PA66 Zytel FG133F1 NC010

Unreinforced Polyamide 66Developed for Food Contact Applications

Information provided by DuPont. This product line has remained with DuPont after the DuPont-Dow merger.

Physical Properties	Metric	English	Comments
Density	1.14g/cc	0.0412lb/in3	DAM; ISO 1183
Linear Mold Shrinkage, Flow	0.0080cm/cm	0.0080in/in	DAM; ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.010cm/cm	0.010in/in	DAM; ISO 294-4, 2577
Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	94.0MPa	13600psi	DAM; ISO 527-1/-2
Elongation at Break	14 %	14 %	Nominal; DAM; ISO 527-1/-2
Elongation at Yield	6.0 %	6.0 %	DAM; ISO 527-1/-2
Tensile Modulus	3.80GPa	551ksi	DAM; ISO 527-1/-2
Poissons Ratio	0.36	0.36	DAM; ISO 527-1/-2
Charpy Impact, Notched	0.300J/cm2 @Temperature 23.0 °C	1.43ft-lb/in2 @Temperature 73.4 °F	DAM; ISO 179/1eA
Thermal Properties	Metric	English	Comments
Melting Point	262°C	504°F	10°C/min; DAM; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	78.0°C	172°F	DAM; ISO 75-1/-2
Flame Spread	=80.0mm/min @Thickness 1.00 mm	=3.15in/min @Thickness 0.0394 in	ISO 3795 (FMVSS 302)

PA特性

1、具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差

2、PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。

3、在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是最常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。PA66的粘性较低，因此流动性很好（但不如PA6）。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。

4、PA66的收缩率在1%~2%之间，加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。PA66对许多溶剂具有抗溶性，但对酸和其它一些氯化剂的抵抗力较弱。

PA66应用

高温电气插座零件、电气零件、齿轮、轴承、滚子、弹簧支架、滑轮、螺栓、叶轮、风扇叶片、螺旋桨、高压封口垫片、阀座、输油管、储油容器、绳索、扎带、传动皮带、砂轮粘合剂、电池箱、绝缘电气零件、线芯、抽丝等