PA66 Zytel FG101L NC010中英文物性参数物性表
|
DuPont Zytel? FG101L NC010 Nylon 66（聚酰胺-尼龙66）
The property table is provided bywww.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Density密度
|
1.14g/cc
|
0.0412lb/in3
|
DAM; ISO 1183
|
|
Water Absorption吸水率
|
2.6 % @Temperature 23.0 °C |
2.6 % @Temperature 73.4 °F |
Equilibrium 50%RH; DAM; ISO 62, Similar to
|
|
8.5 % @Temperature 23.0 °C |
8.5 % @Temperature 73.4 °F |
Saturation, immersed; DAM; ISO 62, Similar to
|
|
|
Linear Mold Shrinkage线性收缩率
|
0.015cm/cm @Thickness 3.20 mm |
0.015in/in @Thickness 0.126 in |
Flow; DAM
|
|
Linear Mold Shrinkage, Flow线性收缩率/流动
|
0.014cm/cm @Thickness 2.00 mm |
0.014in/in @Thickness 0.0787 in |
Parallel; DAM; ISO 294-4
|
|
Linear Mold Shrinkage, Transverse线性收缩率/横向
|
0.014cm/cm @Thickness 2.00 mm |
0.014in/in @Thickness 0.0787 in |
Normal; DAM; ISO 294-4
|
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Hardness, Rockwell M罗氏硬度M
|
59
|
50%RH; ISO 2039/2
|
|
|
79
|
79
|
DAM; ISO 2039/2
|
|
|
Hardness, Rockwell R罗氏硬度R
|
108
|
108
|
50%RH; ISO 2039/2
|
|
121
|
121
|
DAM; ISO 2039/2
|
|
|
Tensile Strength, Yield屈服拉伸强度
|
55.0MPa @Temperature 23.0 °C |
7980psi @Temperature 73.4 °F |
50%RH; ISO 527
|
|
82.0MPa @Temperature 23.0 °C |
11900psi @Temperature 73.4 °F |
DAM; ISO 527
|
|
|
Elongation at Break断裂伸长率
|
25 % @Temperature 23.0 °C |
25 % @Temperature 73.4 °F |
DAM; nominal; ISO 527
|
|
45 % @Temperature 23.0 °C |
45 % @Temperature 73.4 °F |
50mm/min; DAM; ISO 527
|
|
|
= 100 % @Temperature 23.0 °C |
= 100 % @Temperature 73.4 °F |
50%RH; nominal; ISO 527
|
|
|
Elongation at Yield屈服伸长率
|
4.5 % @Temperature 23.0 °C |
4.5 % @Temperature 73.4 °F |
DAM; ISO 527
|
|
25 % @Temperature 23.0 °C |
25 % @Temperature 73.4 °F |
50%RH; ISO 527
|
|
|
Tensile Modulus拉伸模量
|
1.40GPa @Temperature 23.0 °C |
203ksi @Temperature 73.4 °F |
50%RH; ISO 527
|
|
3.10GPa @Temperature 23.0 °C |
450ksi @Temperature 73.4 °F |
DAM; ISO 527
|
|
PA66性质：结晶性热可塑性塑料，有明显熔点，Nylon6Tm为220-230℃，Nylon66则为260-270℃，
Nylon本身具吸水基故有吸水性，成形前须干燥，温度过高干燥则尼龙粒变色。
优点：1、具高抗张强度；2、耐韧、耐冲击性特优；3、自润性、**性佳、耐 性优；4、低温特性佳；5、具自熄性；
用途：广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。
电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座
汽车：散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座
工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输
分类：防静电PA，导电PA，加纤防火PA，防火PA，抗紫外线耐候PA，高温挤出级PA。
导电尼龙66：具有良好的**性、耐热性、耐油性及耐化学 性，还大大降低了原材料的吸水率和收缩率,
具有优良的尺寸稳定性及优异的机械强度。能满足静电消散和静电放电(ESD)防护的要求。这些特殊改性材料经特殊配制，
适用于从100到1012欧姆／平方(ohms/sq)的表面电阻范围，可用于注塑及挤出等成型。
有很多*金属和涂装的优点:零件重量较轻，较易处理，运输成本较低。它们的装配简便，制造成本较低，并且较不会受到撞凹，割损和刮伤。
为了标识或美观目的，一些材料可被预先染色，避**时且昂贵的两次着色加工