东莞市正涛塑胶有限公司
物性表
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
|---|---|---|---|---|
| 断裂伸长率 | ASTM D638/ISO 527 | 550 | % | |
| 抗张强度级限 | ASTM D-638 | 10.78 | Mpa | |
| 拉伸模量 | ASTM D638/ISO 527 | 12 | kg/cm2(MPa)[Lb/in2] | |
| 拉伸强度 | ASTM D638/ISO 527 | 10 | kg/cm2(MPa)[Lb/in2] | |
| 洛氏硬度 | ASTM D785 | 50 | ||
| 伸长率 | ASTM D638/ISO 527 | 600 | % | |
| 弯曲模量 | ASTM D790/ISO 178 | 15 | kg/cm2(MPa)[Lb/in2] | |
| 弯曲强度 | ASTM D790/ISO 178 | 22 | kg/cm2(MPa)[Lb/in2] | |
| 延伸性 | ASTM D-638 | 150 | % | |
| 硬度 | ASTM D-1706 | 42 | ||
| Charpy冲击强度 | ASTM D256/ISO 179 | 12 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 4 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 16 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 5 | kg·cm/cm(J/M)ft·lb/in | ||
| IZOD 缺口冲击强度 | ASTM D256/ISO 179 | 12 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 11 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 13 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 10 | kg·cm/cm(J/M)ft·lb/in | ||
| 拉伸断裂伸长率(延伸率) | ASTM D638/ISO 527 | 700 | % | |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 低温脆化性 | ASTM D-746 | -60 | ℃ | |
| 加热偏向温度 | ASTM D-648 | 46 | ℃ | |
| 燃烧性（率） | UL94 | HB | ||
| 热变形温度 | ASTM D648/ISO 75 | 80 | ℃（℉） | |
| ASTM D648/ISO 75 | 75 | ℃（℉） | ||
| 熔点 | 105 | ℃（℉） | ||
| 维卡软化点 | ASTM D1525/ISO R306 | 95 | ℃（℉） | |
| ASTM D-1525 | 80 | ℃ | ||
| 线性膨胀系数 | ASTM D696/ISO 11359 | 1 | mm/mm.℃ | |
| 物性性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 比重（密度） | ASTM D792/ISO 1183 | 0.9235 | ||
| 成型收缩率 | ASTM D955 | 0.07 | % | |
| 熔融指数（流动系数） | ASTM D1238/ISO 1133 | 50 | g/10min | |
| 吸水率 23℃/24H | ASTM D570/ISO 62 | 0.005 | % |
| 产地 | 品名 | 是否进口 |