PA66 Zytel FG70G50HSLA BK309

50% Glass Reinforced, Heat Stabilized, Polyamide 66Developed for Food Contact Applications

Information provided by DuPont. This product line has remained with DuPont after the DuPont-Dow merger.

Physical Properties	Metric	English	Comments
Density	1.40g/cc	0.0506lb/in3
	1.57g/cc	0.0567lb/in3	DAM; ISO 1183
Water Absorption	4.2 % @Thickness 2.00 mm	4.2 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Moisture Absorption	1.20 % @Thickness 2.00 mm	1.20 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Viscosity Test	100cm3/g	100cm3/g	DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow	0.0030cm/cm	0.0030in/in	DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse	0.0080cm/cm	0.0080in/in	DAM; ISO 294-4 2577

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	190MPa	27600psi	50%RH; ISO 527-1/-2
	250MPa	36300psi	DAM; ISO 527-1/-2
Elongation at Break	2.3 %	2.3 %	DAM; ISO 527-1/-2
	3.2 %	3.2 %	50%RH; ISO 527-1/-2
Tensile Modulus	13.0GPa	1890ksi	50%RH; ISO 527-1/-2
	17.0GPa	2470ksi	DAM; ISO 527-1/-2
Charpy Impact Unnotched	10.0J/cm2	47.6ft-lb/in2	DAM; ISO 179/1eU
	11.0J/cm2	52.3ft-lb/in2	50%RH; ISO 179/1eU

PA66 Zytel FG70G50HSLA BK309

尼龙中的主要品种是尼龙6和尼龙66，占绝对主导地位，尼龙6为聚己内酰胺，而尼龙66为聚己二酸己二胺，尼龙66比尼龙6要硬l2%；其次是尼龙11，尼龙12，尼龙610，尼龙612，另外还有尼龙1010、尼龙46、尼龙7、尼龙9、尼龙13，新品种有尼龙6I、尼龙9T和特殊尼龙MXD6（阻隔性树脂）等，尼龙的改性品种数量繁多，如增强尼龙、单体浇铸尼龙（MC尼龙）、反应注射成型(RIM)尼龙、芳香族尼龙、透明尼龙、高抗冲（超韧）尼龙、电镀尼龙、导电尼龙、阻燃尼龙，尼龙与其他聚合物共混物和合金等，满足不同特殊要求，广泛用作金属，木材等传统材料代用品。

特性

尼龙作为大用量的工程塑料，广泛用于机械、汽车、电器、纺织器材、化工设备、航空、冶金等领域。

成为各行业中不可缺少的结构材料，其主要特点如下：

1．优良的力学性能。尼龙的机械强度高，韧性好。

2．自润性、耐摩擦性好。尼龙具有很好的自润划性，摩擦系数小，从而，作为传动部件其使用寿命长。

3.优良的耐热性。如尼龙46等高结晶性尼龙的热变形温度很高，可在150℃下长期期使用。PA66经过

玻璃纤维增强以后，其热变形温度达到250℃以上。

4.优异的电绝缘性能。尼龙的体积电阻很高，耐击穿电压高，是优良的电气、电器绝缘材料。

5.优良的耐气候性。

6.吸水性。尼龙吸水性大，饱和吸水可达到3%以上。在一定程度影响制件的尺寸稳定性。

应用

高温电气插座零件、电气零件、齿轮、轴承、滚子、弹簧支架、滑轮、螺栓、叶轮、风扇叶片、螺旋桨、高压封口垫片、阀座、输油管、储油容器、绳索、扎带、传动皮带、砂轮粘合剂、电池箱、绝缘电气零件、线芯、抽丝等