埃克森美孚ExxonMobil?PE
泛用塑膠
埃克森美孚ExxonMobil?PE聚乙烯Polyethylene成型條件射出溫度：160-280℃模具溫度：10-60℃
LLDPE線性低密度聚乙烯
埃克森美孚 型号如下
ExxonMobil LDPE LD 156 Series
ExxonMobil LDPE LD 157CW BlownExxonMobil LDPE LD 157CW Wire CableExxonMobil LDPE LD 158 SeriesExxonMobil LDPE LD 159ACExxonMobil LDPE LD 160ATExxonMobil LDPE LD 165BW1ExxonMobil LDPE LD 171BAExxonMobil LDPE LD 185 SeriesExxonMobil LDPE LD 200.48ExxonMobil LDPE LD 201.48ExxonMobil LDPE LD 202.48ExxonMobil LDPE LD 250ExxonMobil LDPE LD 251ExxonMobil LDPE LD 252ExxonMobil LDPE LD 258ExxonMobil LDPE LD 259ExxonMobil LDPE LD 263ExxonMobil LDPE LD 302 SeriesExxonMobil LDPE LD 302.32ExxonMobil LDPE LD 306 SeriesExxonMobil LDPE LD 312.23ExxonMobil LDPE LD 313.NFExxonMobil LDPE LD 317 SeriesExxonMobil LDPE LD 331.08ExxonMobil LDPE LD 358BWExxonMobil LDPE LD 361 SeriesExxonMobil LDPE LD 362 SeriesExxonMobil LDPE LD 363 SeriesExxonMobil LDPE LD 364HEExxonMobil LDPE LD 368 SeriesExxonMobil LDPE LD 380BA Blown
ExxonMobil LDPE LD 380BA Wire Cable
ExxonMobil? LDPE LD 105 Series 物性表
| 基本信息 |
|
| 添加剂 |
- LD 105.BR: 抗结块剂 (1000 ppm); 热稳定剂; 增滑剂 (750 ppm)
- LD 105.30: 抗结块剂 (1000 ppm); 热稳定剂
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 熔流率（熔体流动速率）(190°C/2.16 kg) |
2.0 |
g/10 min |
ASTM D1238 |
| 薄膜 |
额定值 |
单位制 |
测试方法 |
| 割线模量 |
|
|
ASTM D882 |
| 1% 正割, MD |
214 |
MPa |
ASTM D882 |
| 1% 正割, TD |
253 |
MPa |
ASTM D882 |
| 抗张强度 |
|
|
ASTM D882 |
| MD : 屈服 |
11.0 |
MPa |
ASTM D882 |
| TD : 屈服 |
11.1 |
MPa |
ASTM D882 |
| MD : 断裂 |
25.1 |
MPa |
ASTM D882 |
| TD : 断裂 |
21.1 |
MPa |
ASTM D882 |
| 伸长率 |
|
|
ASTM D882 |
| MD : 断裂 |
210 |
% |
ASTM D882 |
| TD : 断裂 |
570 |
% |
ASTM D882 |
| 落锤冲击 |
99 |
g |
ASTM D1709A |
| 埃尔曼多夫抗撕强度 |
|
|
ASTM D1922 |
| MD |
350 |
g |
ASTM D1922 |
| TD |
180 |
g |
ASTM D1922 |
| 光学性能 |
额定值 |
单位制 |
测试方法 |
| 光泽度(45°) |
76 |
|
ASTM D2457 |
| 雾度 |
5.2 |
% |
ASTM D1003 |