东莞市铭汇塑胶有限公司
7130
LCP | 液晶聚合物#
美国杜邦
7130 物性表
| 物理性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 比重 | 1.62 | ASTM D-792 | |
| 模具收缩率 (1.6mm(0.063in)) | -0.1 | % | ASTM D-955 |
| 机械性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 弯曲模量 (1.6mm(0.063in),23℃(73℉)) | 14000 | MPa | ASTM D-790 |
| IZOD冲击强度 (3.2mm(0.125in),23℃(73℉)) | 225 | J/m | ASTM D-256 |
| 拉伸强度 (1.6mm(0.063in),23℃(73℉)) | 173 | MPa | ASTM D-638 |
| 拉伸模量 (1.6mm(0.063in),23℃(73℉)) | 19306 | MPa | ASTM D-638 |
| IZOD冲击强度 (1.6mm(0.063in),23℃(73℉)) | 170 | J/m | ASTM D-256 |
| 拉伸强度 (3.2mm(0.125in),23℃(73℉)) | 150 | MPa | ASTM D-638 |
| 弯曲强度 (0.8mm(0.032in),23℃(73℉)) | 215 | MPa | ASTM D-790 |
| 无缺口冲击强度 (3.2mm(0.125in),23℃(73℉)) | 740.20%NB | J/m | ASTM D-4812 |
| 弯曲模量 (0.8mm(0.032in),23℃(73℉)) | 18000 | MPa | ASTM D-790 |
| 弯曲强度 (3.2mm(0.125in),23℃(73℉)) | 183 | MPa | ASTM D-790 |
| 压缩强度 (3.2mm(0.125in)) | 89 | MPa | ASTM D-695 |
| 断裂伸长率 (1.6mm(0.063in),23℃(73℉)) | 1.6 | % | ASTM D-638 |
| 弯曲模量 (3.2mm(0.125in),23℃(73℉)) | 13100 | MPa | ASTM D-790 |
| IZOD冲击强度 (0.8mm(0.032in),23℃(73℉)) | 400,40%NB | J/m | ASTM D-256 |
| 剪切强度 (0.8mm(0.032in)) | 57 | MPa | ASTM D-732 |
| 弯曲强度 (1.6mm(0.063in),23℃(73℉)) | 192 | MPa | ASTM D-790 |
| 断裂伸长率 (3.2mm(0.125in)) | 1.7 | % | ASTM D-638 |
| 无缺口冲击强度 (1.6mm(0.063in),23℃(73℉)) | 840 | J/m | ASTM D-4812 |
| 洛氏硬度 | 63 | ASTM D-785 | |
| 拉伸模量 (3.2mm(0.125in),23℃(73℉)) | 18000 | MPa | ASTM D-638 |
| 压缩模量 (3.2mm(0.125in)) | 5300 | MPa | ASTM D-695 |
| 剪切强度 (3.2mm(0.125in)) | 58 | MPa | ASTM D-732 |
| 无缺口冲击强度 (0.8mm(0.032in),23℃(73℉)) | NB | J/m | ASTM D-4812 |
| 电气性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 损耗因数 (3.2mm(0.125in),23℃(73℉)) | 0.004 | ASTM D-2520 B | |
| 介电常数 (3.2mm(0.125in),23℃(73℉)) | 4.3 | ASTM D-2520 B | |
| 损耗因数 (3.2mm(0.125in),23℃(73℉)) | 0.029 | ASTM D-150 | |
| 介电常数 | ASTM D-150 | ||
| (3.2mm(0.125in),23℃(73℉)) | 3.8 | ||
| (0.8mm(0.032in),23℃(73℉)) | 3.5 | ||
| (0.8mm(0.032in),23℃(73℉)) | 4.4 | ||
| 损耗因数 | ASTM D-150 | ||
| (3.2mm(0.125in),23℃(73℉)) | 0.013 | ||
| (0.8mm(0.032in),23℃(73℉)) | 0.029 | ||
| 介电常数 (1.6mm(0.063in),23℃(73℉)) | 4.3 | ASTM D-2520 B | |
| 表面电阻率 | 1×10 | Ohm | ASTM D-257 |
| 介电常数 | ASTM D-150 | ||
| (0.8mm(0.032in),23℃(73℉)) | 3.9 | ||
| (3.2mm(0.125in),23℃(73℉)) | 4.3 | ||
| 体积电阻率 | 1×10 | Ohm-cm | ASTM D-257 |
| 介电强度 (3.2mm,23℃(73℉)) | 28 | Kv/mm | ASTM D-149 |
| 损耗因数 (1.6mm(0.063in),23℃(73℉)) | 0.004 | ASTM D-2520 B | |
| 介电强度 (1.6mm,23℃(73℉)) | 35 | Kv/mm | ASTM D-149 |
| 损耗因数 | |||
| (0.8mm(0.032in),23℃(73℉)) | 0.013 | ASTM D-150 | |
| (0.8mm(0.032in),23℃(73℉)) | 0.004 | ASTM D-2520 B | |
| 介电强度 (1.6mm(0.063in)) | 31 | Kv/mm | ASTM D-149 |
| 热性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 表面电阻率 | 1×10 | Ohm | ASTM D-257 |
| 熔点 | 352 | ℃ | ASTM D-3418 |
| 解链温度范围 | 363-371 | ℃ | |
| 热导率 | 0.32 | W/mk | ASTM C-177 |
| 模压温度范围 | 30-95 | ℃ | |
| 玻璃化转变温度 | 120 | ℃ | ASTM D-3418 |
| 干燥温度 | 135 | ℃ | |
| 热变形温度 (1.80MPa) | 289 | ℃ | ASTM D-648 |
| 其它性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| RTI,Mechanical with Impact (1.5mm) | 210 | ℃ | UL 746-B |
| RTI,Electrical (3.0mm) | 240 | ℃ | UL 746-B |
| RTI,Mechanical without Impact (1.5mm) | 240 | ℃ | UL 746-B |
| RTI,Electrical (0.75mm) | 240 | ℃ | UL 746-B |
| RTI,Mechanical without Impact (0.75mm) | 240 | ℃ | UL 746-B |
| RTI,Mechanical with Impact (3.0mm) | 210 | ℃ | UL 746-B |
| RTI,Mechanical without Impact (3.0mm) | 240 | ℃ | UL 746-B |
| RTI,Electrical (1.5mm) | 240 | ℃ | UL 746-B |