Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion thermoforming applications and also for injection molding applications where higher stiffness is needed.

Tensile Stress, yld, Type I, 5 mm/min

64

MPa

ASTM D 638

Tensile Stress, brk, Type I, 5 mm/min

50

MPa

ASTM D 638

Tensile Strain, yld, Type I, 5 mm/min

4.9

%

ASTM D 638

Tensile Strain, brk, Type I, 5 mm/min

80

%

ASTM D 638

Tensile Modulus, 5 mm/min

3570

MPa

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

110

MPa

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

3500

MPa

ASTM D 790

Tensile Stress, yield, 5 mm/min

59

MPa

ISO 527

Tensile Stress, break, 5 mm/min

65

MPa

ISO 527

Tensile Stress, yield, 50 mm/min

63

MPa

ISO 527

Tensile Stress, break, 50 mm/min

50

MPa

ISO 527

Tensile Strain, yield, 5 mm/min

3.6

%

ISO 527

Tensile Strain, break, 5 mm/min

101

%

ISO 527

Tensile Strain, yield, 50 mm/min

3.5

%

ISO 527

Tensile Strain, break, 50 mm/min

97

%

ISO 527

Tensile Modulus, 1 mm/min

3660

MPa

ISO 527

Flexural Stress, yield, 2 mm/min

106

MPa

ISO 178

Flexural Modulus, 2 mm/min

3560

MPa

ISO 178

Hardness, Rockwell R

98

-

ISO 2039-2

Izod Impact, notched, 23°C

500

J/m

ASTM D 256

Izod Impact, notched, -30°C

90

J/m

ASTM D 256

Instrumented Impact Total Energy, 23°C

45

J

ASTM D 3763

Izod Impact, notched 80*10*3 +23°C

45

kJ/m2

ISO 180/1A

Izod Impact, notched 80*10*3 -30°C

10

kJ/m2

ISO 180/1A

Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm

45

kJ/m2

ISO 179/1eA

Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm

10

kJ/m2

ISO 179/1eA

Vicat Softening Temp, Rate B/50

106

°C

ASTM D 1525

HDT, 1.82 MPa, 3.2mm, unannealed

90

°C

ASTM D 648

CTE, -40°C to 40°C, flow

5.7E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow

7.E-05

1/°C

ASTM E 831

Thermal Conductivity

0.3

W/m-°C

ISO 8302

CTE, -40°C to 40°C, flow

5.2E-05

1/°C

ISO 11359-2

CTE, -40°C to 40°C, xflow

6.E-05

1/°C

ISO 11359-2

CTE, 23°C to 60°C, flow

5.2E-05

1/°C

ISO 11359-2

CTE, 23°C to 60°C, xflow

6.E-05

1/°C

ISO 11359-2

Ball Pressure Test, 75°C +/- 2°C

pass

-

IEC 60695-10-2

Ball Pressure Test, approximate maximum

95

°C

IEC 60695-10-2

Vicat Softening Temp, Rate B/50

112

°C

ISO 306

Vicat Softening Temp, Rate B/120

114

°C

ISO 306

HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm

99

°C

ISO 75/Be

HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm

89

°C

ISO 75/Ae

Relative Temp Index, Elec

60

°C

UL 746B

Relative Temp Index, Mech w/impact

60

°C

UL 746B

Relative Temp Index, Mech w/o impact

60

°C

UL 746B

Specific Gravity

1.28

-

ASTM D 792

Mold Shrinkage, flow, 3.2 mm

0.4 - 0.6

%

SABIC Method

Melt Flow Rate, 260°C/5.0 kgf

11.5

g/10 min

ASTM D 1238

Density

1.27

g/cm3

ISO 1183

Water Absorption, (23°C/sat)

0.3

%

ISO 62

Moisture Absorption (23°C / 50% RH)

0.1

%

ISO 62

Melt Volume Rate, MVR at 260°C/5.0 kg

9

cm3/10 min

ISO 1133

Dielectric Strength, in oil, 0.8 mm

38

kV/mm

IEC 60243-1

Dielectric Strength, in oil, 1.6 mm

26

kV/mm

IEC 60243-1

Dielectric Strength, in oil, 3.2 mm

17

kV/mm

IEC 60243-1

Relative Permittivity, 50/60 Hz

2.9

-

IEC 60250

Relative Permittivity, 1 MHz

2.8

-

IEC 60250

Dissipation Factor, 50/60 Hz

0.003

-

IEC 60250

Dissipation Factor, 1 MHz

0.004

-

IEC 60250

Comparative Tracking Index

250

V

IEC 60112

UL Recognized, 94V-0 Flame Class Rating (3)

1.5

mm

UL 94