东莞市恒磊塑胶有限公司
PP EXXONMOBIL PP7414
| General | |
Availability1 |
|
Features |
Impact ModifiedMedium FlowMedium Impact Resistance |
Uses |
Automotive ApplicationsCompoundingConsumer ApplicationsToys |
Appearance |
|
Form(s) |
|
Processing Method |
|
Revision Date |
|
| Physical | Typical Value |
Unit |
Test Based On |
Melt Mass-Flow Rate (MFR)(230°C/2.16 kg) |
20 |
g/10 min |
ASTM D1238 |
Density |
0.900 |
g/cm3 |
ExxonMobil Method |
| Mechanical | Typical Value |
Unit |
Test Based On |
Tensile Strength at Yield(51 mm/min) |
22.2 |
MPa |
ASTM D638 |
Elongation at Yield(51 mm/min) |
6.2 |
% |
ASTM D638 |
Flexural Modulus - 1% Secant |
|||
1.3 mm/min |
1030 |
MPa |
ASTM D790A |
13 mm/min |
1180 |
MPa |
ASTM D790B |
| Impact | Typical Value |
Unit |
Test Based On |
Notched Izod Impact(23°C) |
180 |
J/m |
ASTM D256A |
Gardner Impact(-29°C, 3.18 mm, Geometry GC) |
24.0 |
J |
ASTM D5420 |
| Thermal | Typical Value |
Unit |
Test Based On |
Deflection Temperature Under Load (DTUL) at 66psi - Unannealed |
85.1 |
°C |
ASTM D648 |