PA66物性表 Ascend美国首诺Vydyne 909BK物性表
|
Ascend Vydyne? 909 BK Nylon 66（聚氨酯-尼龙66）
本物性表由中国塑商之家www.plas-cn.com塑料网提供，转载请注明来源！
|
|||
|
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Specific Gravity比重
|
1.47g/cc
|
1.47g/cc
|
ISO 1183
|
|
Water Absorption吸水率
|
0.70 %
|
0.70 %
|
24 hrs; ISO 62
|
|
Moisture Absorption at Equilibrium吸湿平衡
|
1.5 %
|
1.5 %
|
Equilibrium at 50%rh; ISO 62
|
|
Linear Mold Shrinkage线性收缩率
|
0.0040cm/cm @Thickness 2.00 mm |
0.0040in/in @Thickness 0.0787 in |
ISO 294-4
|
|
Linear Mold Shrinkage, Transverse线性收缩率/横向
|
0.010cm/cm @Thickness 2.00 mm |
0.010in/in @Thickness 0.0787 in |
ISO 294-4
|
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Tensile Strength at Break断裂拉伸强度
|
132MPa
|
19100psi
|
ISO 527
|
|
Elongation at Break断裂伸长率
|
2.2 %
|
2.2 %
|
ISO 527
|
|
Tensile Modulus拉伸模量
|
9.10GPa
|
1320ksi
|
ISO 527
|
|
Flexural Strength弯曲强度
|
193MPa
|
28000psi
|
ISO 178
|
|
Flexural Modulus弯曲弹性模量
|
9.30GPa
|
1350ksi
|
ISO 178
|
|
Poissons Ratio泊松比
|
0.37
|
0.37
|
ISO 527
|
|
Shear Modulus剪切模量
|
3.32GPa
|
482ksi
|
Calculated
|
|
Izod Impact, Notched悬臂梁缺口冲击强度(ISO)
|
9.00kJ/m2
|
4.28ft-lb/in2
|
ISO 180
|
|
Charpy Impact Unnotched夏比缺口试样冲击
|
3.50J/cm2 @Temperature -30.0 °C |
16.7ft-lb/in2 @Temperature -22.0 °F |
ISO 179
|
|
4.00J/cm2 @Temperature 23.0 °C |
19.0ft-lb/in2 @Temperature 73.4 °F |
ISO 179
|
|
|
Charpy ImPAct, Notched夏比缺口冲击
|
0.940J/cm2 @Temperature 23.0 °C |
4.47ft-lb/in2 @Temperature 73.4 °F |
ISO 179
|
|
0.950J/cm2 @Temperature -30.0 °C |
4.52ft-lb/in2 @Temperature -22.0 °F |
ISO 179
|
|
|
Electrical Properties电性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Volume ResiSTivity体积电阻率
|
1.00e 15ohm-cm @Thickness 3.00 mm |
1.00e 15ohm-cm @Thickness 0.118 in |
IEC 60093
|
|
Dielectric Strength介电强度
|
13.0kV/mm @Thickness 3.00 mm |
330kV/in @Thickness 0.118 in |
step by step; IEC 60243
|
|
High Voltage Arc Resistance to Ignition高压电弧电阻点火(HVAR)
|
60-120sec @Thickness 3.00 mm |
60-120sec @Thickness 0.118 in |
UL 746A
|
|
Comparative Tracking Index跟踪指数
|
250-399V @Thickness 3.00 mm |
250-399V @Thickness 0.118 in |
IEC 60112
|
|
Hot Wire Ignition, HWI热线圈点燃测试
|
=120sec @Thickness 0.750 mm |
=120sec @Thickness 0.0295 in |
UL 746A
|
|
High Amp Arc Ignition, HAI高电流电弧点燃测试
|
=120arcs @Thickness 0.750 mm |
=120arcs @Thickness 0.0295 in |
UL 746A
|
|
High Voltage Arc-Tracking Rate, HVTR高压电弧跟踪速度
|
=150mm/min @Thickness 3.00 mm |
=5.91in/min @Thickness 0.118 in |
UL 746A
|
|
Thermal Properties热性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
CTE, linear线性热膨胀系数
|
2.00μm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
1.11μin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359
|
|
CTE, linear, Transverse to Flow线性热膨胀系数/横向
|
10.0μm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
5.56μin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359
|
|
Melting Point熔点
|
250°C
|
482°F
|
ISO 3146
|
|
Deflection Temperature at热变形温度0.46 MPa (66 psi)
|
250°C
|
482°F
|
ISO 75
|
|
Deflection Temperature at热变形温度1.8 MPa (264 psi)
|
230°C
|
446°F
|
ISO 75
|
|
Vicat Softening Point维卡软化点
|
233°C
|
451°F
|
50N; ISO 306
|
美国奥升德VYDYNE?PA66 909BK的典型应用：
应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些***工程制品等等。
电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座等等
汽车： 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座等等
工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输等等
外观微黄色均匀颗粒,相对密度 1.30～1.40 含湿量(%) ≤1.5 拉伸强度(MPa) ≥150 静弯曲强度(MPa) ≥220 弯曲弹性模量(MPa) ≥6.5×103 缺口冲击强度(KJ/m2) ≥15 热变形温度(1.81MPa，℃) ≥210 玻璃纤维含量(%) 30±2
二、用途
本产品居于高强度、高耐热性、热胀系数和收缩率小，吸水性低，尺寸稳定性随大气
湿度和温度变化而不大，它适合制作凸轮、伐座、收音机零部件、电子仪表零件、汽车交通零部件等。
PA66 美国首诺909BK注射成型加工：
注射压力通常在750~1250bar，取决于材料和产品设计。
PA66环保加纤料注射速度:高速（对于增强型材料应稍低一些）。
流道和浇口:由于PA66的凝固时间很短，因此浇口的位置非常重要。浇口孔径不要小于0.5*t（这里t为塑件厚度）。