PA66 Zytel ST801 NC010中英文物性参数物性表
DuPont Zytel? ST801 NC010 Nylon 66（聚酰胺-尼龙66）
The property table is provided bywww.plas-cn.com, welcome to download, reprint please indicate the source!
Physical Properties物理性质
Metric公制数据
English英制数据
Comments测试方法
Density密度
1.08g/cc
0.0390lb/in3
DAM; ISO 1183
Water Absorption吸水率
2.2 %
@Temperature 23.0 °C
2.2 %
@Temperature 73.4 °F
Equilibrium 50%RH; DAM; ISO 62, Similar to
6.7 %
@Temperature 23.0 °C
6.7 %
@Temperature 73.4 °F
Saturation, immersed; DAM; ISO 62, Similar to
Viscosity粘度
38000cP
@Shear Rate 7000 1/s,
Temperature 315 °C
38000cP
@Shear Rate 7000 1/s,
Temperature 599 °F
DAM; ISO 11443
88000cP
@Shear Rate 7000 1/s,
Temperature 275 °C
88000cP
@Shear Rate 7000 1/s,
Temperature 527 °F
DAM; ISO 11443
135000cP
@Shear Rate 1000 1/s,
Temperature 295 °C
135000cP
@Shear Rate 1000 1/s,
Temperature 563 °F
DAM; ISO 11443
181000cP
@Shear Rate 500 1/s,
Temperature 295 °C
181000cP
@Shear Rate 500 1/s,
Temperature 563 °F
DAM; ISO 11443
244000cP
@Shear Rate 700 1/s,
Temperature 275 °C
244000cP
@Shear Rate 700 1/s,
Temperature 527 °F
DAM; ISO 11443
283000cP
@Shear Rate 500 1/s,
Temperature 275 °C
283000cP
@Shear Rate 500 1/s,
Temperature 527 °F
DAM; ISO 11443
Linear Mold Shrinkage, Flow线性收缩率/流动
0.017cm/cm
@Thickness 2.00 mm
0.017in/in
@Thickness 0.0787 in
Parallel; DAM; ISO 294-4
Mechanical Properties力学性能
Metric公制数据
English英制数据
Comments测试方法
Tensile Stress拉伸应力
0.000MPa
@Strain 0.000 %,
Temperature -20.0 °C
0.000psi
@Strain 0.000 %,
Temperature -4.00 °F
50%RH; ISO 527
1410psi
@Strain 5.01 %,
Temperature 248 °F
50%RH; ISO 527
19.8MPa
@Strain 8.58 %,
Temperature 90.0 °C
2870psi
@Strain 8.58 %,
Temperature 194 °F
DAM; ISO 527
|
DuPont Zytel? ST801 NC010 Nylon 66（聚酰胺-尼龙66）
The property table is provided bywww.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Density密度
|
1.08g/cc
|
0.0390lb/in3
|
DAM; ISO 1183
|
|
Water Absorption吸水率
|
2.2 % @Temperature 23.0 °C |
2.2 % @Temperature 73.4 °F |
Equilibrium 50%RH; DAM; ISO 62, Similar to
|
|
6.7 % @Temperature 23.0 °C |
6.7 % @Temperature 73.4 °F |
Saturation, immersed; DAM; ISO 62, Similar to
|
|
|
Viscosity粘度
|
38000cP @Shear Rate 7000 1/s, Temperature 315 °C |
38000cP @Shear Rate 7000 1/s, Temperature 599 °F |
DAM; ISO 11443
|
|
88000cP @Shear Rate 7000 1/s, Temperature 275 °C |
88000cP @Shear Rate 7000 1/s, Temperature 527 °F |
DAM; ISO 11443
|
|
|
135000cP @Shear Rate 1000 1/s, Temperature 295 °C |
135000cP @Shear Rate 1000 1/s, Temperature 563 °F |
DAM; ISO 11443
|
|
|
181000cP @Shear Rate 500 1/s, Temperature 295 °C |
181000cP @Shear Rate 500 1/s, Temperature 563 °F |
DAM; ISO 11443
|
|
|
244000cP @Shear Rate 700 1/s, Temperature 275 °C |
244000cP @Shear Rate 700 1/s, Temperature 527 °F |
DAM; ISO 11443
|
|
|
283000cP @Shear Rate 500 1/s, Temperature 275 °C |
283000cP @Shear Rate 500 1/s, Temperature 527 °F |
DAM; ISO 11443
|
|
|
Linear Mold Shrinkage, Flow线性收缩率/流动
|
0.017cm/cm @Thickness 2.00 mm |
0.017in/in @Thickness 0.0787 in |
Parallel; DAM; ISO 294-4
|
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Tensile Stress拉伸应力
|
0.000MPa @Strain 0.000 %, Temperature -20.0 °C |
0.000psi @Strain 0.000 %, Temperature -4.00 °F |
50%RH; ISO 527
|
|
1410psi @Strain 5.01 %, Temperature 248 °F |
50%RH; ISO 527
|
||
|
19.8MPa @Strain 8.58 %, Temperature 90.0 °C |
2870psi @Strain 8.58 %, Temperature 194 °F |
DAM; ISO 527
|
|
PA66美国杜邦 ST801 增韧耐寒级 耐寒-40 增韧剂22.0%
PA66性质：结晶性热可塑性塑料，有明显熔点，Nylon6Tm为220-230℃，Nylon66则为260-270℃，
Nylon本身具吸水基故有吸水性，成形前须干燥，温度过高干燥则尼龙粒变色。
优点：1、具高抗张强度；2、耐韧、耐冲击性特优；3、自润性、**性佳、耐 性优；4、低温特性佳；5、具自熄性；
用途：广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。
电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座
汽车：散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座
工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输
分类：防静电PA，导电PA，加纤防火PA，防火PA，抗紫外线耐候PA，高温挤出级PA。
导电尼龙66：具有良好的**性、耐热性、耐油性及耐化学 性，还大大降低了原材料的吸水率和收缩率,
具有优良的尺寸稳定性及优异的机械强度。能满足静电消散和静电放电(ESD)防护的要求。这些特殊改性材料经特殊配制，
适用于从100到1012欧姆／平方(ohms/sq)的表面电阻范围，可用于注塑及挤出等成型。
有很多*金属和涂装的优点:零件重量较轻，较易处理，运输成本较低。它们的装配简便，制造成本较低，并且较不会受到撞凹，割损和刮伤。
为了标识或美观目的，一些材料可被预先染色，避**时且昂贵的两次着色加工