东莞市常平浩云塑胶经营部
Dynaflex D3202-1000-03 TPE
Dynaflex D3204-1000-03 TPE
Dynaflex D3226-1000-03 TPE
Dynaflex G2701-1000-02 TPE
Dynaflex G2701C TPE
Dynaflex G2703-1000-00 TPE
Dynaflex G2706-1000-00 TPE
Dynaflex G2709-1000-00 TPE
Dynaflex G2711-1000-00 TPE
Dynaflex G2712-1000-02 TPE
Dynaflex G2730 TPE
Dynaflex G2745 TPE
Dynaflex G2755-1000-00 TPE
Dynaflex G2755C TPE
Dynaflex G2780-0001 TPE
Dynaflex G6703-0001 TPE
Dynaflex G6713-0001 TPE
Dynaflex G6713C GLS TPE
Dynaflex G7410-1000-00 TPE
Dynaflex G7430-9001-00 TPE
Dynaflex G7431-1001-00 TPE
Dynaflex G7630-1 TPE
Dynaflex G7630-9 TPE
Dynaflex G7640-1 TPE
Dynaflex G7640-9 TPE
Dynaflex G7650-1 TPE
Dynaflex G7650-9 TPE
Dynaflex G7660-1 TPE
Dynaflex G7660-9 TPE
Dynaflex G7670-1 TPE
Dynaflex G7670-9 TPE
Dynaflex G7680-1 TPE
Dynaflex G7680-9 TPE
Dynaflex G7690-1 TPE
Dynaflex G7690-9 TPE
Dynaflex G7702-9001-02 TPE
Dynaflex G7736-1 GLS TPE
Dynaflex G7930-1001-00 GLS TPE
Dynaflex G7930-9001-02 GLS TPE
Dynaflex G7940-1001-00 GLS TPE
Dynaflex G7940-9001-02 GLS TPE
Dynaflex G7950-1001-00 GLS TPE
Dynaflex G7950-9001-02 GLS TPE
Dynaflex G7960-1001-00 GLS TPE
Dynaflex G7960-9001-02 GLS TPE
Dynaflex G7970-1001-00 GLS TPE
Dynaflex G7970-9001-02 GLS TPE
Dynaflex G7980-1001-00 GLS TPE
Dynaflex G7980-9001-02 GLS TPE
Dynalloy 8900-30 TPE
Dynalloy 8900-60 TPE
Dynalloy 8900-80 TPE
Dynalloy OBC 8100-N50 TPE
Dynalloy OBC 8100-N65 TPE
Dynalloy OBC 8100-N75 TPE
Dynalloy OBC8000-B30 TPE
Dynalloy OBC8000-N30 TPE
Dynalloy OBC8000-T05 TPE
Dynalloy OBC8000-T40 TPE
Dynalloy OBC8000-T60 TPE
Dynalloy OBC8200-BT50 TPE
Dynaflex G7410-1000-00
热塑性弹性体
PolyOne Corporation
产品说明：
Dynaflex G7410-1000-00 是一种容易加工的高性能复合材料，设计用于要求材料具有坚韧、经久耐用特性的各种应用。
- 着色性极佳
- 热稳定性极佳
- 可以重叠模塑方式粘接在聚丙烯上
- 适合于室外用途
Dynaflex G7410-1000-00 物性表
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.898 | g/cm3 | ASTM D792 |
| 熔流率（熔体流动速率）(200°C/5.0 kg) | 2.0 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 | 1.8 到 2.2 | % | ASTM D955 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度(邵氏 A, 10 秒) | 68 | ASTM D2240 |
| 弹性体 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力1 | ASTM D412 | ||
| 100%应变, 23°C2 | 2.69 | MPa | ASTM D412 |
| 300%应变, 23°C3 | 3.55 | MPa | ASTM D412 |
| 抗张强度(断裂, 23°C) | 5.17 | MPa | ASTM D412 |
| 伸长率(断裂, 23°C) | 500 | % | ASTM D412 |
| 撕裂强度 | 28.0 | kN/m | ASTM D624 |
| 压缩永久变形(23°C, 22 hr) | 19 | % | ASTM D395B |
| 充模分析 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 表观粘度(200°C, 11200 sec^-1) | 14.8 | Pa·s | ASTM D3835 |
| 补充信息 |
|---|
| Dynaflex G7410-1000-00 can be recycled as a filler or impact modifier for polyolefins, or can be recycled by grinding and reintroduction to the molding process. Similar to PP or PE recycling process, if separated appropriately, it can be recycled many times.Municipality waste stream recycle code is "7" which is designated for "Other".Please contact GLS Thermoplastic Elastomers for a copy of our Recyclability Compliance letter. |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 建议的最大回制料比例 | 20 | % | |
| 料筒后部温度 | 166 到 204 | °C | |
| 料筒中部温度 | 177 到 216 | °C | |
| 料筒前部温度 | 182 到 221 | °C | |
| 射嘴温度 | 182 到 221 | °C | |
| 模具温度 | 15.6 到 26.7 | °C | |
| 背压 | 0.345 到 1.03 | MPa | |
| 螺杆转速 | 25 到 75 | rpm |
| 注射说明 |
|---|
| 以聚丙烯 (PP)、乙烯醋酸乙烯共聚物 (EVA) 或低密度聚乙烯 (PE) 为基础的色母料最适合 Dynaflex? G7410-1000-00 着色。使用熔体流动速率较高（范围为 25 - 40 克/10 分钟）的色母料，则能达到较好的颜色分散效果。典型的色母料用量为 1% 至 5%（重量）。可以使用液体颜料，但以矿物油为基础的载体对最终硬度值会有显著的影响。不应采用以 PVC 为基础的色母料。若使用 GLS 可供的预着色复合材料，则可达到较好的配色一致性。色母料是否适用，应由用户通过试验来最终确定。在使用此产品之前或之后，均须用熔体流动速率较低 (0.5 - 2.5 MFR) 的聚乙烯 (PE) 或聚丙烯 (PP) 彻底进行置换。Dynaflex? G7410-1000-00 可利用高达 20% 的回收料同时其性能所受影响却极小，但该回收料必须是未受到污染的。回收料的有效性应由用户最终确定。Dynaflex? G7410-1000-00 具有极好的熔体稳定性。如果机器闲置三十 (30) 分钟或以上，则应将机筒排空。不需要干燥注射速度：1 - 5 英寸/秒第一阶段 - 提升压力：250 - 650 psi第二阶段 - 保持压力：70% 的升压保持时间（厚部件）：4 - 10 秒保持时间（薄部件）：1 - 3 秒 |
| 备注 | |
|---|---|
| 1 . | 2 小时 |
| 2 . | 口模 C |
| 3 . | C 模具 |