉剂等药品包装,衬衫、服装、针织棉制品及化纤制品等纤维制品包装。洗衣粉、洗涤剂、化妆品等日化用品包装。由于单层PE薄膜的机械性能较差,所以通常用作复合包装袋的内层,即多层复合薄膜热封性基材。