PA6 Zytel 73G30HSL BK416

Physical Properties	Metric	English	Comments
Density	1.36g/cc	0.0491lb/in3	DAM; ISO 1183
Water Absorption	6.3 % @Thickness 2.00 mm	6.3 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Moisture Absorption	2.10 % @Thickness 2.00 mm	2.10 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Viscosity Number	140cm3/g	1.40dl/g	ISO 307, 1157, 1628
Linear Mold Shrinkage, Flow	0.0020cm/cm	0.0020in/in	DAM; ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.0060cm/cm	0.0060in/in	DAM; ISO 294-4, 2577
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	120MPa	17400psi	50% RH; ISO 527-1/-2
	190MPa	27600psi	DAM; ISO 527-1/-2
Elongation at Break	3.5 %	3.5 %	DAM; ISO 527-1/-2
	6.0 %	6.0 %	50% RH; ISO 527-1/-2
Tensile Modulus	6.00GPa	870ksi	50% RH; ISO 527-1/-2
	10.0GPa	1450ksi	DAM; ISO 527-1/-2
Flexural Strength	180MPa	26100psi	50% RH; ISO 178
	250MPa	36300psi	DAM; ISO 178
Flexural Modulus	5.50GPa	798ksi	50% RH; ISO 178
	8.50GPa	1230ksi	DAM; ISO 178

PA6 Zytel 73G30HSL BK416

增强PA

在PA中 加入30% 的玻璃纤维，PA 的力学性能、尺寸稳定性、耐热性、耐老化性能有明显提高，耐疲劳

尼龙PA特性：

阻燃PA

由于在PA中加入了阻燃剂，大部分阻燃剂在高温下易分解，释放出酸性物质，对金属具有腐蚀作用.

透明PA

具有良好的拉伸强度、耐冲击强度、刚性、耐磨性、耐化学性、表面硬度等性能，透光率高，与光学玻璃相近.

耐候PA

在PA 中加入了炭黑等吸收紫外线的助剂，这些对PA的自润滑性和对金属的磨损大大增强，成型加工时会影响下料和磨损机件。因此，需要采用进料能力强及耐磨性高的螺杆、机筒、过胶头、过胶圈、过胶垫圈组合。

主要在以下几方面进行改性：

①改善尼龙的吸水性，提高制品的尺寸稳定性。

②提高尼龙的阻燃性，以适应电子、电气、通讯等行业的要求。

③提高尼龙的机械强度，以达到金属材料的强度，取代金属

④提高尼龙的抗低温性能，增强其对耐环境应变的能力。

⑤提高尼龙的耐磨性，以适应耐磨要求高的场合。

⑥提高尼龙的抗静电性，以适应矿山及其机械应用的要求。

⑦提高尼龙的耐热性，以适应如汽车发动机等耐高温条件的领域.

⑧降低尼龙的成本，提高产品竞争力。

PA6 应用：

汽车的小型化、电子电气设备的高性能化、机械设备轻量化的进程加快，对尼龙的需求将更高更大。特别是尼龙作为结构性材料，对其强度、耐热性、耐寒性等方面提出了很高的要求。尼龙的固有缺点也是限制其应用的重要因素，特别是对于PA6、PA66两大品种来说，与PA46、PAl2等品种比具有很强的价格优势，虽某些性能不能满足相关行业发展的要求。

因此，必须针对某一应用领域，通过改性，提高其某些性能，来扩大其应用领域。 由于PA强极性的特点，吸湿性强，尺寸稳定性差，但可以通过改性来改善。