ARLEN? E630N by Mitsui Chemicals is a modified polyamide 6T reinforced with 30% glass fiber. Possesses high dimensional stability, high melting point, high rigidity and minimum water absorption. Exhibits good chemical and heat resistance. Is suitable for processing by injection molding. ARLEN? E630N is recommended for electrical electronic parts including connectors, jacks, switches and power supply terminals. Complies with UL 94 V-0 flame rating.Features:

• High dimensional stability

• High melting point

• High rigidity

• Minimum water absorption

• Good chemical and heat resistance

• Flame retardant

Applications:

• Electrical and electronic parts including: connectors, jacks, switches, and power supply terminals.

• ARLEN? E630N 物性表

  基本信息
  填料/增强材料	玻璃纤维增强材料, 30% 填料按重量
  添加剂	阻燃性
  特性	Good Heat Resistance High Dimensional Stability 刚性，高 耐化学性良好 吸水低或不吸水 阻燃性
  用途	电气/电子应用领域 开关 连接器
  加工方法	注射成型

  物理性能	额定值	单位制	测试方法
  比重	1.58	g/cm3	ASTM D792
  收缩率	ASTM D955
  流动	0.20	%	ASTM D955
  横向流动	0.80	%	ASTM D955
  吸水率(23°C, 24 hr, 65%r.h)	2.1	%	ASTM D570

  硬度	额定值	单位制	测试方法
  洛氏硬度(M 级)	100	ASTM D785

  机械性能	额定值	单位制	测试方法
  抗张强度	210	MPa	ASTM D638
  伸长率(断裂)	6.0	%	ASTM D638
  弯曲模量	12500	MPa	ASTM D790
  弯曲强度	275	MPa	ASTM D790

  冲击性能	额定值	单位制	测试方法
  悬壁梁缺口冲击强度	100	J/m	ASTM D256

  热性能	额定值	单位制	测试方法
  载荷下热变形温度(1.8 MPa, 未退火)	310	°C	ASTM D648
  玻璃转化温度	95.0	°C
  熔融温度	320	°C
  线形热膨胀系数	ASTM E831
  流动	1.6E-5	cm/cm/°C	ASTM E831
  横向	6.8E-5	cm/cm/°C	ASTM E831

  电气性能	额定值	单位制	测试方法
  体积电阻率	1.0E+15	ohms·cm	ASTM D257
  介电强度	24	kV/mm	ASTM D149
  介电常数(1 MHz)	3.90	ASTM D150
  耗散因数(1 MHz)	0.013	ASTM D150

  可燃性	额定值	单位制	测试方法
  UL 阻燃等级	V-0	UL 94