产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 流动系数 | ASTM D-1238 | 22 | g/10min | ||
| 比重 | ASTM D792 | 1.20 | ||||
| 吸水率 | ASTM D570 | 0.2 | % | |||
| 成型收缩率 | - | 流动方向 | ASTM D955 | 0.5-0.7 | % | |
| - | 垂直方向 | ASTM D955 | 0.5-0.7 | % | ||
| 机械性能 | 引张强度 | ASTM D-638 | 630 | kg/cm2 | ||
| IZOD 冲击强度 | ASTM D-256 | 80 | kg-cm/cm | |||
| 弯曲强度 | ASTM D-790 | 920 | kg/cm2 | |||
| 引张强度 | ASTM D638 | 630 | kg/cm2 | |||
| 弯曲强度 | 23℃ | ASTM D790 | 920 | kg/cm2 | ||
| 弯曲模量 | 23℃ | ASTM D790 | 24000 | kg/cm2 | ||
| 洛氏硬度 | ASTM D785 | 77 | M | |||
| 压缩强度 | ASTM D695 | 780 | kg/cm2 | |||
| 电气性能 | 介电常数 | - | 60Hz | ASTM D150 | 2.95 | |
| - | 106Hz | ASTM D150 | 2.9 | |||
| 介质损耗 | - | 60Hz | ASTM D150 | 0.0004 | ||
| - | 106Hz | ASTM D150 | 0.009 | |||
| 绝缘破坏强度 | 1.6mm | ASTM D149 | 30 | KV/mm | ||
| 耐电弧性 | ASTM D495 | 110 | sec | |||
| 热性能 | 软化点 | ASTM D-1525 | 150 | ℃ | ||
| 热变形温度 | - | 0.46Mpa | ASTM D648 | 136 | ℃ | |
| - | 1.8Mpa | ASTM D648 | 125 | ℃ | ||
| 膨胀系数 | ASTM D696 | 6-8 | ||||
| 热传导率 | ASTM C177 | 0.2 | ||||
| 阻燃性 | 1/16" | UL94 | V-2 | |||
| 光学性能 | 全光穿透率 | ASTM D1003 | 89 | % | ||
| 折射率 | ASTM D542 | 1.585 | ||||
售后说明
1、物流运费说明
店铺报价不含运费，运费由买家承担，拍下付款后，买家可自行安排自己熟悉的物流上门提货，也可由卖家安排物流，运费提付。
2、在线下单
因塑胶行情价格波动较大，请用旺旺客服或电话直接询价确认后再拍，请拍下后当天内付款。
3、货物退换
到货后请买家仔细确认货物完好后再签收，否则如无质量问题，不退不换。
4、发票制度说明
本公司可以线下交易也可线上支付交易，都可提供正规的增值税专用发票。
产品介绍
PC聚碳酸酯，英文名为Polycarbonate，简称PC，是一种非结晶体工程材料，具有特别好的抗冲击强度、热稳定性、光泽度、抑制细菌特性、阻燃特性以及抗污染性。PC的缺口冲击强度非常高，并且收缩率很低，一般为0.1%-0.2%。
纯PC树脂是一种无定型、无味、无嗅、无毒、透明的热塑性聚合物，分子量一般为20000-70000范围内，相对密度1.18-1.20，玻璃化温度140-150°C，熔程220-230°C。
PC有很好的机械特性，但流动特性较差，因此这种材料的注塑过程较困难。如果塑件要求有较高的抗冲击性，那么就使用低流动率的PC材料；反之，可以使用高流动率的PC材料，这样可以优化注塑过程。
主要特性
产品应用
PC聚碳酸酯是一种强韧、高透光的热塑性树脂。主要应用于玻璃装配业、汽车零部件、电子电器、光学照明、工业机械领域等。
仓库图 
| 温馨提示：受国际形势及石油价格的影响，塑胶原料价格每天均呈现波动，报价仅供参考，当天具体价格，请以来电或在线咨询实际行情为准！感谢您的体谅 |