ASI POLYPROPYLENE 1102-01 PP
ASI POLYPROPYLENE 1188-01 PP
ASI POLYPROPYLENE 1255H-01 PP
ASI POLYPROPYLENE 1259 PP
ASI POLYPROPYLENE 1277A-01 PP
ASI POLYPROPYLENE 1277E-01 PP
ASI POLYPROPYLENE 1329 PP
ASI POLYPROPYLENE 1329H-01 PP
ASI POLYPROPYLENE 1349 PP
ASI POLYPROPYLENE 1404-01 PP
ASI POLYPROPYLENE 1407H-01 PP
ASI POLYPROPYLENE 1449-01 PP
ASI POLYPROPYLENE 1467-01 PP
ASI POLYPROPYLENE 1498-01 PP
ASI POLYPROPYLENE 1500-01 PP
ASI POLYPROPYLENE 1500X-01 PP
ASI POLYPROPYLENE 1579 PP
ASI POLYPROPYLENE 1667-01 PP
ASI POLYPROPYLENE 1692 PP
ASI POLYPROPYLENE 1901-01 PP
ASI POLYPROPYLENE 1930-01 PP
ASI POLYPROPYLENE 2173-01 PP
ASI POLYPROPYLENE 2175 PP
ASI POLYPROPYLENE 3052X-01 PP
ASI POLYPROPYLENE 3353-01 PP
ASI POLYPROPYLENE 3479-01 PP
ASI POLYPROPYLENE 3486-01 PP
ASI POLYPROPYLENE 3495 PP
ASI POLYPROPYLENE 3515 PP
ASI POLYPROPYLENE 3521-01 PP
ASI POLYPROPYLENE 828-01 PP
ASI POLYPROPYLENE 829-01 PP
ASI POLYPROPYLENE 984 PP
ASI POLYPROPYLENE PP 3480-01 PP
ASI POLYPROPYLENE PP 828H-01 PP
温馨提示;因塑料行情波动频繁,网页上的报价会与当天实际报价有差异,
ASI POLYPROPYLENE 1259 物性表
| 基本信息 |
|
| 特性 |
- 低翘曲性
- 抗冲共聚物
- 可加工性，良好
- 快的成型周期
- 中等抗撞击性
|
| 用途 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
0.900 |
g/cm3 |
ASTM D792 |
| 熔流率（熔体流动速率）(230°C/2.16 kg) |
8.0 |
g/10 min |
ASTM D1238 |
| 吸水率(24 hr) |
0.030 |
% |
ASTM D570 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 洛氏硬度(R 级) |
75 |
|
ASTM D785 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 抗张强度1(屈服) |
24.1 |
MPa |
ASTM D638 |
| 伸长率(屈服) |
7.0 |
% |
ASTM D638 |
| 弯曲模量 |
1140 |
MPa |
ASTM D790 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 悬壁梁缺口冲击强度 |
130 |
J/m |
ASTM D256 |
| 无缺口悬臂梁冲击 |
1600 |
J/m |
ASTM D256 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
ASTM D648 |
| 0.45 MPa, 未退火 |
90.6 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火 |
57.2 |
°C |
ASTM D648 |
| 熔融温度2 |
166 |
°C |
内部方法 |
| 可燃性 |
额定值 |
单位制 |
|
| 燃烧速率 |
36 |
mm/min |
|
| 备注 |
| 1 . |
51 mm/min |
| 2 . |
Fisher Johns |