PC/ABS LUPOY GN5001RFH

Physical Properties	Metric	English	Comments
Specific Gravity	1.19g/cc	1.19g/cc	ASTM D792
Maximum Moisture Content	0.020	0.020	Injection Molding
Linear Mold Shrinkage, Flow	0.0040-0.0060cm/cm @Thickness 3.20 mm	0.0040-0.0060in/in @Thickness 0.126 in	ASTM D955
Melt Flow	15g/10 min @Load 2.16 kg, Temperature 250 ?°C	15g/10 min @Load 4.76 lb, Temperature 482 ?°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	113	113	ASTM D785
Tensile Strength, Yield	62.8MPa @Thickness 3.20 mm	9100psi @Thickness 0.126 in	50mm/min; ASTM D638
Elongation at Break	= 80 % @Thickness 3.20 mm	= 80 % @Thickness 0.126 in	50mm/min; ASTM D638
Flexural Yield Strength	93.2MPa @Thickness 3.20 mm	13500psi @Thickness 0.126 in	10mm/min; ASTM D790

PC/ABS LUPOY GN5001RFH

PC/ABS，聚碳酸酯和丙烯腈-丁二烯-苯乙烯共聚物和混合物，是由聚碳酸酯（Polycarbonate）和聚丙烯腈（ABS）合金而成的热可塑性塑胶，结合了两种材料的优异特性，ABS材料的成型性和PC的机械性、冲击强度和耐温、抗紫外线（UV）等性质，可广泛使用在汽车内部零件、事务机器、通信器材、家电用品及照明设备上。

性能

1、一般性能

ABS工程塑料外观为不透明呈象牙色粒料，其制品可着成五颜六色，并具有高光泽度。ABS相对密度为1.05左右，吸水率低。ABS同其他材料的结合性好，易于表面印刷、涂层和镀层处理。ABS的氧指数为18~20，属易燃聚合物，火焰呈黄色，有黑烟，并发出特殊的肉桂味。

2、力学性能

ABS有优良的力学性能，其冲击强度极好，可以在极低的温度下使用：ABS的耐磨性优良，尺寸稳定性好，又具有耐油性，可用于中等载荷和转速下的轴承。ABS的耐蠕变性比PSF及PC大，但比PA及POM小。ABS的弯曲强度和压缩强度属塑料中较差的。ABS的力学性能受温度的影响较大。

3、热学性能

ABS的热变形温度为93~118℃，制品经退火处理后还可提高10℃左右。ABS在-40℃时仍能表现出一点的韧性，可在-40~100℃的温度范围内使用。

4、电学性能

ABS的电绝缘性较好，并且几乎不受温度、湿度和频率的影响，可在大多数环境下使用。

5、环境性能

ABS不受水、无机盐、碱及多种酸的影响，但可溶于酮类、醛类及氯代烃中，受冰乙酸、植物油等侵蚀会产生应力开裂。ABS的耐候性差，在紫外光的作用下易产生降解；于户外半年后，冲击强度下降一半