深圳市亿之圣塑化有限公司
DuPont Performance Polymers Zytel? 45HSB NC010 Nylon 66 (Unverified Data**) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.14 g/cc | 1.14 g/cc | DAM; ASTM D792 |
| 密度 | 1.14 g/cc | 0.0412 lb/in3 | DAM; ISO 1183 |
| 线性成型收缩率,Flow | 0.014 cm/cm
@Thickness 2.00 mm
|
0.014 in/in
@Thickness 0.0787 in
|
DAM; ISO 294-4 |
| 线性成型收缩率，横向 | 0.014 cm/cm
@Thickness 2.00 mm
|
0.014 in/in
@Thickness 0.0787 in
|
DAM; ISO 294-4 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度 | 83.0 MPa
@Temperature 23.0 °C
|
12000 psi
@Temperature 73.4 °F
|
DAM; ASTM D638 |
| 抗张强度(屈服) | 55.0 MPa
@Temperature 23.0 °C
|
7980 psi
@Temperature 73.4 °F
|
50%RH; ISO 527 |
| 83.0 MPa
@Temperature 23.0 °C
|
12000 psi
@Temperature 73.4 °F
|
DAM; ISO 527 | |
| 伸长率 (断裂) | = 50 %
@Temperature 23.0 °C
|
= 50 %
@Temperature 73.4 °F
|
DAM; nominal; ISO 527 |
| = 50 %
@Temperature 23.0 °C
|
= 50 %
@Temperature 73.4 °F
|
50%RH; nominal; ISO 527 | |
| 90 %
@Temperature 23.0 °C
|
90 %
@Temperature 73.4 °F
|
DAM; ASTM D638 | |
| Elongation at Yield | 4.0 %
@Temperature 23.0 °C
|
4.0 %
@Temperature 73.4 °F
|
DAM; ISO 527 |
| 25 %
@Temperature 23.0 °C
|
25 %
@Temperature 73.4 °F
|
50%RH; ISO 527 | |
| 拉伸模量 | 1.30 GPa
@Temperature 23.0 °C
|
189 ksi
@Temperature 73.4 °F
|
50%RH; ISO 527 |
| 3.10 GPa
@Temperature 23.0 °C
|
450 ksi
@Temperature 73.4 °F
|
DAM; ISO 527 | |
| 弯曲模量 | 2.80 GPa
@Temperature 23.0 °C
|
406 ksi
@Temperature 73.4 °F
|
DAM; ISO 178 |
| 3.03 GPa
@Temperature 23.0 °C
|
439 ksi
@Temperature 73.4 °F
|
DAM; ASTM D790 | |
| 悬壁梁缺口冲击强度 | 0.640 J/cm
@Temperature 23.0 °C
|
1.20 ft-lb/in
@Temperature 73.4 °F
|
DAM; ASTM D256 |
| 6.00 kJ/m2
@Temperature -40.0 °C
|
2.86 ft-lb/in2
@Temperature -40.0 °F
|
DAM; ISO 180/1A | |
| 6.00 kJ/m2
@Temperature 23.0 °C
|
2.86 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 180/1A | |
| 简支梁缺口冲击强度 | 0.550 J/cm2
@Temperature -30.0 °C
|
2.62 ft-lb/in2
@Temperature -22.0 °F
|
DAM; ISO 179/1eA |
| 0.600 J/cm2
@Temperature 23.0 °C
|
2.86 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 179/1eA |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| Comparative Tracking Index | 600 V
@Temperature 23.0 °C
|
600 V
@Temperature 73.4 °F
|
DAM; UL 746A |
| = 600 V
@Temperature 23.0 °C
|
= 600 V
@Temperature 73.4 °F
|
DAM; UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 500 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
278 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ISO 11359-1/-2 |
| 线性热膨胀系数,横向流动 | 100 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
55.6 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ISO 11359-1/-2 |
| 熔融温度 | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| 262 °C | 504 °F | DAM; ASTM D3418 | |
| 载荷下热变形温度(0.46 MPa) | 200 °C | 392 °F | DAM; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 65.0 °C | 149 °F | DAM; ASTM D648 |
