POM CELCON GC10

Physical Properties	Metric	English	Comments
Density	1.46g/cc	0.0527lb/in3	ISO 1183
Moisture Absorption	0.200 %	0.200 %	23°C/50%RH; ISO 62
Water Absorption at Saturation	0.80 %	0.80 %	ISO 62
Linear Mold Shrinkage, Flow	0.0090cm/cm	0.0090in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.012cm/cm	0.012in/in	ISO 294-4
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	75.0MPa	10900psi	5mm/min; ISO 527-2/1A
Elongation at Break	3.0 %	3.0 %	5mm/min; ISO 527-2/1A
Tensile Modulus	4.50GPa	653ksi	50mm/min; ISO 527-2/1A
Flexural Modulus	4.25GPa	616ksi	ISO 178
Izod Impact, Notched (ISO)	4.80kJ/m2	2.28ft-lb/in2	ISO 180/1A
Charpy Impact Unnotched	3.00J/cm2	14.3ft-lb/in2	ISO 179/1eU
	4.50J/cm2 @Temperature -30.0 °C	21.4ft-lb/in2 @Temperature -22.0 °F	ISO 179/1eU
Charpy Impact, Notched	0.450J/cm2	2.14ft-lb/in2	ISO 179/1eA

POM CELCON GC10

特点

（1）POM加工前可不用干燥,最好在加工过程中进行预热(80℃左右),对产品尺寸的稳定性有好处.

（2） POM的加工温度很窄(0～215℃),在炮筒内停留时间稍长或温度超过220℃时就会分解,产生刺激性强的甲醛气体.

（3） POM料注塑时保压压力要较大(与注射压力相近),以减少压力降.螺杆转速不能过高,残量要少;

（4） POM产品收缩率较大,易产生缩水或变形.POM比热大,模温高(80～100℃),产品脱模时很烫,需防止烫伤手指.

（5） POM宜在“中压、中速、低料温、较高模温”的条件下成型加工,精密制品成型时需用控制模温

（6）具高机械强度和刚性

（7）最高的疲劳强度

（8）环境抵抗性、耐有机溶剂性佳

（9）耐反覆冲击性强,良好的电气性质,复原性良好,具自已润滑性、耐磨性良好,尺寸安定性优.

应用

.可代替大部分有色金属、汽车、机床、仪表内件、轴承、紧固件、齿轮、弹簧片、管道、运输带配件、电水煲、泵壳、沥水器、水龙头等.