TPEE HYTREL HTR4275 BK316
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
Density密度
|
1.16g/cc
|
0.0419lb/in3
|
ISO 1183
|
Water Absorption吸水率
|
0.20 % @Temperature 23.0 °C |
0.20 % @Temperature 73.4 °F |
Equilibrium 50%RH; ISO 62
|
0.50 % @Temperature 23.0 °C, Time 86400 sec |
0.50 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570
|
|
Linear Mold Shrinkage, Flow线性收缩率/流动
|
0.017cm/cm @Thickness 2.00 mm |
0.017in/in @Thickness 0.0787 in |
Parallel; ISO 294-4, Similar
|
0.015-0.020cm/cm @Thickness 1.00 mm |
0.015-0.020in/in @Thickness 0.0394 in |
Parallel; Blow Molded; ISO 294-4, Similar
|
|
Linear Mold Shrinkage, Transverse线性收缩率/横向
|
0.019cm/cm @Thickness 2.00 mm |
0.019in/in @Thickness 0.0787 in |
Normal; ISO 294-4, Similar
|
0.022-0.027cm/cm @Thickness 1.00 mm |
0.022-0.027in/in @Thickness 0.0394 in |
Normal; Blow Molded; ISO 294-4, Similar
|
|
Melt Flow熔体流动速率
|
0.50g/10 min @Load 2.16 kg, Temperature 230 °C |
0.50g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133
|
TPEE HYTREL HTR4275 BK316
TPEE性能:
热性能
TPEE具有优异的耐热性能,硬度越高,耐热性越好;TPEE在110~140℃连续加热10h基本不失重,在160℃和180℃分别加热10h,失重仅为0.05%和0.1%,因而TPEE的使用温度非常高,短期使用温度更高,能适应汽车生产线上的烘漆温度(150~160℃),并且它在高低温下机械性能损失小。TPEE在120℃以上使用,其拉伸强度远远高于TPU此外TPEE还具有出色的耐低温性能,TPEE脆点低于-70℃并且硬度越低,耐寒性越好,大部分TPEE可在-40℃下长期使用。
耐化学介质性
TPEE具有极佳的耐油性,在室温下能耐大多数极性液体化学介质(如酸、碱、胺二醇类化合物),但对卤代烃(氟里昂除外)及酚类的作用却无能为力,其耐化学品的能力随其硬度的提高而提高。TPEE对大多数有机溶剂、燃料及气体的抗溶胀性能和抗渗透性能是好的,对燃油渗透性仅为氯丁胶、氯磺化聚乙烯、丁腈胶等耐油橡胶的1/3~1/300但TPEE耐热水性较差,添加聚碳酰亚胺稳定剂可以明显改善其抗水解性能。
耐老化性
TPEE在很多不同条件下,如在水雾、臭氧、室外大气老化等条件下,化学稳定性优良。象大多数弹性体一样,在紫外光作用下会发生降解,因此对于室外应用或制品受阳光照射的条件,配方中应添加紫外光防护助剂,其中包括炭黑和各种颜料或其它屏蔽材料;此外TPEE还具有不同程度的水解性。
TPEE应用
TPEE主要用于要求减震、耐冲击、耐曲挠、密封性和弹性、耐油、耐化学品并要求足够强度的领域。如:聚合物改性、汽车部件、耐高低温电线护套、液压软管、鞋材、传动皮带、旋转成型轮胎、挠性连轴节、消音齿轮、电梯滑道、化工设备管道阀件中的防腐耐磨耐高低温材料等。