| 70.0 °C | 158 °F | DAM; ISO 75-1/-2 | |
| UL RTI | 140 °C
@Thickness 3.00 mm
|
284 °F
@Thickness 0.118 in
|
DAM; UL 746B |
| 140 °C
@Thickness 1.50 mm
|
284 °F
@Thickness 0.0591 in
|
DAM; UL 746B | |
| 140 °C
@Thickness 0.710 mm
|
284 °F
@Thickness 0.0280 in
|
DAM; UL 746B | |
| UL RTI，机械冲击 | 95.0 °C
@Thickness 0.710 mm
|
203 °F
@Thickness 0.0280 in
|
DAM; UL 746B |
| 110 °C
@Thickness 1.50 mm
|
230 °F
@Thickness 0.0591 in
|
DAM; UL 746B | |
| 110 °C
@Thickness 3.00 mm
|
230 °F
@Thickness 0.118 in
|
DAM; UL 746B | |
| UL RTI，机械无冲击 | 115 °C
@Thickness 0.710 mm
|
239 °F
@Thickness 0.0280 in
|
DAM; UL 746B |
| 125 °C
@Thickness 1.50 mm
|
257 °F
@Thickness 0.0591 in
|
DAM; UL 746B | |
| 125 °C
@Thickness 3.00 mm
|
257 °F
@Thickness 0.118 in
|
DAM; UL 746B | |
| 可燃性(UL94) | HB
@Thickness 3.00 mm
|
HB
@Thickness 0.118 in
|
DAM; IEC 60695-11-10 |
| HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
DAM; IEC 60695-11-10 | |
| HB
@Thickness 0.710 mm
|
HB
@Thickness 0.0280 in
|
DAM; IEC 60695-11-10 | |
| HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
DAM; UL94 | |
| HB
@Thickness 3.00 mm
|
HB
@Thickness 0.118 in
|
DAM; UL94 | |
| HB
@Thickness 0.710 mm
|
HB
@Thickness 0.0280 in
|
DAM; UL94 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 280 - 290 °C | 536 - 554 °F | DAM; Extrusion |
| 285 °C | 545 °F | DAM; Optimum; Extrusion | |
| 290 °C | 554 °F | DAM; Optimum; Injection Molding | |
| 280 - 300 °C | 536 - 572 °F | DAM; Injection Molding | |
| 模具温度 | 70.0 °C | 158 °F | DAM; optimum; Injection Molding |
| 50.0 - 90.0 °C | 122 - 194 °F | DAM; Injection Molding | |
| 干燥温度 | 80.0 °C | 176 °F | DAM; Extrusion |
| 80.0 °C | 176 °F | DAM; Injection Molding | |
| 干燥时间 | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Injection Molding |
| 4.00 - 6.00 hour | 4.00 - 6.00 hour | DAM; Extrusion | |
| 水分含量 | = 0.050 % | = 0.050 % | DAM; Extrusion |
| = 0.050 % | = 0.050 % | DAM; Injection Molding |
| 材料描述 | 测试方法 | |
|---|---|---|
| 添加剂 | Heat Stabilizer | DAM |
| 外观 | Natural Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Extrudable - Coating | Yes | DAM |
| Extrudable - Filament | Yes | DAM |
| Extrudable - Sheet | Yes | DAM |
| Extrudable - Tubing | Yes | DAM |
| 特性 | Heat Aging Resistance, Good | DAM |
| Molecular Wt., High | DAM | |
| Viscosity, High | DAM | |
| 形式 | Pellets | DAM |
| Generic | Nylon 66 | DAM |
| Heat Stabilized | Yes | DAM |
| Material Status | Current | DAM |
| 部件标识代码 | PA66 | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA66 | DAM |
| 加工方法 | Extrusion | DAM |
| Extrusion | DAM | |
| Injection Molding | DAM | |
| 产品分类 | Extrusion Resins | DAM |
| Unreinforced Resins | DAM | |
| 树脂识别 | PA66 | ISO 1043; DAM |
| 符合RoHS指令 | Contact Manufacturer | DAM |
| Ultrasonic Weldable | Yes | DAM |
| 用途 | Gears | DAM |
| Stock Material for Machining | DAM |