东莞市铭汇塑胶有限公司
Ultradur? B 4406 G4
聚丁烯对苯二甲酸酯
20% 玻璃纤维增强材料
BASF Corporation
产品说明：
Ultradur B 4406 G4 is an injection molding grade with 20 % glass fibers for parts requiring enhanced fire resistance (eg relay housings, plug-and-socket connectors, switches, lighting components).
Applications
Applications
Typical applications include relay housings, plug-and-socket connectors, switches, and lighting components.
Ultradur? B 4406 G4 物性表
| 基本信息 | |
|---|---|
| 黄卡编号 | |
| 填料/增强材料 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| RoHS 合规性 |
|
| 形式 |
|
| 加工方法 |
|
| 多点数据 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.55 | g/cm3 | ASTM D792, ISO 1183 |
| 溶化体积流率（MVR）(250°C/2.16 kg) | 11.0 | cm3/10min | ISO 1133 |
| 收缩率 - 流动(3.18 mm) | 0.30 | % | |
| 吸水率 | |||
| 饱和 | 0.40 | % | ASTM D570 |
| 饱和, 23°C | 0.40 | % | ISO 62 |
| 平衡, 50% RH | 0.20 | % | ASTM D570 |
| 平衡, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Viscosity Number (Reduced Viscosity) | 112.0 | ml/g | ISO 1628 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量(23°C) | 8200 | MPa | ISO 527-2 |
| 抗张强度 | |||
| 断裂, 23°C | 117 | MPa | ASTM D638 |
| 断裂, 23°C | 125 | MPa | ISO 527-2 |
| 伸长率 | |||
| 断裂, 23°C | 2.2 | % | ASTM D638 |
| 断裂, 23°C | 2.6 | % | ISO 527-2 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度(23°C) | 9.0 | kJ/m2 | ISO 179 |
| 简支梁无缺口冲击强度(23°C) | 48 | kJ/m2 | ISO 179 |
| 悬壁梁缺口冲击强度(23°C) | 53 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 | |||
| 0.45 MPa, 未退火 | 215 | °C | ASTM D648 |
| 0.45 MPa, 未退火 | 223 | °C | ISO 75-2/B |
| 1.8 MPa, 未退火 | 177 | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 200 | °C | ISO 75-2/A |
| 熔融峰值温度 | 223 | °C | ASTM D3418, ISO 3146 |
| 线形热膨胀系数 - 流动 | |||
| -- | 3.0E-5 | cm/cm/°C | ASTM E831 |
| -- | 5.0E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | ||
| 0.750 mm | 140 | °C | UL 746 |
| 1.50 mm | 140 | °C | UL 746 |
| 3.00 mm | 140 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 0.750 mm | 120 | °C | UL 746 |
| 1.50 mm | 120 | °C | UL 746 |
| 3.00 mm | 120 | °C | UL 746 |
| RTI | UL 746 | ||
| 0.750 mm | 125 | °C | UL 746 |
| 1.50 mm | 130 | °C | UL 746 |
| 3.00 mm | 130 | °C | UL 746 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 体积电阻率 | |||
| 1.50 mm | 1.0E+15 | ohms·cm | ASTM D257 |
| -- | 1.0E+15 | ohms·cm | IEC 60093 |
| 介电常数 | IEC 60250 | ||
| 100 Hz | 3.90 | IEC 60250 | |
| 1 MHz | 3.60 | IEC 60250 | |
| 耗散因数 | IEC 60250 | ||
| 100 Hz | 7.0E-3 | IEC 60250 | |
| 1 MHz | 0.017 | IEC 60250 | |
| 漏电起痕指数 | 200 | V | IEC 60112 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| UL 阻燃等级 | UL 94 | ||
| 0.400 mm | V-0 | UL 94 | |
| 0.750 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 100 到 120 | °C | |
| 干燥时间 | 4.0 | hr | |
| 建议的最大水分含量 | 0.040 | % | |
| 加工（熔体）温度 | 250 到 270 | °C | |
| 模具温度 | 60.0 到 100 | °C | |
| 注塑压力 | 3.50 到 12.5 | MPa | |
| 注射速度 | 快速 | ||
| 背压 | 1.00 | MPa |