Lupoy EC5000AF ABS PC
Lupoy ER5001RFA ABS PC
Lupoy ER5151RFA ABS PC
Lupoy GN1000F ABS PC
Lupoy GN1000FA ABS PC
Lupoy GN5001EF ABS PC
Lupoy GN5001RF ABS PC
Lupoy GN5001RFD ABS PC
Lupoy GN5001RFH ABS PC
Lupoy GN5001RFJ ABS PC
Lupoy GN5001RFM ABS PC
Lupoy GN5001RFP ABS PC
Lupoy GN5001RFS ABS PC
Lupoy GN5001RFT ABS PC
Lupoy GN5001SF ABS PC
Lupoy GN5001TF ABS PC
Lupoy GN5007FL ABS PC
Lupoy GN5008HF ABS PC
Lupoy GN5008LF ABS PC
Lupoy GN5009F ABS PC
Lupoy GN5101RF ABS PC
Lupoy GN5151RF ABS PC
Lupoy GN5151RFA ABS PC
Lupoy GN5201F ABS PC
Lupoy GN5301F ABS PC
Lupoy GP5001AF ABS PC
Lupoy GP5006AF ABS PC
Lupoy GP5006B ABS PC
Lupoy GP5006BH ABS PC
Lupoy GP5008A ABS PC
Lupoy GP5008BF ABS PC
Lupoy GP5008BFH ABS PC
Lupoy GP5056F ABS PC
Lupoy GP5100 ABS PC
Lupoy GP5106F ABS PC
Lupoy GP5200 ABS PC
Lupoy GP5206F ABS PC
Lupoy HG5000B ABS PC
Lupoy HI5002A ABS PC
Lupoy HP5004 ABS PC
Lupoy HP5004A ABS PC
Lupoy HP5004HF ABS PC
Lupoy HP5008 ABS PC
Lupoy HR5007A ABS PC
Lupoy HR5007AE ABS PC
Lupoy MP5000AM ABS PC
Lupoy NS5000 ABS PC
Lupoy NS5000C ABS PC
Lupoy SG5009F ABS PC
Lupoy HR5007A 物性表
基本信息 | |
---|---|
黄卡编号 | |
添加剂 |
|
特性 |
|
用途 |
|
外观 |
|
形式 |
|
加工方法 |
|
多点数据 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
比重 | |||
-- | 1.14 | g/cm3 | ASTM D792 |
-- | 1130 | kg/m3 | ISO 11831 |
熔流率(熔体流动速率)(250°C/2.16 kg) | 5.3 | g/10 min | ASTM D1238 |
熔体体积流动速率(260°C/5.0 kg) | 18.0 | cm3/10min | ISO 11332 |
收缩率 - 流动(3.20 mm, 注塑) | 0.50 到 0.80 | % | ASTM D955 |
吸水率(饱和) | 0.15 | % | ISO 623 |
硬度 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
洛氏硬度(R 级) | 114 | ASTM D785 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸模量 | 2200 | MPa | ISO 527-24 |
抗张强度 | |||
屈服, 3.20 mm, 注塑5 | 56.9 | MPa | ASTM D638 |
屈服 | 60.0 | MPa | ISO 527-26 |
拉伸应变 | |||
屈服 | 4.9 | % | ISO 527-27 |
断裂, 3.20 mm, 注塑8 | 100 | % | ASTM D638 |
断裂伸长率 | 50 | % | ISO 527-29 |
弯曲模量10(3.20 mm, 注塑) | 2110 | MPa | ASTM D790 |
弯曲强度11(3.20 mm) | 77.5 | MPa | ASTM D790 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
简支梁缺口冲击强度 | ISO 179/1eA12 | ||
-30°C | 36.3 | kJ/m2 | ISO 179/1eA |
23°C | 无断裂 | ISO 179/1eA | |
简支梁冲击强度 | ISO 179/1eU13 | ||
-30°C | 无断裂 | ISO 179/1eU | |
23°C | 无断裂 | ISO 179/1eU | |
悬壁梁缺口冲击强度 | ASTM D256 | ||
-30°C, 3.20 mm, 注塑 | 490 | J/m | ASTM D256 |
23°C, 3.20 mm, 注塑 | 640 | J/m | ASTM D256 |
无缺口悬臂梁冲击 | 无断裂 | ASTM D256 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
载荷下热变形温度 | |||
1.8 MPa, 未退火, 6.40 mm, 注塑 | 113 | °C | ASTM D648 |
1.8 MPa | 104 | °C | ISO 75-214 |
玻璃转化温度15 | 150 | °C | ISO 11357-216 |
维卡软化温度(50°C/h, B (50N)) | 119 | °C | ISO 30617 |
线形膨胀系数 | ISO 11359-218 | ||
流动 | 7.7E-5 | cm/cm/°C | ISO 11359-2 |
横向 | 8.3E-5 | cm/cm/°C | ISO 11359-2 |
RTI Elec | UL 746 | ||
1.60 mm | 60.0 | °C | UL 746 |
3.00 mm | 60.0 | °C | UL 746 |
RTI Imp | UL 746 | ||
1.60 mm | 60.0 | °C | UL 746 |
3.00 mm | 60.0 | °C | UL 746 |
RTI | UL 746 | ||
1.60 mm | 60.0 | °C | UL 746 |
3.00 mm | 60.0 | °C | UL 746 |
电气性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
表面电阻率 | 3.8E+14 | ohms | IEC 6009319 |
体积电阻率 | 1.0E+13 | ohms·m | IEC 6009320 |
耐电强度 | 42 | kV/mm | IEC 60243-121 |
相对电容率(1 MHz) | 2.80 | IEC 6025022 | |
耗散因数(1 MHz) | 0.010 | IEC 6025023 | |
耐电弧性 | PLC 6 | ASTM D495 | |
相比耐漏电起痕指数(CTI) | PLC 0 | UL 746 | |
漏电起痕指数 | 200 | IEC 6011224 | |
高电弧燃烧指数(HAI) | UL 746 | ||
1.60 mm | PLC 1 | UL 746 | |
3.00 mm | PLC 1 | UL 746 | |
高压电弧抗点燃指数 (HVAR) (PLC) | PLC 6 | UL 746 | |
热丝引燃 (HWI) | UL 746 | ||
1.60 mm | PLC 3 | UL 746 | |
3.00 mm | PLC 3 | UL 746 |
可燃性 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
UL 阻燃等级 | UL 94 | ||
1.60 mm | HB | UL 94 | |
3.00 mm | HB | UL 94 |
注射 | 额定值 | 单位制 | |
---|---|---|---|
干燥温度 | 80.0 到 100 | °C | |
干燥时间 | 4.0 到 6.0 | hr | |
建议的最大水分含量 | 0.020 | % | |
料筒后部温度 | 240 到 270 | °C | |
料筒中部温度 | 245 到 275 | °C | |
料筒前部温度 | 245 到 275 | °C | |
射嘴温度 | 245 到 275 | °C | |
加工(熔体)温度 | 250 到 275 | °C | |
模具温度 | 50.0 到 70.0 | °C | |
螺杆转速 | 40 到 70 | rpm |
|
---|