EVA泰国石化YV1055 热熔胶粘合剂
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | MFI | ASTM D-1238 | 8 | g/10 | ||
密度 | ASTM D-1505 | 0.935 | g/cm3 | |||
物理性能 | 膜厚 | 40 | u | |||
VA含量 | ISC.DIS 8965/1989(E) | 28 | % | |||
光泽度 | ASTM D-1003A | 65 | % | |||
机械性能 | 拉伸屈服强度 | MD | ASTM D-638 | 5 | N/mm2 | |
TD | ASTM D-638 | 4 | N/mm2 | |||
拉伸断裂伸长率 | MD | ASTM D-6398 | 440 | % | ||
TD | ASTM D-6398 | 720 | % | |||
拉伸断裂强度 | MD | ASTM D-638 | 24 | N/mm2 | ||
TD | ASTM D-638 | 24 | N/mm2 | |||
雾度 | ASTM D-2457 | 5 | % | |||
落花流水标冲击强度 | ASTM D-1709 A-B | 大于等于300 | g | |||
1%断裂割线模量度 | MD | ASTM D-882B | 44 | N/mm2 | ||
TD | ASTM D-882B | 50 | N/mm2 | |||
邵氏硬度 | A | ASTM D-2240 | 89~93 | |||
D | ASTM D-2240 | 33 | ||||
撕裂强度 | MD | ASTM D-1922 | 91 | g | ||
TD | ASTM D-1922 | 129 | g | |||
电气性能 | 介电常数 | 2×10HZ | ASTM D-150 | 2.9 | ||
介电强度 | ASTM D-149 | 670 | KV/cm | |||
热性能 | 熔点 | 95 | °C | |||
维卡软化点 | ASTM D-1525 | 68~72 | °C |
EVA泰国石化YV1055 热熔胶粘合剂
EVA是乙烯和醋酸共聚而成的,中文化学名称:乙烯-醋酸乙烯共聚物(乙烯-乙酸乙烯共聚物),英文化学名称:Ethylene Vinyl Acetate Copolymer ,简称EVA。一般醋酸乙烯(VA)的含量在5%-40%,与聚乙烯(PE)相比,EVA由于在分子链中引入醋酸乙烯单体,从而降低了高结晶度,提高了韧性、抗冲击性、填料相溶性和热密封性能,被广泛用于发泡鞋材、功能性棚膜、包装模、热熔胶、电线电缆及玩具等领域。
广泛用于发泡鞋材、功能性棚膜、包装模、热熔胶、电线电缆及玩具等领域。
1) VA含量在5%以下的EVA,其主要产品是薄膜、电线电缆、LDPE改性剂、胶粘剂等;
2) VA含量在5%~10%的EVA,产品为弹性薄膜、注塑和发泡制品等;
3) VA含量在20%~28%的EVA,主要用于热熔粘合剂和涂层制品;
4) VA含量在28%-33%的EVA,光伏材料、太阳能电池粘合剂等;
5) VA含量在38%-40%的EVA,胶粘剂;
6) VA含量在5%~45%,主要产品为薄膜(包括农用薄膜)和片材,注塑、模塑制品,发泡制品,热熔粘合剂等。
EVA泰国石化YV1055 热熔胶粘合剂
我司长期销售;通用材料、工程材料、特种工程材料、氟系列材料、生物降解材料、弹性体。
长期供应销售;通用材料;ABS、AS(SAN)、PP
工程材料;PA66、PA6、PBT、POM、PC
特种工程材料;COC、CPVC、LCP、PA12、PA46、PEEK、PEI、PPA、PPS、POK、PSU、PPSU、PA11
氟系列材料;PFA、FEP、PTFE、ETFE、ECTFE、PVDF、THV、EFEP
生物降解材料;PLA、PBST、PBAT、PCL、PHA、PHB、PVA
弹性体;POP、TPU、TPV、TPE、TPR、TPISV、TPO
本诚信为本、赢得广大客户的认可,、欢迎来电咨询,由于近期原材料波动较大,需要电话确认