东莞市华韵塑胶原料有限公司
防火阻燃级PET FR543 NC010美国杜邦增强级
产品说明:
Rynite? FR543 NC010 is a flame retardant, 43% glass reinforced polyethylene terephthalate. Has a 155C temperature index that is equivalent to many thermosets. Recognized by UL as UL94V-0 at 0.8mm(0.03in).
Information provided by DuPont Performance Polymers
DuPont Performance Polymers Rynite? FR543 NC010 PET 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.79 g/cc | 1.79 g/cc | ASTM D792 |
| 密度 | 1.79 g/cc | 0.0647 lb/in3 | ISO 1183 |
| 填料含量 | 43 % | 43 % | |
| Water Absorption | 0.060 %
@Temperature 23.0 °C
|
0.060 %
@Temperature 73.4 °F
|
50%RH,23°C,24h; ASTM D570 |
| 0.11 %
@Temperature 23.0 °C
|
0.11 %
@Temperature 73.4 °F
|
Equilibrium 50%RH; ISO 62, Similar to | |
| 0.62 %
@Temperature 23.0 °C
|
0.62 %
@Temperature 73.4 °F
|
Saturation, immersed; ISO 62, Similar to | |
| 线性成型收缩率 | 0.0013 cm/cm
@Thickness 1.57 mm
|
0.0013 in/in
@Thickness 0.0618 in
|
Flow |
| 0.0020 cm/cm
@Thickness 3.20 mm
|
0.0020 in/in
@Thickness 0.126 in
|
Flow | |
| 0.0048 cm/cm
@Thickness 1.57 mm
|
0.0048 in/in
@Thickness 0.0618 in
|
Transverse | |
| 0.0065 cm/cm
@Thickness 3.20 mm
|
0.0065 in/in
@Thickness 0.126 in
|
Transverse | |
| 线性成型收缩率,Flow | 0.0025 cm/cm | 0.0025 in/in | Annealed; ISO 294-4 |
| 0.0020 cm/cm
@Thickness 2.00 mm
|
0.0020 in/in
@Thickness 0.0787 in
|
ISO 294-4 | |
| 线性成型收缩率，横向 | 0.0105 cm/cm | 0.0105 in/in | Annealed; ISO 294-4 |
| 0.0075 cm/cm
@Thickness 2.00 mm
|
0.0075 in/in
@Thickness 0.0787 in
|
ISO 294-4 | |
| 化合物熔体指数 | 6.0 g/10 min
@Load 2.16 kg, Temperature 280 °C
|
6.0 g/10 min
@Load 4.76 lb, Temperature 536 °F
|
cm3/10 min; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | 95 | 95 | ASTM D785 |
| 102 | 102 | ISO 2039/2 | |
| 洛氏硬度（R 级） | 120 | 120 | ASTM D785 |
| 122 | 122 | ISO 2039/2 | |
| 抗张强度(断裂) | 170 MPa
@Temperature 23.0 °C
|
24700 psi
@Temperature 73.4 °F
|
ISO 527 |
| 抗张强度 | 55.2 MPa
@Temperature 150 °C
|
8010 psi
@Temperature 302 °F
|
ASTM D638 |
| 86.5 MPa
@Temperature 90.0 °C
|
12500 psi
@Temperature 194 °F
|
ASTM D638 | |
| 172 MPa
@Temperature 23.0 °C
|
24900 psi
@Temperature 73.4 °F
|
ASTM D638 | |
| 210 MPa
@Temperature -40.0 °C
|
30500 psi
@Temperature -40.0 °F
|
ASTM D638 | |
| 22.4 MPa
@Strain 0.470 %, Temperature 150 °C
|
3250 psi
@Strain 0.470 %, Temperature 302 °F
|
ISO 527 | |
| 27.22 MPa
@Strain 0.430 %, Temperature 120 °C
|
3948 psi
@Strain 0.430 %, Temperature 248 °F
|
ISO 527 | |
| 27.5 MPa
@Strain 0.160 %, Temperature 0.000 °C
|
3990 psi
@Strain 0.160 %, Temperature 32.0 °F
|
ISO 527 | |
| 28.39 MPa
@Strain 0.350 %, Temperature 90.0 °C
|
4118 psi
@Strain 0.350 %, Temperature 194 °F
|
ISO 527 | |
| 29.0 MPa
@Strain 0.140 %, Temperature -40.0 °C
|
4210 psi
@Strain 0.140 %, Temperature -40.0 °F
|
ISO 527 |
pet材料可在120℃温度范围内长期使用，短期使用可耐150℃高温，可耐-70℃低温，且高、低温时对其机械性能影响很小。
pet材料，英文名为Polyethylene terephthalate，俗称涤纶树脂，是热塑性聚酯中最主要的品种。
它是对苯二甲酸与乙二醇的缩聚物，与PBT一起统称为热塑性聚酯，或饱和聚酯。1946年英国发表了第一个制备PET的专利，1949年英国ICI公式完成中试，但美国杜邦公司购买专利后，1953年建立了生产装置，在世界最先实现工业化生产。初期PET几乎都用于
合成纤维(我国俗称涤纶、的确良)。80年代以来，PET作为工程塑料有突破性的发展，相继研制出成核剂和结晶促进剂，目前PET与PBT一起作为热塑性聚酯，成为五大工程塑料之一。PET分为纤维级聚酯切片和非纤维级聚酯切片。①纤维级聚酯用于制造涤纶短纤维
和涤纶长丝，是供给涤纶纤维企业加工纤维及相关产品的原料。涤纶作为化纤中产量最大的品种。②非纤维级聚酯还有瓶类、薄膜等用途，广泛应用于包装业、电子电器、医疗卫生、建筑、汽车等领域，其中包装是聚酯最大的非纤应用市场，同时也是PET增长最快
的领域。作为包装材料PET优点:1.有良好的力学性能，冲击强度是其他薄膜的3~5倍，耐折性好。2.耐油、耐脂肪、耐烯酸、稀碱，耐大多数溶剂。3.具有优良的耐高、低温性能，可在120℃温度范围内长期使用，短期使用可耐150℃高温，可耐-70℃低温，且高、
低温时对其机械性能影响很小。4.气体和水蒸气渗透率低，既有优良的阻气、水、油及异味性能。5.透明度高，可阻挡紫外线，光泽性好。
6.无毒、无味，卫生安全性好，可直接用于食品包装。
pet材料耐温就是固定的，答案都是统一的。