| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 5 | g/10min |
| 熔体流动速率 | 190℃/2.16kg | ISO 1133 | 5 | g/10min | |
| 单体含量 | Internal Method | 9.7 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 0.93 | g/cm3 | |
| 比重 | ISO 1183 | 0.93 | g/cm3 | ||
| 机械性能 | 拉伸屈服强度 | Compression Molded | ASTM D-638 | 7.67 | MPa |
| 拉伸屈服强度 | Compression Molded | ISO 527-2/508 | 7.67 | MPa | |
| 拉伸断裂强度 | Compression Molded | ASTM D-638 | 19.5 | MPa | |
| 拉伸断裂强度 | Compression Molded | ISO 527-2/508 | 19.5 | MPa | |
| 拉伸断裂伸长率 | Compression Molded | ASTM D-638 | 580 | % | |
| 拉伸断裂伸长率 | Compression Molded | ISO 527-2/508 | 580 | % | |
| 薄膜厚度-Tested | 50.8 | um | |||
| 拉伸屈服强度 | 50.8um | ASTM D-882 | |||
| MD | TD | ||||
| 10.4 | 10.2 | ||||
| MPa | |||
| 拉伸屈服强度 | 50.8um | ISO 527-3 | |
| MD | TD | ||
| 10.4 | 10.2 |
| MPa | |||
| 拉伸断裂强度 | 50.8um | ASTM D-882 | |
| MD | TD | ||
| 30.6 | 31.0 |
| MPa | |||
| 拉伸断裂强度 | 50.8um | ISO 527-3 | |
| MD | TD | ||
| 30.6 | 31 |
| MPa | |||
| 拉伸断裂伸长率 | 50.8um | ASTM D-882 | |
| MD | TD | ||
| 420 | 470 |
| % | |||
| 拉伸断裂伸长率 | 50.8um | ISO 527-3 | |
| MD | TD | ||
| 420 | 470 |
| % | |||
| 埃尔曼多夫撕裂强度 | 50.8um | ASTM D-1922 | |
| MD | TD | ||
| 470 | 730 |
| g | |||
| 埃尔曼多夫撕裂强度 | 50.8um | ISO 6383-2 | |
| TD | MD | ||
| 3300 | 2100 |
| N | |||||
| 热性能 | 维卡软化点 | ASTM D-1525 | 76.1 | ℃ | |
| 维卡软化点 | ISO 306 | 76.1 | ℃ | ||
| 熔融温度 | Internal Method | 96.1 | ℃ | ||
| 光学性能 | 光泽度 | 45°，50.8um | ASTM D-2457 | 74 | |
| 雾度 | 50.8um | ISO 14782 | 4 | % | |
| 雾度 | 50.8um | ASTM D-1003 | 4 | % | |
| 熔体温度 | 196 | ℃ |