PRIMACOR? 3004
Copolymer
产品说明：
PRIMACOR? 3004 is an ethylene acrylic acid copolymer designed for extrusion/coextrusion coating and laminating. It provides excellent hot tack and adhesion to metallic, paper and polyethylene substrates with excellent heat seal strength, even through many oil and powdered products. This resin also offers outstanding resistance to delamination, as well as excellent toughness and environmental stress crack resistance (ESCR).
- Excellent draw down and edge stability
- Excellent product resistance
- Excellent hot tack, heat seal, toughness
- High performance sealant or tie layer
Complies with:
- U.S. FDA 21 CFR 177.1310(a)(1)
Consult the regulations for complete details.
| 基本信息 |
|
| 机构评级 |
- FDA 21 CFR 177.1310 (a) 1
- 欧洲 No 10/2011
|
| 形式 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
0.938 |
g/cm3 |
ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率）1(190°C/2.16 kg) |
8.5 |
g/10 min |
ASTM D1238, ISO 1133 |
| 共聚单体含量2 |
9.7 |
% |
|
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 抗张强度 |
|
|
ASTM D638, ISO 527-2 |
| 屈服, 模压成型 |
7.93 |
MPa |
ASTM D638, ISO 527-2 |
| 断裂, 模压成型 |
17.6 |
MPa |
ASTM D638, ISO 527-2 |
| 伸长率(断裂, 模压成型) |
600 |
% |
ASTM D638, ISO 527-2 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 维卡软化温度 |
81.1 |
°C |
ASTM D1525, ISO 306 |
| 溶融温度（DSC） |
98.0 |
°C |
内部方法 |
| 挤出 |
额定值 |
单位制 |
测试方法 |
| 熔体温度 |
260 到 290 |
°C |
|
| 内缩量(288°C, 25.4 μm) |
50.8 |
mm |
内部方法 |
| 最小涂层厚度 |
10 |
μm |
内部方法 |
| 最小涂层重量 |
9.8 |
g/m2 |
内部方法 |