东莞市铭汇塑胶有限公司
6330
LCP | 液晶聚合物#
美国杜邦
6330 物性表
| 物理性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 比重 | 1.64 | ASTM D-792 | |
| 模具收缩率 (3.2mm(0.126in)) | 0.5 | % | ASTM D-955 |
| 机械性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 弯曲强度 (3.2mm(0.125in),23℃(73℉)) | 125 | MPa | ASTM D-790 |
| 断裂伸长率 (3.2mm(0.125in),23℃(73℉)) | 4 | % | ASTM D-638 |
| 弯曲模量 | ASTM D-790 | ||
| (3.2mm(0.125in),23℃(73℉)) | 9600 | MPa | |
| (3.2mm(0.125in),23℃(73℉)) | 9600 | MPa | |
| (0.8mm(0.032in),23℃(73℉)) | 13900 | MPa | |
| 拉伸模量 (1.6mm(0.063in),23℃(73℉)) | 11569 | MPa | ASTM D-638 |
| 拉伸强度 (1.6mm(0.063in),23℃(73℉)) | 141 | MPa | ASTM D-638 |
| 断裂伸长率 (1.6mm(0.063in),23℃(73℉)) | 3.3 | % | ASTM D-638 |
| 压缩模量 | 4100 | MPa | ASTM D-695 |
| 弯曲强度 (3.2mm(0.125in),23℃(73℉)) | 125 | MPa | ASTM D-790 |
| IZOD冲击强度 (3.2mm(0.126in)) | 160 | J/m | ASTM D-256 |
| 断裂伸长率 (3.2mm(0.125in),23℃(73℉)) | 4 | % | ASTM D-638 |
| 拉伸模量 | ASTM D-638 | ||
| (3.2mm) | 10500 | MPa | |
| (1.6mm(0.063in),23℃(73℉)) | 11569 | MPa | |
| 压缩模量 | 4100 | MPa | ASTM D-695 |
| 弯曲强度 (0.8mm(0.032in),23℃(73℉)) | 158 | MPa | ASTM D-790 |
| 弯曲模量 (0.8mm(0.032in),23℃(73℉)) | 13900 | MPa | ASTM D-790 |
| 拉伸模量 (3.2mm(0.125in),23℃(73℉)) | 10500 | MPa | ASTM D-638 |
| IZOD冲击强度 (3.2mm(0.126in)) | 160 | J/m | ASTM D-256 |
| 弯曲强度 (0.8mm(0.032in),23℃(73℉)) | 158 | MPa | ASTM D-790 |
| 拉伸强度 (3.2mm(0.125in),23℃(73℉)) | 125 | MPa | ASTM D-638 |
| 电气性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 损耗因数 | ASTM D-2520 B | ||
| (0.8mm(0.032in),23℃(73℉)) | 0.001 | ||
| (1.6mm(0.063in),23℃(73℉)) | 0.002 | ||
| 介电强度 (0.8mm) | 49 | Kv/mm | ASTM D-149 |
| 介电常数 | |||
| (0.8mm(0.032in),23℃(73℉)) | 3.9 | ASTM D-2520 B | |
| (0.8mm(0.032in)) | 2.9 | ASTM D-150 | |
| (1.6mm(0.063in),23℃(73℉)) | 4 | ASTM D-2520 B | |
| 损耗因数 (0.8mm(0.032in)) | 0.013 | ASTM D-150 | |
| 介电强度 (3.2mm) | 26 | Kv/mm | ASTM D-149 |
| 介电常数 | |||
| (0.8mm) | 3.3 | ASTM D-150 | |
| (3.2mm(0.125in),23℃(73℉)) | 4.1 | ASTM D-2520 B | |
| (3.2mm(0.125in)) | 3.6 | ASTM D-150 | |
| 介电强度 (1.6mm) | 41 | Kv/mm | ASTM D-149 |
| 损耗因数 (1.6mm(0.063in),23℃(73℉)) | 0.001 | ASTM D-2520 B | |
| 介电常数 (3.2mm(0.125in)) | 3.6 | ASTM D-150 | |
| 损耗因数 | ASTM D-150 | ||
| (0.8mm(0.032in)) | 0.029 | ||
| (0.8mm(0.032in)) | 0.009 | ||
| (3.2mm(0.125in)) | 0.013 | ||
| 介电常数 (0.8mm(0.032in)) | 3.3 | ASTM D-150 | |
| 表面电阻率 | 1×10 | Ohm | ASTM D-257 |
| 介电常数 | ASTM D-2520 B | ||
| (3.2mm(0.125in),23℃(73℉)) | 3.9 | ||
| (0.8mm(0.032in),23℃(73℉)) | 4.1 | ||
| 体积电阻率 | 1×10 | Ohm-cm | ASTM D-257 |
| 损耗因数 | ASTM D-2520 B | ||
| (0.8mm(0.032in),23℃(73℉)) | 0.002 | ||
| (3.2mm(0.125in),23℃(73℉)) | 0.002 | ||
| (3.2mm(0.125in),23℃(73℉)) | 0.001 | ||
| 介电常数 | |||
| (3.2mm(0.125in)) | 3.2 | ASTM D-150 | |
| (1.6mm(0.063in),23℃(73℉)) | 3.9 | ASTM D-2520 B | |
| 损耗因数 | ASTM D-150 | ||
| (3.2mm(0.125in)) | 0.028 |
| 加工性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| (3.2mm(0.125in)) | 0.008 |
| 热性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 热变形温度 (1.80MPa) | 239 | ℃ | ASTM D-648 |
| 玻璃化转变温度 | 120 | ℃ | ASTM D-3418 |
| 模压温度范围 | 30-95 | ℃ | |
| 干燥温度 | 135 | ℃ | |
| 熔点 | 335 | ℃ | ASTM D-3418 |
| 解链温度范围 | 350-360 | ℃ |
| 其它性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 工业含水量 | 0.01 | % | |
| RTI,Electrical (1.5mm) | 130 | ℃ | UL 746-B |
| RTI,Mechanical with Impact (1.5mm) | 130 | ℃ | UL 746-B |
| RTI,Mechanical without Impact (1.5mm) | 130 | ℃ | UL 746-B |