PC/ABS LUPOY GN5001RFT
Lupoy? GN5001RFT是一种聚碳酸酯 丙烯腈丁二烯苯乙烯(PC ABS)材料,。 该产品在北美洲、拉丁美洲、欧洲或亚太地区有供货,加工方式为:注射成型。
Lupoy? GN5001RFT的主要特性有:
阻燃/额定火焰
Flame Retardant
无卤素
典型应用领域包括:
电气/电子应用
房屋
| Physical | Nominal Value |
Unit |
Test Method |
Density / Specific Gravity |
ASTM D792 | ||
Melt Mass-Flow Rate (MFR)(250°C/2.16 kg) |
g/10 min |
ASTM D1238 | |
Molding Shrinkage - Flow(73°F, 0,126 in, Injection Molded) |
in/in |
ASTM D955 | |
| Mechanical | Nominal Value |
Unit |
Test Method |
Tensile Strength2(Yield, 73°F, 0,126 in, Injection Molded) |
psi |
ASTM D638 | |
Tensile Elongation2(Break, 73°F, 0,126 in, Injection Molded) |
% |
ASTM D638 | |
Flexural Modulus3(73°F, 0,126 in, Injection Molded) |
psi |
ASTM D790 | |
Flexural Strength3(73°F, 0,126 in, Injection Molded) |
psi |
ASTM D790 | |
| Impact | Nominal Value |
Unit |
Test Method |
Notched Izod Impact(73°F, 0,126 in, Injection Molded) |
ft·lb/in |
ASTM D256 | |
| Thermal | Nominal Value |
Unit |
Test Method |
Deflection Temperature Under Load(66 psi, Unannealed, 0,252 in, Injection Molded) |
°F |
ASTM D648 | |
RTI Elec |
°F |
UL 746 | |
RTI Imp |
°F |
UL 746 | |
RTI Str |
°F |
UL 746 |
PC/ABS LUPOY GN5001RFT
PC/ABS合金，PC与ABS共混物可以综合PC和ABS的优良性能，提高ABS的耐热性、抗冲击和拉伸强度，降低PC成本和熔体粘度，改善加工性能，减少制品内应力和冲击强度对制品厚度的敏感性。PC/ABS合金发展迅速，全球产量约为80万吨/年左右，世界各大公司纷纷开发推出PC/ABS合金新品种，如阻燃、玻纤增强、电镀、耐紫外线等品种，尤其是在汽车工业中得到广泛应用，另外还广泛应用于计算机、复印机和电子电气部件等。我国也开始一定研究和生产，如上海杰事杰公司的PC/ABS合金材料已应用于汽车装饰件、灯壳和耐热电器壳体；中科院长春应用化学所开发的高耐热、高耐热高抗冲、高耐热阻燃三个品级的PC/ABS合金材料已被国内数家汽车制造公司使用，用做前装饰板、仪表板及物品箱盖专用料等。兰州大学研究在PC/ABS共混体系中加入高压聚乙烯进行增容改性，得到混合物流动性好且低温韧性与模量几乎不受影响，适用于制作薄壁板材；国内研究人员为了降低PC/ABS两相之间的界面能，在PC和ABS中加入抗冲击剂MBS，合金的空冲击度可以达到极高值，