ABS Lustran 488

Physical Properties	Metric	English	Comments
Density	1.06g/cc	0.0383lb/in3
Melt Flow	19g/10 min @Load 10.0 kg, Temperature 220 °C	19g/10 min @Load 22.0 lb, Temperature 428 °F	cm3/10 min.
Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	46.3MPa	6720psi
Elongation at Break	19 %	19 %	Nominal
Elongation at Yield	3.5 %	3.5 %
Tensile Modulus	2.36GPa	342ksi
Charpy Impact Unnotched	9.50J/cm2 @Temperature -30.0 °C	45.2ft-lb/in2 @Temperature -22.0 °F
Charpy Impact, Notched	3.20J/cm2	15.2ft-lb/in2
Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	90.0μm/m-°C @Temperature 20.0 °C	50.0μin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	93.0°C	199°F
Deflection Temperature at 1.8 MPa (264 psi)	85.0°C	185°F
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	UL Recognized
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	UL Recognized
Processing Properties	Metric	English	Comments
Melt Temperature	250°C	482°F	Injection Moldin

ABS Lustran 488

成型性能

无定形材料,流动性中等,吸湿大,必须充分干燥,表面要求光泽的塑件须长时间预热干燥80-90度,3小时；

宜取高料温,高模温,但料温过高易分解(分解温度为270度).对精度较高的塑件,模温宜取50-60度,对高光泽.耐热塑件,模温宜取60-80度；

如需解决夹水纹，需提高材料的流动性，采取高料温、高模温，或者改变入水位等方法；

如成形耐热级或阻燃级材料，生产3-7天后模具表面会残存塑料分解物，导致模具表面发亮，需对模具及时进行清理，同时模具表面需增加排气位置；

冷却速度快，模具浇注系统应以粗，短为原则，宜设冷料穴，浇口宜取大，如：直接浇口，圆盘浇口或扇形浇口等，但应防止内应力增大，必要时可采用调整式浇口。模具宜加热，应选用耐磨钢；

料温对塑件质量影响较大，料温过低会造成缺料，表面无光泽，银丝紊乱料温过高易溢边，出现银丝暗条，塑件变色起泡；

用途

ABS树脂的最大应用领域是汽车、电子电器和建材。汽车领域的使用包括汽车仪表板、车身外板、内装饰板、方向盘、隔音板、门锁、保险杠、通风管等很多部件。在电器方面则广泛应用于电冰箱、电视机、洗衣机、空调器、计算机、复印机等电子电器中。建材方面，ABS管材、ABS卫生洁具、ABS装饰板广泛应用于建材工业。此外ABS还广泛的应用于包装、家具、体育和娱乐用品、机械和仪表工业中。